Suspension polymerization
Assignee: 3M Co
•
Filing: 1989-05-22
•
Granted: 1990-08-28
•
Expires: 2009-05-22
Abstract
Abstract The present invention relates to a method for suspension polymerization of a pressure-sensitive acrylatre copolymer bead having a glass transition temperature of 0° C. or less. The method comprises making a monomer premix comprising an acrylic acid ester of non-tertiary alcohol, the alcohol having from 1 to 14 carbon atoms, with the average number of carbon atoms being about 4 to about 12, a polar monomer copolymerizable with the acrylic acid ester, a chain transfer agent, a free-radical initiator, and a modifier moiety selected from the group consisting of 2-polystyrylethyl methacrylate macromolecular monomers, reactive zinc salts and hydrophobic silicas. The premix is then combined with a water phase containing a sufficient amount of suspending agent to form a suspension. The suspension is concurrently agitated and polymerization of the polymer premix is permitted until polymer beads are formed. The polymer beads are then collected. The amount of the modifier moiety must be sufficient to render the copolymer bead non-agglomerating at room temperature and safely handleable and transportable.
Inventors
- 👤 Chung I. Young
- 👤 Rudyard M. Enanoza
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 15:23
CPC Classifications
C; C08; C08F; C08F220/00; C08F220/02; C08F220/10; C09; C09J; C09J7/00; C09J7/30; C09J7/38; C09J7/381; C09J7/385
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
153 words
A method for suspension polymerization of a pressure-sensitive acrylate copolymer bead having a glass transition temperature of 0° C. or less, comprising the steps of: (a) making a monomer premix comprising (i) acrylic acid ester of non-tertiary alcohol, said alcohol having from about 1 to 14 carbon atoms, with the average number of carbon atoms being about 4 to about 12, (ii) a polar monomer copolymerizable with said acrylic acid ester, (iii) a chain transfer agent, (iv) a free-radical initiator, and (v) a modifier moiety; (b) combining said monomer premix with a water phase containing a suspension agent to form a suspension; (c) concurrently agitating said suspension and permitting polymerization of said monomer premix until copolymer beads are formed, and (d) collecting said copolymer beads, wherein said modifier moiety is a hydrophobic silica, and is present in an amount of from about 0.05 part to about 10 parts per 100 parts monomer premix.
Claim 2
Independent Claim
153 words
A method for suspension polymerization of a pressure-sensitive acrylate copolymer bead having a glass transition temperature of 0° C. or less, comprising the steps of: (a) making a monomer premix comprising (i) acrylic acid ester of non-tertiary alcohol, said alcohol having from about 1 to 14 carbon atoms, with the average number of carbon atoms being about 4 to about 12, (ii) a polar monomer copolymerizable with said acrylic acid ester, (iii) a chain transfer agent, (iv) a free-radical initiator, and (v) a modifier moiety; (b) combining said monomer premix with a water phase containing a suspension agent to form a suspension; (c) concurrently agitating said suspension and permitting polymerization of said monomer premix until copolymer beads are formed, and (d) collecting said copolymer beads, wherein said modifier moiety is a hydrophobic silica, and is present in an amount of from about 0.05 part to about 10 parts per 100 parts monomer premix.
Claim 3
Independent Claim
154 words
A method for suspension polymerization of a pressure-sensitive acrylate copolymer bead having a glass transition temperature of 20 C. or less, comprising the steps of: (a) making a monomer premix comprising (i) acrylic acid ester of non-tertiary alcohol, said alcohol having from about 1 to 14 carbon atoms, with the average number of carbon atoms being about 4 to about 12, (ii) a polar monomer copolymerizable with said acrylic acid ester, (iii) a chain transfer agent, (iv) a free-radical initiator, and (v) a modifier moiety; (b) combining said monomer premix with a water phase containing a suspension agent to form a suspension; (c) concurrently agitating said suspension and permitting polymerization of said monomer premix until copolymer beads are formed, and (d) collecting said copolymer beads, wherein said modifier moiety is a reactive zinc salt, and is present in an amount of from about 0.05 part to about 10 parts per 100 parts monomer premix.
Claim 4
Independent Claim
154 words
A method for suspension polymerization of a pressure-sensitive acrylate copolymer bead having a glass transition temperature of 20 C. or less, comprising the steps of: (a) making a monomer premix comprising (i) acrylic acid ester of non-tertiary alcohol, said alcohol having from about 1 to 14 carbon atoms, with the average number of carbon atoms being about 4 to about 12, (ii) a polar monomer copolymerizable with said acrylic acid ester, (iii) a chain transfer agent, (iv) a free-radical initiator, and (v) a modifier moiety; (b) combining said monomer premix with a water phase containing a suspension agent to form a suspension; (c) concurrently agitating said suspension and permitting polymerization of said monomer premix until copolymer beads are formed, and (d) collecting said copolymer beads, wherein said modifier moiety is a reactive zinc salt, and is present in an amount of from about 0.05 part to about 10 parts per 100 parts monomer premix.
Claim 5
Dependent Claim
22 words
The method of claim 2 wherein the reactive zinc salt is selected from the group consisting of zinc methacrylate and zinc acrylates.
Claim 6
Dependent Claim
25 words
A method according to claim 1 wherein said modifier moiety comprises from about 0.05 to about 10 parts per 100 parts of the monomer premix.
References Cited (Backward Citations)
US24906A
Cited
US2934530A
Cited
USRE24906E
Cited
GB952351A
Cited
GB1025719A
Cited
GB1133328A
Cited
US3691140A
Cited
US3786116A
Cited
DE2455133A1
Cited
US4269959A
Cited
JPS5742778A
Cited
US4554324A
Cited
US4543403A
Cited
US4551388A
Cited
JPS62119254A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-08-27 | 1994-02-26 | 1994-08-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-08-27 | 1998-02-26 | 1998-08-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-08-27 | 2002-02-26 | 2002-08-28 | $7700.00 | Window Closed / Lapsed |