Method for the preparation of silicone rubber composition
Assignee: Shin-Etsu Chemical Co Ltd
•
Filing: 1989-07-28
•
Granted: 1991-05-07
•
Expires: 2009-07-28
Abstract
Abstract A novel method is proposed for the preparation of a curable organopolysiloxane composition which is suitable as a material of a mold-making having excellent mechanical properties and durability in use for replica molding. The method comprises (a) blending a vinyl-containing organopolysiloxane with a hydrophobic reinforcing silica filler and hexamethyl disilazane, optionally, together with water each in a limited amount, (b) subjecting the blend to a heat treatment and (c) admixing the heat-treated blend with an organohydrogenpolysiloxane as a crosslinking agent of the vinyl-containing organopolysiloxane and a platinum compound as a catalyst for promoting the addition reaction between the silicon-bonded vinyl groups and the silicon-bonded hydrogen atoms.
Inventors
- 👤 Hironao Fujiki
- 👤 Morio Oohashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 16:07
CPC Classifications
C; C08; C08K; C08K9/00; C08K9/04; C08K9/06; C08L; C08L83/00; C08L83/04; C08G; C08G77/00; C08G77/04; C08G77/12; C08G77/20
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
152 words
A method for the preparation of a curable organopolysiloxane composition which comprises the steps of: (a) blending 100 parts by weight of a vinyl-containing organopolysiloxane having, in a molecule, at least two vinyl groups directly bonded to the silicon atoms, from 1 to 50 parts by weight of a finely divided silica filler having a hydrophobic surface and from 1 to 30 parts by weight of hexamethyl disilazane into a uniform mixture: (b) subjecting the uniform mixture obtained in step (a) to a heat treatment at a temperature ranging from 120° C. to 180° C. for a length of time of at least 120 minutes; and (c) admixing the heat-treated mixture with an organohydrogenpolysiloxane in an amount sufficient to provide from 0.4 to 4.0 moles of hydrogen atoms directly bonded to the silicon atoms per mole of the vinyl groups in the vinyl-containing organopolysiloxane and a catalytic amount of a platinum compound.
Claim 2
Independent Claim
152 words
A method for the preparation of a curable organopolysiloxane composition which comprises the steps of: (a) blending 100 parts by weight of a vinyl-containing organopolysiloxane having, in a molecule, at least two vinyl groups directly bonded to the silicon atoms, from 1 to 50 parts by weight of a finely divided silica filler having a hydrophobic surface and from 1 to 30 parts by weight of hexamethyl disilazane into a uniform mixture: (b) subjecting the uniform mixture obtained in step (a) to a heat treatment at a temperature ranging from 120° C. to 180° C. for a length of time of at least 120 minutes; and (c) admixing the heat-treated mixture with an organohydrogenpolysiloxane in an amount sufficient to provide from 0.4 to 4.0 moles of hydrogen atoms directly bonded to the silicon atoms per mole of the vinyl groups in the vinyl-containing organopolysiloxane and a catalytic amount of a platinum compound.
Claim 3
Dependent Claim
34 words
The method for the preparation of a curable organopolysiloxane composition as claimed in claim 1 wherein the vinyl-containing organopolysiloxane has a viscosity in the range from 800 centipoise to 100,000 centipoiise at 25° C.
Claim 4
Dependent Claim
39 words
The method for the preparation of a curable organopolysiloxane composition as claimed in claim 1 wherein the finely divided silica filler has a specific surface area in the range from 50 m 2 /g to 400 m 2 /g.
Claim 5
Dependent Claim
47 words
The method for the preparation of a curable organopolysiloxane composition as claimed in claim 1 wherein the heat treatment in step (b) is performed at a temperature in the range of from 130° C. to 160° C. for a length of time of 3 to 6 hours.
Claim 6
Dependent Claim
44 words
The method for the preparation of a curable organopolysiloxane composition as claimed in claim 1 wherein the uniform mixture obtained in step (a) is further admixed with water in an amount not exceeding 100% by weight based on the amount of the hexamethyl disilazane.
Claim 7
Dependent Claim
27 words
The method for the preparation of a curable organopolysiloxane composition as claimed in claim 1 wherein the organohydrogenpolysiloxane has an average degree of polymerization not exceeding 300.
Claim 8
Dependent Claim
35 words
The method for the preparation of a curable organopolysiloxane composition as claimed in claim 1 wherein the vinyl-containing organopolysiloxane is a dimethyl polysiloxane terminated at each molecular chain end with a vinyl dimethyl silyl group.
Claim 9
Dependent Claim
23 words
The method for the preparation of a curable organopolysiloxane composition as claimed in claim 1 wherein the organohydrogenpolysiloxane is a methyl hydrogen polysiloxane.
Claim 10
Dependent Claim
38 words
The method for the preparation of a curable organopolysiloxane composition as claimed in claim 1 wherein the platinum compound is selected from the group consisting of chloroplatinic acid and complexes thereof with an alcohol, olefin or vinyl siloxane.
Claim 11
Dependent Claim
43 words
The method for the preparation of a curable organopolysiloxane composition as claimed in claim 1 wherein the amount of the platinum compound is in the range from 1 ppm to 200 ppm calculated as platinum based on the amount of the vinyl-containing organopolysiloxane.
Claim 12
Dependent Claim
37 words
The method for the preparation of a curable organopolysiloxane composition as claimed in claim 1 wherein the finely divided silica filler has a surface rendered hydrophobic as blocked with (CH 3 ) 3 SiO 0 .5 units.
Claim 13
Dependent Claim
35 words
The method for the preparation of a curable organopolysiloxane composition as claimed in claim 1 wherein the finely divided silica filler has a surface rendered hydrophobic as blocked with (CH 3 ) 2 SiO units.
Claim 14
Dependent Claim
44 words
The method for the preparation of a curable organopolysiloxane composition as claimed in claim 1 wherein the finely divided silica filler has a surface rendered hydrophobic as blocked with (CH 3 ) 2 SiO units and CH 3 SiO 1 .5 units in combination.
Claim 15
Dependent Claim
35 words
The method for the preparation of a curable organopolysiloxane composition as claimed in claim 1 wherein the finely divided silica filler has a surface rendered hydrophobic as blocked with CH 3 SiO 1 .5 units.
Claim 16
Dependent Claim
19 words
A cured organopolysiloxane composition obtained by curing the curable organopolysiloxane composition prepared according to the method of claim 1.
References Cited (Backward Citations)
US4427801A
Cited
US4764577A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-05-06 | 1994-11-05 | 1995-05-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-05-06 | 1998-11-05 | 1999-05-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-05-06 | 2002-11-05 | 2003-05-07 | $7700.00 | Window Closed / Lapsed |