US5037515A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for making smooth-surfaced magnetic recording medium
Assignee: WD Media LLC
•
Filing: 1989-09-18
•
Granted: 1991-08-06
•
Expires: 2009-09-18
Abstract
Abstract A high-density thin-film magnetic disc and method of producing the disc. In forming the disc, chromium is sputtered onto a smooth-surfaced, non-metallic substrate, such as a glass substrate, first at room temperature, to form a substratum with a random structure, then at a high temperature, to form a chromium underlayer with anisotropic crystal orientation. A cobalt-based alloy is sputtered onto the underlayer to form the thin film magnetic layer. The disc has high coercivity, low bit shift, and can be operated at a flying height of between 2-4 μinches.
Inventors
- 👤 Hsiao-Chu Tsai
- 👤 Atef H. Eltoukhy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 14:17
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/06; C23C14/14; C23C14/16; C23C14/165; C23C14/18; C23C14/185; G; G11; G11B; G11B5/00; G11B5/62; G11B5/73; G11B5/7368; G11B5/7373; G11B5/739; G11B5/73911; G11B5/73921; G11B5/84; G11B5/851
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
168 words
A method of producing a smooth-surfaced magnetic recording disc which can be operated at a flying head clearance of between about 2-4μ inches, comprising (a) sputtering chromium onto the surface of a smooth-surfaced, non-metallic substrate, at a temperature below about 100° C., to form a chromium substratum having a thickness of between about 50 Å and 400 Å, and a relatively randomly oriented crystal structure; (b) heating the substrate and substratum to a temperature of at least about 200° C., to form a heated substratum; (c) sputtering chromium onto the heated substratum to form thereon, an upper stratum whose crystal structure is substantially more anisotropic than that of the substratum, and which has a thickness of at least about 400 Å, said substratum and upper stratum forming a chromium underlayer having a total underlayer thickness of less than about 4,000 Å; and (d) sputtering a cobalt-based alloy onto the surface of said underlayer to form a magnetic thin-film layer having a thickness substantially between 300 and 1,500 Å.
Claim 2
Independent Claim
168 words
A method of producing a smooth-surfaced magnetic recording disc which can be operated at a flying head clearance of between about 2-4μ inches, comprising (a) sputtering chromium onto the surface of a smooth-surfaced, non-metallic substrate, at a temperature below about 100° C., to form a chromium substratum having a thickness of between about 50 Å and 400 Å, and a relatively randomly oriented crystal structure; (b) heating the substrate and substratum to a temperature of at least about 200° C., to form a heated substratum; (c) sputtering chromium onto the heated substratum to form thereon, an upper stratum whose crystal structure is substantially more anisotropic than that of the substratum, and which has a thickness of at least about 400 Å, said substratum and upper stratum forming a chromium underlayer having a total underlayer thickness of less than about 4,000 Å; and (d) sputtering a cobalt-based alloy onto the surface of said underlayer to form a magnetic thin-film layer having a thickness substantially between 300 and 1,500 Å.
Claim 3
Dependent Claim
50 words
The method of claim 1, wherein the substrate on which the substratum is sputtered is a glass substrate, and the sputtering steps are carried out under conditions which produce a coercivity, in longitudinal recording, of greater than about 1,200 Oe, and a bit shift of less than about 16 ns.
Claim 4
Dependent Claim
36 words
The method of claim 1, wherein sputtering the substratum is performed substantially at room temperature, and said heating is carried out under conditions which raise the temperature of the substrate to at least about 300° C.
Claim 5
Dependent Claim
36 words
The method of claim 1, wherein the chromium substratum has a final thickness of between about 50 and 200 Å and the chromium underlayer has a final thickness of between about 500 Å and 2,000 Å.
Claim 6
Dependent Claim
18 words
The method of claim 1, wherein said magnetic thin-film layer contains 1-10% tantalum, 10-16% chromium and 60-85% cobalt.
Claim 7
Dependent Claim
18 words
The method of claim 1, wherein said magnetic thin-film layer contains 2-10% chromium, 10-28% nickel, and 70-88% cobalt.
Claim 8
Independent Claim
121 words
A method of forming a chromium underlayer on a smooth-surfaced, non-metallic substrate comprising: (a) sputtering chromium onto the surface of the substrate, with the substrate at a temperature below about 100° C., to form on the substrate, a heat absorbing substratum on the substrate having a thickness of between about 50 Å and 400 Å, and a relatively randomly oriented crystal structure; (b) heating the substrate and substratum to a temperature of at least about 200° C., to form a heated substratum; and (c) sputtering chromium onto the heated substratum to form thereon, a chromium deposition layer whose crystal structure is substantially more anisotropic than that of of the substratum, and which has a thickness of at least about 400 Å.
Claim 9
Independent Claim
121 words
A method of forming a chromium underlayer on a smooth-surfaced, non-metallic substrate comprising: (a) sputtering chromium onto the surface of the substrate, with the substrate at a temperature below about 100° C., to form on the substrate, a heat absorbing substratum on the substrate having a thickness of between about 50 Å and 400 Å, and a relatively randomly oriented crystal structure; (b) heating the substrate and substratum to a temperature of at least about 200° C., to form a heated substratum; and (c) sputtering chromium onto the heated substratum to form thereon, a chromium deposition layer whose crystal structure is substantially more anisotropic than that of of the substratum, and which has a thickness of at least about 400 Å.
Claim 10
Dependent Claim
17 words
The method of claim 7, which further includes sputtering a cobalt-based magnetic thin layer over the substrate.
References Cited (Backward Citations)
US4245008A
Cited
US4426265A
Cited
US4576700A
Cited
US4552820A
Cited
US4604179A
Cited
WO1989005362A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-08-05 | 1995-02-04 | 1995-08-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-08-05 | 1999-02-04 | 1999-08-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-08-05 | 2003-02-04 | 2003-08-06 | $7700.00 | Window Closed / Lapsed |