Screen-printable acrylate pressure-sensitive adhesive composition
Assignee: 3M Co
•
Filing: 1990-12-07
•
Granted: 1992-08-25
•
Expires: 2010-12-07
Abstract
Abstract Screen-printable acrylate pressure-sensitive adhesive composition suitable for adhesive products having simultaneously, and independently from temperature, high values of adhesion, peel strength and shear strength as well as a high water and humidity resistance, comprising (A) about 25 to 225 parts by weight of at least one dissolved inherently tacky pressure-sensitive adhesive selected from non-crosslinked (meth)acrylic ester/(meth)acrylic acid copolymers having an average molecular weight corresponding to an inherent viscosity of not more than 1.0 dl/g; and (B) 100 parts by weight of an organic solvent or solvent mixture having a low partial vapor pressure of less than about 3 kPa (30 mbar) at 20° C. and a dipole amount of at least 1.0 Debye. The acrylate copolymer preferably has structural units of the formula ##STR1## wherein R 1 and R 2 independently are hydrogen or lower alkyl having 1 to 4 carbon atoms; R 3 is hydrogen, a lower alkyl group having 1 to 4 carbon atoms and a cyano group; and R 4 is hydrogen or an alkyl group having 1 to 14 carbon atoms, n is the average degree of polymerization, subject to R 4 being a hydrogen atom in at least 5 weight % of the total monomer units, one of groups R 1 and R 2 optionally being carboxyl of the formula --C(═O)--OR 4 and R 3 optionally being a methylene carboxyl group having the formula --CH 2 --C(═O)--OR 4 .
Inventors
- 👤 Dieter Jung
- 👤 Katharina J. Bischof nee Mitrowsky
- 👤 Kai Grimmel
- 👤 Robert R. L. Smolders
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 22:11
CPC Classifications
C; C09; C09J; C09J133/00; C09J133/04; C09J133/06; C09J133/062; C09J133/064; C09J133/08; C09J7/00; C09J7/30; C09J7/38; C09J7/381; C09J7/385; C09J2301/00; C09J2301/30; C09J2301/302; Y; Y10; Y10T; Y10T428/00; Y10T428/28; Y10T428/2809; Y10T428/2852; Y10T428/2878; Y10T428/2891
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
98 words
Screen-printable acrylate pressure-sensitive adhesive composition suitable for adhesive products comprising a solution of about 25 to 225 parts by weight of at least one dissolved inherently tacky pressure-sensitive adhesive which is an essentially non-crosslinked acrylate polymer selected from (meth)acrylic acid ester/(meth)acrylic acid copolymers which have an average molecular weight corresponding to an inherent viscosity of not more than 1.0 dl/g; and 100 parts by weight of an organic solvent or solvent mixture having a low partial vapor pressure of less than about 3 kPa (30 mbar) at 20° C. and a dipole moment of at least 1.0 Debye.
Claim 2
Dependent Claim
98 words
Screen-printable acrylate pressure-sensitive adhesive composition suitable for adhesive products comprising a solution of about 25 to 225 parts by weight of at least one dissolved inherently tacky pressure-sensitive adhesive which is an essentially non-crosslinked acrylate polymer selected from (meth)acrylic acid ester/(meth)acrylic acid copolymers which have an average molecular weight corresponding to an inherent viscosity of not more than 1.0 dl/g; and 100 parts by weight of an organic solvent or solvent mixture having a low partial vapor pressure of less than about 3 kPa (30 mbar) at 20° C. and a dipole moment of at least 1.0 Debye.
Claim 3
Dependent Claim
80 words
A composition as in claim 1, characterized in that the acrylate copolymer has structural units having the general formula ##STR3## wherein R 1 and R 2 independently are hydrogen or lower alkyl having 1 to 4 carbon atoms, R 3 stands for hydrogen, a lower alkyl group having 1 to 4 carbon atoms or a cyano group, R 4 is hydrogen or an alkyl group having 1 to about 14 carbon atoms and n is the mean degree of polymerization.
Claim 4
Dependent Claim
64 words
A composition as in claim 1 characterized in that R 4 is a hydrogen atom in at least 5 weight percent of the total monomer units, at least one of the groups R 1 and R 2 optionally being a carboxyl having the formula --C(═O)--OR 4 , and R 3 optionally being a methylene carboxyl group having the formula --CH 2 --C(═O)--OR 4 .
Claim 5
Dependent Claim
17 words
A composition as in claim 1 characterized in that said acrylate polymer contains a crosslinking component therein.
Claim 6
Dependent Claim
22 words
A composition as in claim 4 characterized in that said crosslinking component is a monoethylenically unsaturated monomer free from orthoaromatic hydroxyl groups.
Claim 7
Dependent Claim
27 words
A composition as in one of claim 1 characterized in that the acrylate polymer has been made by a radically initiated solution polymerization in a polar solvent.
Claim 8
Dependent Claim
28 words
A composition as in claim 6 characterized in that the acrylate polymer was made by radical solution polymerization in the same solvent B in which it was dissolved.
Claim 9
Dependent Claim
25 words
A composition as in claim 1 characterized by having a viscosity in the range of 100 to 7,500 Centipoise at the screen printing temperatures utilized.
Claim 10
Dependent Claim
21 words
A composition as in claim 1 characterized in that the composition contains a UV crosslinking agent or a thermal crosslinking agent.
Claim 11
Dependent Claim
51 words
A composition as in claim 1 characterized in that it additionally contains a tackifier in an amount of 20 to 80 parts by weight relative to 100 parts by weight of solvent, said tackifier being selected preferably from the group comprising the polyol rosin acid ester and hydrogenated rosin acid esters.
Claim 12
Dependent Claim
19 words
A composition as in claim 1 characterized in that it contains additives such as coloring matter, dyes and antioxidants.
Claim 13
Dependent Claim
51 words
A process of making the screen printable acrylate pressure-sensitive adhesive composition according to claim 1, characterized by radically polymerizing a monomer mixture to provide a polymer of group A in a solvent selected from group B, and then crosslinking the copolymer or the polymerized copolymer solution to form a pressure-sensitive adhesive.
Claim 14
Dependent Claim
28 words
A process as in claim 12 characterized in that the polymer of group A is isolated from solvent B and dried before crosslinking to form the pressure-sensitive adhesive.
Claim 15
Dependent Claim
32 words
A process as in claim 12 characterized by using as the solvent an alkyleneglycol diether or an alkyleneglycol monoether having 2 to 6 carbon atoms in the alkylene group, preferably isopropanediol monomethylether.
Claim 16
Dependent Claim
70 words
A screen printed substrate having a screen print of a pressure-sensitive adhesive composition as specified in claim 1 applied to at least a portion of its surface, wherein said pressure-sensitive adhesive composition has been dried and crosslinked and wherein the coat of adhesive has a peel strength of 4 to 20 N/cm and an adhesion in shear higher than 10,000 minutes at temperatures ranging from room temperature to 120° C.
Claim 17
Dependent Claim
72 words
A screen printed substrate having a screen print of a pressure-sensitive adhesive composition as specified in claim 1 applied to at least a portion of its surface, wherein said pressure sensitive adhesive composition has been dried and crosslinked and wherein the water or humidity resistance of the cross-linked pressure-sensitive adhesive is high enough to produce peel strengths in the range of 4 to 20 N/cm in the long-term test at 100% humidity.
Claim 18
Dependent Claim
64 words
A screen-printable acrylate pressure-sensitive adhesive composition comprising a solid essentially non-crosslinked acrylate copolymer dissolved in a polar, low molecular weight solvent wherein: A) said acrylate copolymer has an inherent viscosity of less than 1.0 dl/g, and B) said polar solvent has a partial vapor pressure of less than 3 kPa (30 mbar) at 20° C. and a dipole moment of at least 1 Debye.
Claim 19
Dependent Claim
64 words
A screen-printable acrylate pressure-sensitive adhesive composition comprising a solid essentially non-crosslinked acrylate copolymer dissolved in a polar, low molecular weight solvent wherein: A) said acrylate copolymer has an inherent viscosity of less than 1.0 dl/g, and B) said polar solvent has a partial vapor pressure of less than 3 kPa (30 mbar) at 20° C. and a dipole moment of at least 1 Debye.
Claim 20
Dependent Claim
70 words
A screen-printable pressure-sensitive adhesive composition comprising a solution of (a) from 20 to 225 parts by weight of a non-crosslinked (meth)acrylic acid ester/(meth)acrylic acid copolymer having an inherent viscosity of 1 dl/g or less, and (b) 100 parts by weight of a polar organic solvent having a partial vapor pressure of less than about 3 kPa (30 mbar) at 20° C. and a dipole moment of 1 Debye or more.
Claim 21
Dependent Claim
70 words
A screen-printable pressure-sensitive adhesive composition comprising a solution of (a) from 20 to 225 parts by weight of a non-crosslinked (meth)acrylic acid ester/(meth)acrylic acid copolymer having an inherent viscosity of 1 dl/g or less, and (b) 100 parts by weight of a polar organic solvent having a partial vapor pressure of less than about 3 kPa (30 mbar) at 20° C. and a dipole moment of 1 Debye or more.
Claim 22
Dependent Claim
15 words
A screen-printable adhesive composition according to claim 1 which does not string when screen printed.
References Cited (Backward Citations)
US3607816A
Cited
US3617362A
Cited
US3707518A
Cited
US3740366A
Cited
US4077926A
Cited
US4418120A
Cited
JPS6032869A
Cited
US4587152A
Cited
JPS6248780A
Cited
US4737559A
Cited
JPH0297416A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-08-25 | 1996-02-24 | 1996-08-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-08-25 | 2000-02-24 | 2000-08-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-08-25 | 2004-02-24 | 2004-08-25 | $7700.00 | Window Closed / Lapsed |