Process for fabricating superconducting ceramic materials by HIP treatment
Assignee: Mitsubishi Materials Corp
•
Filing: 1991-04-22
•
Granted: 1992-09-08
•
Expires: 2011-04-22
Abstract
Abstract A process for fabricating worked superconducting ceramic material of a mean grain size not more than 10 um is disclosed, which comprises the steps of: (a) preparing a metal casing containing a starting powder material having a composition for forming an oxide superconductor; (b) calcining the starting powder material contained in the casing at a temperature range of 850° to 950° C.; (c) subjecting said casing to a HIP treatment; (d) subjecting said casing containing hot deformed material to cold deformation processing; and (e) subjecting said casing to stress relief treatment by annealing in the presence of oxygen.
Inventors
- 👤 Takuo Takeshita
- 👤 Sadaaki Hagino
- 👤 Tatsuro Ajima
- 👤 Motokazu Suzuki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 12:27
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/01; H10N60/0268; H10N60/0801; C; C04; C04B; C04B35/00; C04B35/01; C04B35/45; C04B35/4504; C04B35/622; C04B35/64; C04B35/645; C04B35/6455; Y; Y10; Y10S; Y10S505/00; Y10S505/70; Y10S505/704; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49014
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
147 words
A process for fabricating worked superconducting ceramic material of a mean grain size not more than 10 μm, said process comprising the steps of: (a) preparing a metal casing containing a starting powder material having a composition for forming an oxide superconductor, comprising: an oxide of a yttrium-including rare earth element, an oxide of an alkaline metal, and copper oxide,; (b) calcining the starting powder material contained in the casing at a temperature in the range of 850° to 950° C.; (c) subjecting said casing to hot deformation processing at a pressure in the range of 1600 to 1700 atmospheres and at a temperature in the range of 750° to 850° C. for about one hour; (d) subjecting said casing containing hot deformed material to cold deformation processing, including wire drawing; and (e) subjecting said casing to stress relief treatment by annealing in the presence of oxygen.
Claim 2
Dependent Claim
147 words
A process for fabricating worked superconducting ceramic material of a mean grain size not more than 10 μm, said process comprising the steps of: (a) preparing a metal casing containing a starting powder material having a composition for forming an oxide superconductor, comprising: an oxide of a yttrium-including rare earth element, an oxide of an alkaline metal, and copper oxide,; (b) calcining the starting powder material contained in the casing at a temperature in the range of 850° to 950° C.; (c) subjecting said casing to hot deformation processing at a pressure in the range of 1600 to 1700 atmospheres and at a temperature in the range of 750° to 850° C. for about one hour; (d) subjecting said casing containing hot deformed material to cold deformation processing, including wire drawing; and (e) subjecting said casing to stress relief treatment by annealing in the presence of oxygen.
Claim 3
Dependent Claim
23 words
The process of fabricating worked superconducting ceramic material as claimed in claim 1, wherein said step (b) is performed after said step (c).
Claim 4
Dependent Claim
23 words
The process of fabricating worked superconducting ceramic material as claimed in claim 1, wherein said step (b) is performed after said step (d).
Claim 5
Dependent Claim
39 words
The process of fabricating worked superconducting ceramic material as claimed in claim 1, wherein said starting material contains an oxygen supply agent selected from the group consisting of the oxides of silver, copper, tungsten, vanadium, titanium, manganese and molybdenum.
Claim 6
Dependent Claim
32 words
The process of fabricating worked superconducting ceramic material as claimed in claim 1, wherein said starting material consists essentially of non-superconducting powder materials blended in a ratio of a targeted superconducting material.
Claim 7
Dependent Claim
26 words
The process of fabricating worked superconducting ceramic material as claimed in claim 1, wherein said casing is provided with an oxide layer on the inner surface.
Claim 8
Dependent Claim
33 words
The process of fabricating worked superconducting ceramic material as claimed in claim 1, wherein said metal casing is formed of metal selected from the group consisting of silver, copper, aluminum and alloys thereof.
Claim 9
Dependent Claim
23 words
The process of fabricating worked superconducting ceramic material as claimed in claim 1, wherein said step (d) is performed after the step (e).
Claim 10
Dependent Claim
23 words
The process of fabricating worked superconducting ceramic material as claimed in claim 1, wherein said cold deformation processing produces wires and fine rods.
Claim 11
Dependent Claim
30 words
The process of fabricating worked superconducting ceramic material as claimed in claim 1, wherein said annealing is performed at a temperature in the range of 300° C. to 500° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-09-08 | 1996-03-09 | 1996-09-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-09-08 | 2000-03-09 | 2000-09-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-09-08 | 2004-03-09 | 2004-09-08 | $7700.00 | Window Closed / Lapsed |