Selective chemical vapor deposition of tungsten for microdynamic structures
Assignee: Cornell Research Foundation Inc
•
Filing: 1991-09-19
•
Granted: 1992-09-22
•
Expires: 2011-09-19
Abstract
Abstract A selective chemical vapor deposition (CVD) tungsten process is used to fabricate three-dimensional tungsten cantilever beams on a substrate. Two beams form micromechanical tweezers that move in three dimensions by the application of potential differences between the beams, and between the beams and the silicon substrate. A high deposition rate selective tungsten CVD process is used to fabricate beams of greater than 3 micrometers thickness in patterned, CVD silicon dioxide trenches ion-implanted with silicon. Tweezers 200 micrometers in length with a cross section of 2.7 by 2.5 micrometers will close upon application of a voltage of less than 150 volts.
Inventors
- 👤 Noel C. MacDonald
- 👤 Liang-Yuh Chen
- 👤 Zuoying L. Zhang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 21:28
CPC Classifications
H; H02; H02N; H02N1/00; H02N1/002; H02N1/006; H02N1/008; B; B82; B82Y; B82Y15/00; H01; H01H; H01H1/00; H01H1/0094
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
169 words
A method of forming a microdynamic structure, comprising: forming on a top surface of a substrate wafer a first dielectric layer; forming a second layer of silicon dioxide on a top surface of said first layer to produce a composite dielectric wafer; patterning and etching said composite dielectric wafer to produce at least one channel in said wafer, said channel extending partially through said second layer and having a bottom wall in said silicon dioxide layer, the bottom wall being spaced above said top surface of said first layer; implanting silicon in said silicon dioxide bottom wall of said channel; selectively depositing a refractory metal in said channel to fill said channel; depositing an isolation mask on said first layer to and on said refractory metal to mask said refractory metal in said channel; etching said silicon dioxide layer in the region surrounding at least a part of said metal-filled channel to produce a cavity and to free said metal to provide a cantilever beam extending into said cavity.
Claim 2
Independent Claim
169 words
A method of forming a microdynamic structure, comprising: forming on a top surface of a substrate wafer a first dielectric layer; forming a second layer of silicon dioxide on a top surface of said first layer to produce a composite dielectric wafer; patterning and etching said composite dielectric wafer to produce at least one channel in said wafer, said channel extending partially through said second layer and having a bottom wall in said silicon dioxide layer, the bottom wall being spaced above said top surface of said first layer; implanting silicon in said silicon dioxide bottom wall of said channel; selectively depositing a refractory metal in said channel to fill said channel; depositing an isolation mask on said first layer to and on said refractory metal to mask said refractory metal in said channel; etching said silicon dioxide layer in the region surrounding at least a part of said metal-filled channel to produce a cavity and to free said metal to provide a cantilever beam extending into said cavity.
Claim 3
Dependent Claim
11 words
The method of claim 1, further including removing said isolation mask.
Claim 4
Dependent Claim
18 words
The method of claim 2, further including applying a thin film layer of insulating material on said beam.
Claim 5
Dependent Claim
25 words
The method of claim 2, wherein the step of patterning and etching produces two spaced channels, whereby two cantilever beams are produced in said cavity.
Claim 6
Dependent Claim
26 words
The method of claim 4, further including applying an electrical potential across said beams to produce an electrostatic force therebetween for mechanical deflection of said beams.
Claim 7
Dependent Claim
26 words
The method of claim 2, further including applying an electrical potential between said beam and said substrate to produce an electrostatic deflection force on said beam.
Claim 8
Dependent Claim
21 words
The method of claim 6, wherein the step of applying an electrical potential includes applying a step voltage to said beam.
Claim 9
Dependent Claim
29 words
The method of claim 1, wherein the step of depositing a refractory material includes chemical vapor deposition of tungsten, said tungsten seeding on said implanted silicon in said channel.
Claim 10
Dependent Claim
37 words
The method of claim 8, wherein the step of patterning and etching includes forming a third layer of silicon nitride on the top surface of said second layer, said third layer forming a mask for said channel.
Claim 11
Independent Claim
146 words
A method of forming a microdynamic structure comprising: providing a wafer including an insulating layer covered by a tungsten seeding layer: depositing a layer of silicon dioxide on said tungsten seeding layer; etching through said layer of silicon dioxide at least one elongated channel having a bottom wall formed by said tungsten seeding layer, said channel serving as a mold for formation of said microdynamic structure; selectively depositing tungsten by chemical vapor deposition in said channel, said tungsten seeding in said channel on said bottom wall of said channel and filling said channel to form an elongated tungsten structure in said silicon dioxide layer; and selectively removing a portion of said silicon dioxide layer surrounding said tungsten-filled channel to form a cavity around at least a part of said tungsten structure to release said structure and to form a cantilever tungsten beam extending into said cavity.
Claim 12
Independent Claim
146 words
A method of forming a microdynamic structure comprising: providing a wafer including an insulating layer covered by a tungsten seeding layer: depositing a layer of silicon dioxide on said tungsten seeding layer; etching through said layer of silicon dioxide at least one elongated channel having a bottom wall formed by said tungsten seeding layer, said channel serving as a mold for formation of said microdynamic structure; selectively depositing tungsten by chemical vapor deposition in said channel, said tungsten seeding in said channel on said bottom wall of said channel and filling said channel to form an elongated tungsten structure in said silicon dioxide layer; and selectively removing a portion of said silicon dioxide layer surrounding said tungsten-filled channel to form a cavity around at least a part of said tungsten structure to release said structure and to form a cantilever tungsten beam extending into said cavity.
Claim 13
Dependent Claim
17 words
The method of claim 10, further including applying an electrical insulator to the surface of said beam.
Claim 14
Dependent Claim
22 words
The method of claim 10, wherein the step of forming a cavity further includes removing said seeding layer from within said cavity.
Claim 15
Dependent Claim
21 words
The method of claim 10, further including applying a conformal coating of an electrically insulating oxide to surfaces of said beam.
Claim 16
Dependent Claim
18 words
The method of claim 10, further including applying conformal coating of silicon dioxide to surfaces of said beam.
References Cited (Backward Citations)
US3039897A
Cited
US3641373A
Cited
US3769531A
Cited
US3672985A
Cited
US3835338A
Cited
US4011144A
Cited
US4203128A
Cited
US4319397A
Cited
US4348650A
Cited
JPS5710270A
Cited
US4381672A
Cited
GB2101404A
Cited
US4983535A
Cited
US4516148A
Cited
US4654555A
Cited
US4517486A
Cited
US4959515A
Cited
US4706374A
Cited
US4835585A
Cited
US4570139A
Cited
US4772928A
Cited
US4788158A
Cited
JPS62232171A
Cited
US4697118A
Cited
US4776924A
Cited
US4754185A
Cited
JPS63136982A
Cited
US4746621A
Cited
US4805033A
Cited
US4789803A
Cited
US4906840A
Cited
US4956619A
Cited
US5057450A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-09-22 | 1996-03-23 | 1996-09-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-09-22 | 2000-03-23 | 2000-09-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-09-22 | 2004-03-23 | 2004-09-22 | $7700.00 | Window Closed / Lapsed |