Method of preparing a heat shrinkable, elastic, glueable polyethylene and ethylene vinyl acetate film
Assignee: JPMorgan Chase Bank NA
•
Filing: 1989-11-07
•
Granted: 1992-10-20
•
Expires: 2009-11-07
Abstract
Abstract A process is provided for producing a novel two layered or three-layered film of polyethylene and ethylene vinyl acetate copolymer which is heat shrinkable, and after heat shrinking, is elastic and glueable. The process involves uniaxially stretching under controlled, relatively low temperature conditions.
Inventors
- 👤 Everson Amaral
- 👤 Ralf Korpman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 12:02
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/06; B32B27/08; B32B27/18; B32B27/20; B32B27/30; B32B27/306; B32B27/32; B32B37/00; B32B37/14; B32B37/15; B32B37/153; B32B2323/00; B32B2323/04; B32B2323/046
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
241 words
A process for the preparation of a heat shrinkable film which in its heat shrunk state is elastic and glueable, said process comprising the step of: uniaxially stretching a starting film to an extent such that the stretch ratio is in the range of about 3:1 to 6:1, said stretching being accomplished while maintaining said film at a temperature in the range of about 20° to about 50° C., said starting film having a pair of opposed outside layers, and a thickness in the range of about 3 to about 7 mils, said starting film consisting of at least two interbonded layers and not more than three interbonded layers, one said layer of said starting film comprising a low density polyethylene polymer, a second said layer of said starting film comprising an ethylene/vinyl acetate copolymer having a molecular weight in the range of about 10,000 to about 75,000, said ethylene/vinyl acetate copolymer consisting of about 72 to about 91 weight percent ethylene, and, correspondingly, about 9 to about 28 weight percent vinyl acetate, and when said starting film contains a third said layer, said third layer comprises a low density polyethylene polymer and said second layer is positioned between said first layer and said third layer, and wherein the ratio of the thickness of each one of said first layer and of said third layer when present to said second layer is in the range of about 1:5 to about 1:20.
Claim 2
Dependent Claim
241 words
A process for the preparation of a heat shrinkable film which in its heat shrunk state is elastic and glueable, said process comprising the step of: uniaxially stretching a starting film to an extent such that the stretch ratio is in the range of about 3:1 to 6:1, said stretching being accomplished while maintaining said film at a temperature in the range of about 20° to about 50° C., said starting film having a pair of opposed outside layers, and a thickness in the range of about 3 to about 7 mils, said starting film consisting of at least two interbonded layers and not more than three interbonded layers, one said layer of said starting film comprising a low density polyethylene polymer, a second said layer of said starting film comprising an ethylene/vinyl acetate copolymer having a molecular weight in the range of about 10,000 to about 75,000, said ethylene/vinyl acetate copolymer consisting of about 72 to about 91 weight percent ethylene, and, correspondingly, about 9 to about 28 weight percent vinyl acetate, and when said starting film contains a third said layer, said third layer comprises a low density polyethylene polymer and said second layer is positioned between said first layer and said third layer, and wherein the ratio of the thickness of each one of said first layer and of said third layer when present to said second layer is in the range of about 1:5 to about 1:20.
Claim 3
Dependent Claim
49 words
The process of claim 1 wherein said starting film structure consists of three said layers, and wherein each of said first and said third layers thereof additionally has incorporated thereinto up to about 50 weight percent of said ethylene vinyl acetate copolymer on a total respective layer weight basis.
Claim 4
Dependent Claim
41 words
The process of claim 1 wherein said starting film consists of three said layers and wherein each of said first and said third layers thereof additionally has incorporated thereinto up to about 10 weight percent of a filler based antiblocking agent.
Claim 5
Dependent Claim
71 words
The process of claim 1 wherein said starting film consists of three layers and wherein each of said first and said third layers thereof is comprised on a 100 weight percent layer basis of about 50 to about 100 weight percent of a low density polyethylene polymer, 0 to about 50 weight percent of said ethylene/vinyl acetate copolymer, and 0 to about 10 weight percent of a filler based antiblocking agent.
Claim 6
Dependent Claim
29 words
The process of claim 1 wherein said film is heat set while in its stretched state at a temperature in the range of about 38° to about 55° C.
Claim 7
Dependent Claim
22 words
The process of claim 5 wherein said heat setting is accomplished in a time range of about 5 to about 15 seconds.
Claim 8
Dependent Claim
15 words
The process of claim 1 wherein said uniaxial stretching is carried out using a tenter.
Claim 9
Dependent Claim
13 words
The process of claim 1 wherein said starting film is prepared by coextrusion.
Claim 10
Dependent Claim
26 words
The process of claim 1 wherein said uniaxial stretching is carried out in a direction which is transverse relative to the continuous length of said film.
Claim 11
Dependent Claim
34 words
The process of claim 9 wherein said heat shrinkable film is slit in the direction of said continuous length to provide a plurality of elongated strips which are each convolutely wound into a roll.
Claim 12
Dependent Claim
45 words
The process of claim 9 wherein said heat shrinkable film is first convolutely wound into a roll and then said roll is cut at each of a plurality of transversely spaced locations, thereby to provide a plurality of smaller rolls of said product film structure.
Claim 13
Dependent Claim
45 words
The process of claim 11 wherein each of said smaller rolls is cut by a successive series of longitudinally spaced, parallel sequential transverse cuts, thereby to provide a plurality of generally rectangularly configured film segments which are each heat shrinkable in their respective elongated directions.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-10-20 | 1996-04-20 | 1996-10-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-10-20 | 2000-04-20 | 2000-10-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-10-20 | 2004-04-20 | 2004-10-20 | $7700.00 | Window Closed / Lapsed |