Coating blend compositions
Assignee: Henniges Automotive Sealing Systems North America Inc
•
Filing: 1991-06-06
•
Granted: 1993-06-22
•
Expires: 2011-06-06
Abstract
Abstract A coating blend composition is a physical admixture of an adhesion promoter resin and a coating material resin. The blend can be cured by one or more curing agents existing within either the adhesion promoter resin, the coating material resin, or both. The utilization of such a blend eliminates the need for priming a substrate such as a rubber, or a thermoplastic or a thermoset polyolefin. The adhesion promoter resin is a urethane composition containing a blocked polyurethane prepolymer whereas the coating material resin can generally be any compound which has a functional or cosmetic purpose such as a different type of blocked polyurethane, and is generally utilized in a major amount. A particular application of the coating blend compositions of the present invention is to a glass run channel made from, for example, EPDM, as in an automotive door.
Inventors
- 👤 Kohji Y. Chihara
- 👤 James R. Goewey
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 16:53
CPC Classifications
C; C09; C09D; C09D175/00; C09D175/04; B; B60; B60J; B60J10/00; B60J10/15; B60J10/17; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/10; C08G18/28; C08G18/40; C08G18/62; C08G18/6204; C08G18/6208; C08L; C08L75/00; C08L75/04; C09D201/00
Claims Analysis
Total Claims: 40
Claim 1
Independent Claim
34 words
A coating blend composition, comprising: a physical blend of a coating material resin and an effective amount of a blocked polyurethane prepolymer adhesion promoter resin capable of securing said coating blend to a substrate.
Claim 2
Dependent Claim
34 words
A coating blend composition, comprising: a physical blend of a coating material resin and an effective amount of a blocked polyurethane prepolymer adhesion promoter resin capable of securing said coating blend to a substrate.
Claim 3
Dependent Claim
107 words
A coating blend composition, according to claim 1,, wherein the precursor of the polyurethane prepolymer is the reaction product of a hydroxyl functional hydrogenated polydiene or polyolefin intermediate with at least 1.8 equivalents of a polyisocyanate for each equivalent of said hydroxyl functional hydrocarbon intermediate, said hydrogenated polydiene or polyolefin having greater than 1.5 hydroxyl groups per average intermediate molecule and a number average molecular weight of from about 500 to about 15,000, and said precursor polyurethane prepolymer being blocked with a blocking agent, wherein said coating material resin is a polyolefin, an epoxy, an acrylate, a phenolic resin, a melamine-containing polymer, or a blocked polyurethane prepolymer.
Claim 4
Dependent Claim
28 words
A coating blend composition, according to claim 2, wherein said coating material resin polyurethane is made from a hydroxyl-terminated polyester intermediate, a hydroxyl-terminated polyether intermediate, or combinations thereof.
Claim 5
Dependent Claim
102 words
A coating blend composition, according to claim 3, wherein said polyisocyanate of said adhesion promoter resin has the formula ##STR11## wherein n is 2, 3, or 4 and R is aromatic, aliphatic, or combinations thereof, having from 4 to 100 carbon atoms, and wherein said hydroxyl functional hydrogenated polydiene or polyolefin is mad-e by polymerizing an olefin monomer having from 2 to 6 carbon atoms, or a diene monomer having from 4 to 10 carbon atoms, and optionally, up to 50 mole percent of an ethylenically unsaturated comonomer, and optionally wherein said hydrogenated diene polymer is at least 50 mole percent hydrogenated.
Claim 6
Dependent Claim
35 words
A coating blend composition, according to claim 4, wherein said hydroxyl functional hydrogenated diene polymer is at least 95 mole percent hydrogenated, and wherein R of said polyisocyanate has from 4 to 30 carbon atoms.
Claim 7
Dependent Claim
87 words
A coating blend composition, according to claim 5, wherein the equivalent ratio of said polyisocyanate to said hydroxyl functional hydrogenated diene polymer or polyolefin is from about 2.0 to about 8.0, wherein the molecular weight of said hydroxyl functional hydrogenated diene polymer or polyolefin is from about 1,000 to about 8,000, wherein said hydroxyl functional hydrocarbon intermediate has from about 1.8 to about 6.0 hydroxyl groups per average intermediate molecule, wherein said polyisocyanate is 4,4-methylene diphenyl isocyanate, 2,4-toluene diisocyanate, 2,6-toluene diisocyanate, or 1,4-phenylene diisocyanate, or mixtures thereof.
Claim 8
Dependent Claim
74 words
A coating blend composition, according to claim 6, wherein the molecular weight of said hydroxyl functional hydrocarbon intermediate is from about 1,000 to about 8,000, wherein said hydroxyl functional hydrogenated polydiene or polyolefin has the approximate formula ##STR12## wherein the x and y units are randomly distributed, wherein the x/y ratio is from 0.10 to about 10.0 and wherein the average number of OH groups per molecule is from about 1.5 to about 4.0.
Claim 9
Dependent Claim
43 words
A coating blend composition, according to claim 3, wherein said coating material resin is said polyurethane prepolymer derived from said polyester intermediate, said polyether intermediate, or combinations thereof, and wherein said intermediate has a molecular weight of from about 5,000 to about 15,000.
Claim 10
Dependent Claim
111 words
A coating blend composition, according to claim 5, wherein said coating material resin is said polyurethane prepolymer derived from said polyester intermediate, said polyether intermediate, or combinations thereof, wherein said intermediate has a molecular weight of from about 5,000 to about I5,000, and wherein said blocked polyurethane prepolymer is the reaction product of said intermediate and a polyisocyanate wherein said polyisocyanate has the formula ##STR13## where n is from about 1.8 to about 4, and wherein R is an aliphatic having from 2 to 20 carbon atoms, a cycloaliphatic having from 4 to about 20 carbon atoms, an aromatic having from about 6 to about 20 carbon atoms, or combinations thereof.
Claim 11
Dependent Claim
100 words
A coating blend composition, according to claim 7, wherein said coating material resin is said polyurethane prepolymer derived from said polyester intermediate, said polyether intermediate, or combinations thereof, wherein said intermediate has a molecular weight of from about 5,000 to about 15,000, wherein said blocked polyurethane prepolymer is the reaction product of said intermediate and a polyisocyanate wherein said polyisocyanate is toluene diisocyanate or methylenediphenyl isocyanate, wherein said polyether intermediate is made from ethylene oxide or propylene oxide, and wherein said polyester intermediate is made from adipic acid, terephthalic acid, or phthalic acid, and wherein said glycol is hexamethylene glycol.
Claim 12
Dependent Claim
47 words
A coating blend composition, according to claim 1, including a curing agent, said curing agent comprising an equivalent excess of a polyisocyanate compound, a crosslinking agent, a polyol containing three or more hydroxyl groups therein, a polyisocyanate having three or more isocyanate groups therein, or combinations thereof.
Claim 13
Dependent Claim
49 words
A coating blend composition, according to claim 8, including a curing agent, said curing agent comprising an equivalent excess of said polyisocyanate compound, a crosslinking agent, a polyol containing three or more hydroxyl groups therein, a polyamine, a polyisocyanate having three or more isocyanate groups therein, and combinations thereof.
Claim 14
Dependent Claim
49 words
A coating blend composition, according to claim 10, including a curing agent, said curing agent comprising an equivalent excess of said polyisooyanate compound, a crosslinking agent, a polyol containing three or more hydroxyl groups therein, a polyamine, a polyisocyanate having three or more isocyanate groups therein, and combinations thereof.
Claim 15
Dependent Claim
12 words
A cured coating blend composition comprising the cured composition of claim 1.
Claim 16
Dependent Claim
12 words
A cured coating blend composition comprising the cured composition of claim 5.
Claim 17
Dependent Claim
12 words
A cured coating blend composition comprising the cured composition of claim 7.
Claim 18
Dependent Claim
12 words
A cured coating blend composition comprising the cured composition of claim 8.
Claim 19
Dependent Claim
12 words
A cured coating blend composition comprising the cured composition of claim 9.
Claim 20
Dependent Claim
12 words
A cured coating blend composition comprising the cured composition of claim 10.
Claim 21
Dependent Claim
12 words
A cured coating blend composition comprising the cured composition of claim 11.
Claim 22
Dependent Claim
12 words
A cured coating blend composition comprising the cured composition of claim 12.
Claim 23
Dependent Claim
12 words
A cured coating blend composition comprising the cured composition of claim 13.
Claim 24
Dependent Claim
23 words
A coated substrate, comprising: a cured coating composition secured to said substrate, said cured coating composition being the cured composition of claim 1.
Claim 25
Dependent Claim
23 words
A coated substrate, comprising: a cured coating composition secured to said substrate, said cured coating composition being the cured composition of claim 6.
Claim 26
Dependent Claim
23 words
A coated substrate, comprising: a cured coating composition secured to said substrate, said cured coating composition being the cured composition of claim 8.
Claim 27
Dependent Claim
35 words
A coated substrate, comprising: a cured coating composition secured to said substrate, said cured coating composition being the cured composition of claim 9, and wherein said substrate is a rubber substrate or a polyolefin substrate.
Claim 28
Dependent Claim
30 words
A coated substrate, comprising: a cured coating composition secured to said substrate, said cured coating composition being the cured composition of claim 10, and wherein said cured substrate is EPDM.
Claim 29
Dependent Claim
10 words
A glass run channel comprising the composition of claim 23.
Claim 30
Dependent Claim
10 words
A glass run channel comprising the composition of claim 25.
Claim 31
Dependent Claim
10 words
A glass run channel comprising the composition of claim 27.
Claim 32
Dependent Claim
31 words
A process for preparing a physical blend capable of adhering to a substrate, comprising, forming a physical blend of a blocked polyurethane prepolymer adhesion promoter resin and a coating material resin.
Claim 33
Dependent Claim
31 words
A process for preparing a physical blend capable of adhering to a substrate, comprising, forming a physical blend of a blocked polyurethane prepolymer adhesion promoter resin and a coating material resin.
Claim 34
Dependent Claim
81 words
A process according to claim 31, including forming said adhesion promoter resin by reacting a hydroxyl functional hydrogenated polydiene or polyolefin with at least 1.8 equivalents of a polyisocyanate for each equivalent of said hydrogenated polydiene or polyolefin to form a prepolymer, said hydrogenated polydiene or polyolefin having at least 1.5 hydroxyl groups per average molecule and a number average molecular weight of from about 500 to about 15,000, and blocking said prepolymer to form a blocked adhesion promoter prepolymer resin.
Claim 35
Dependent Claim
41 words
A process according to claim 32, wherein said coating material resin is said polyurethane prepolymer derived from said polyester intermediate, said polyether intermediate, or combinations thereof, and wherein said intermediate has a molecular weight of from about 5,000 to about 15,000.
Claim 36
Dependent Claim
63 words
A cured coating blend composition, comprising the reaction product of a coating material resin, an effective amount of a blocked polyurethane prepolymer adhesion promoter resin capable of securing said coating blend to a substrate, and from about 0.5 to about 50 parts by weight of a curing agent based upon the total weight of said coating material resin and said adhesion promoter resin.
Claim 37
Dependent Claim
63 words
A cured coating blend composition, comprising the reaction product of a coating material resin, an effective amount of a blocked polyurethane prepolymer adhesion promoter resin capable of securing said coating blend to a substrate, and from about 0.5 to about 50 parts by weight of a curing agent based upon the total weight of said coating material resin and said adhesion promoter resin.
Claim 38
Dependent Claim
83 words
A cured coating blend composition, according to claim 34, wherein said coating material resin is a polyurethane prepolymer derived from a polyester intermediate, said polyether intermediate, or combinations thereof, and wherein said intermediate has a molecular weight of from about 5,000 to about 15,000, and wherein said curing agent comprises an equivalent excess of said polyisocyanate compound, a crosslinking agent, a polyol containing three or more hydroxyl groups therein, a polyamine, a polyisocyanate having three or more isocyanate groups therein, and combinations thereof.
Claim 39
Dependent Claim
113 words
A cured coating blend composition, according to claim 35, wherein said coating material resin is said polyurethane prepolymer derived from said polyester intermediate, said polyether intermediate, or combinations thereof, and wherein said intermediate has a molecular weight of from about 5,000 to about 15,000, and wherein said blocked polyurethane prepolymer is the reaction product of said intermediate and a polyisocyanate wherein said polyisocyanate has the formula ##STR14## where n is from about 1.8 to about 4, and wherein R is an aliphatic having from 2 to 20 carbon atoms, a cycloaliphatic having from 4 to about 20 carbon atoms, an aromatic having from about 6 to about 20 carbon atoms, or combinations thereof.
Claim 40
Dependent Claim
103 words
A cured coating blend composition, according to claim 35, wherein said coating material resin is said polyurethane prepolymer derived from said polyester intermediate, said polyether intermediate, or combinations thereof, and wherein said intermediate has a molecular weight of from about 5,000 to about 15,000, and wherein said blocked polyurethane prepolymer is the reaction product of said intermediate and a polyisocyanate wherein said polyisocyanate is toluene diisocyanate or methylenediphenyl isocyanate, wherein said polyether intermediate is made from ethylene oxide or propylene oxide, and wherein said polyester intermediate is made from adipic acid, terephthalic acid, or phthalic acid, and wherein said glycol is hexamethylene glycol.
References Cited (Backward Citations)
US4101530A
Cited
US4267206A
Cited
US4606974A
Cited
JPS59201838A
Cited
JPS6024821A
Cited
JPS60173011A
Cited
JPS60179251A
Cited
JPS60181137A
Cited
US4631206A
Cited
JPS61136528A
Cited
JPS61137735A
Cited
JPS60179470A
Cited
JPS6241215A
Cited
JPS63130616A
Cited
US4856502A
Cited
JPS646017A
Cited
US4898919A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-06-21 | 1996-12-21 | 1997-06-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-06-21 | 2000-12-21 | 2001-06-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-06-21 | 2004-12-21 | 2005-06-22 | $7700.00 | Window Closed / Lapsed |