Method of manufacturing gradient index optical elements
Assignee: Olympus Corp
•
Filing: 1992-02-18
•
Granted: 1993-09-14
•
Expires: 2012-02-18
Abstract
Abstract A method of manufacturing a gradient index optical element comprises preparing a sol using silicon alkoxide and an aqueous metal salt solution as a source of index-modifying cations. The sol is treated to obtain a wet gel. Metal salt from the wet gel is eluted by immersing the wet gel in a solvent to produce a concentration gradiation of the metal salt in the wet gel. The metal salt is fixed in the wet gel by immersing the wet gel in a solvent. The steps of eluting and fixing are repeated so that a gradient index optical element is produced having a large difference in refractive index between the outer periphery portion and the center of the gel.
Inventors
- 👤 Minoru Inami
- 👤 Masayuki Yamane
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 21:47
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/02; G02B6/028; G02B6/0288; C; C03; C03C; C03C1/00; C03C1/006; G02B3/00; G02B3/0087
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
113 words
A method of manufacturing gradient index optical elements utilizing a sol-gel process, comprising the steps of: (a) preparing a sol using silicon alkoxide and an aqueous metal salt solution as a source of refractive index-modifying cations, subjecting said sol to a gelling treatment to obtain a wet gel, and immersing said gel in a solvent to fix said metal salt in said gel; and (b) immersing said wet gel in a solvent to dissolve said metal salt and elute said metal salt outside said gel thereby producing a concentration gradient of said metal salt in said gel, and thereafter immersing said gel in a solvent to fix said metal salt in said gel.
Claim 2
Independent Claim
113 words
A method of manufacturing gradient index optical elements utilizing a sol-gel process, comprising the steps of: (a) preparing a sol using silicon alkoxide and an aqueous metal salt solution as a source of refractive index-modifying cations, subjecting said sol to a gelling treatment to obtain a wet gel, and immersing said gel in a solvent to fix said metal salt in said gel; and (b) immersing said wet gel in a solvent to dissolve said metal salt and elute said metal salt outside said gel thereby producing a concentration gradient of said metal salt in said gel, and thereafter immersing said gel in a solvent to fix said metal salt in said gel.
Claim 3
Dependent Claim
55 words
A method according to claim 1; wherein step (b) is repeated a plurality of times, and the time duration the first time the wet gel is immersed in the solvent to dissolve said metal salt is longer than the time duration of a subsequent time the wet gel is immersed to dissolve said metal salt.
Claim 4
Dependent Claim
42 words
A method according to claim 2; wherein the time duration of the first time the wet gel is immersed in the solvent to dissolve the metal salt is long enough for the solvent to reach a center portion of the wet gel.
Claim 5
Dependent Claim
43 words
A method according to claim 3; wherein the time duration of each subsequent time the wet gel is immersed in the solvent to dissolve the metal salt is not long enough for the solvent to reach the center portion of the wet gel.
Claim 6
Dependent Claim
15 words
A method according to claim 1; further comprising (c) drying and sintering the wet gel.
Claim 7
Independent Claim
96 words
A method of manufacturing a gradient index optical element, comprising the step of: preparing a sol by using silicon alkoxide and at least one aqueous metal salt solution as a source of refractive index-modifying cations; treating the sol to a gelling treatment to obtain a wet gel; eluting some of the metal salt from the wet gel by immersing the wet gel in a solvent to produce a concentration gradient of the metal salt in the wet gel; and then fixing the metal salt in the wet gel by immersing the wet gel in a solvent.
Claim 8
Independent Claim
96 words
A method of manufacturing a gradient index optical element, comprising the step of: preparing a sol by using silicon alkoxide and at least one aqueous metal salt solution as a source of refractive index-modifying cations; treating the sol to a gelling treatment to obtain a wet gel; eluting some of the metal salt from the wet gel by immersing the wet gel in a solvent to produce a concentration gradient of the metal salt in the wet gel; and then fixing the metal salt in the wet gel by immersing the wet gel in a solvent.
Claim 9
Dependent Claim
54 words
A method of manufacturing a gradient index optical element according to claim 6; wherein the steps of eluting and fixing are repetitively performed, and the first time the eluting step is performed the wet gel is immersed in the solvent for a longer time period than in subsequent times the eluting step is performed.
Claim 10
Dependent Claim
45 words
A method of manufacturing a gradient index optical element according to claim 6; wherein the step of eluting comprises immersing the wet gel in the solvent for a time at least long enough for the solvent to reach a center portion of the wet gel.
Claim 11
Dependent Claim
94 words
A method of manufacturing a gradient index optical element according to claim 6; wherein the steps of eluting and fixing are repetitively performed, and the first time the eluting step is performed the wet gel is immersed in the solvent for a time at least long enough for the solvent to reach a center portion of the wet gel, and each subsequent time the eluting step is performed the wet gel is immersed in the solvent for a time not long enough for the solvent to reach the center portion of the wet gel.
Claim 12
Dependent Claim
28 words
A method of manufacturing a gradient index optical element according to claim 6; further comprising the steps of drying the wet gel; and sintering the dried wet gel.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-09-13 | 1997-03-15 | 1997-09-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-09-13 | 2001-03-15 | 2001-09-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-09-13 | 2005-03-15 | 2005-09-14 | $7700.00 | Window Closed / Lapsed |