Method for manufacturing biodegradable high molecular aliphatic polyester
Assignee: Resonac Holdings Corp
•
Filing: 1993-06-01
•
Granted: 1994-05-10
•
Expires: 2013-06-01
Abstract
Abstract A method for manufacturing a biodegradable high molecular weight aliphatic polyester. This method comprises the steps of: [A] synthesizing an aliphatic polyester having a number average molecular weight of at least 5,000 and/or a weight average molecular weight of at least 30,000 by reacting aliphatic or alicyclic glycol with aliphatic dicarboxylic acid or its anhydride, applying a 0.001-0.5 part by weight of organic or inorganic metallic compound as a catalyst with respect to 100 parts by weight of aliphatic polyester to be produced; [B] adding a 0.01-3 parts by weight of organic or inorganic phosphorus compound with respect to 100 parts by weight of aliphatic polyester upon completion of the reaction; and [C] reacting a 0.1-5 parts by weight of polyvalent isocyanate compound with 100 parts by weight of the aliphatic polyester so that the polyester has a number average molecular weight of at least 10,000 and/or a weight average molecular weight of at least 50,000.
Inventors
- 👤 Eiichiro Takiyama
- 👤 Takashi Fujimaki
- 👤 Shigekatu Seki
- 👤 Takao Hokari
- 👤 Yoshitaka Hatano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 22:27
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/42; C08G18/4236; C08G18/4238; C08G18/4205; C08G18/423; C08G18/4241; C08G63/00; C08G63/02; C08G63/12; C08G63/16; C08G63/91; C08G63/914; C08G63/916; C08G2230/00
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
131 words
A method for manufacturing a biodegradable high molecular weight aliphatic polyester comprising the steps of: synthesizing an aliphatic polyester having a number average molecular weight of at least 5,000 by reacting aliphatic or alicyclic glycol with aliphatic dicarboxylic acid or its anhydride, applying a 0.001-0.5 part by weight of organic or inorganic metallic compound as a catalyst with respect to 100 parts by weight of aliphatic polyester to be produced; adding a 0.01-3 parts by weight of organic or inorganic phosphorus compounds with respect to 100 parts by weight of aliphatic polyester upon completion of the reaction; and reacting a 0.1-5 parts by weight of polyfunctional isocyanate compound with 100 parts by weight of the aliphatic polyester so that the polyester has a number average molecular weight of at least 10,000.
Claim 2
Independent Claim
131 words
A method for manufacturing a biodegradable high molecular weight aliphatic polyester comprising the steps of: synthesizing an aliphatic polyester having a number average molecular weight of at least 5,000 by reacting aliphatic or alicyclic glycol with aliphatic dicarboxylic acid or its anhydride, applying a 0.001-0.5 part by weight of organic or inorganic metallic compound as a catalyst with respect to 100 parts by weight of aliphatic polyester to be produced; adding a 0.01-3 parts by weight of organic or inorganic phosphorus compounds with respect to 100 parts by weight of aliphatic polyester upon completion of the reaction; and reacting a 0.1-5 parts by weight of polyfunctional isocyanate compound with 100 parts by weight of the aliphatic polyester so that the polyester has a number average molecular weight of at least 10,000.
Claim 3
Independent Claim
130 words
A method for manufacturing a biodegradable high molecular weight aliphatic polyester comprising the steps of: synthesizing an aliphatic polyester having a weight average molecular weight of at least 30,000 by reacting aliphatic or alicyclic glycol with aliphatic dicarboxylic acid or its anhydride, applying a 0.001-0.5 part by weight of organic or inorganic metallic compound as a catalyst with respect to 100 parts by weight of aliphatic polyester to be produced; adding a 0.01-3 parts by weight of organic or inorganic phosphorus compound with respect to 100 parts by weight of aliphatic polyester completion of the reaction; and reacting a 0.1-5 parts by weight of polyfunctional isocyanate compound with 100 parts by weight of the aliphatic polyester so that the polyester has a weight average molecular weight of at least 50,000.
Claim 4
Independent Claim
130 words
A method for manufacturing a biodegradable high molecular weight aliphatic polyester comprising the steps of: synthesizing an aliphatic polyester having a weight average molecular weight of at least 30,000 by reacting aliphatic or alicyclic glycol with aliphatic dicarboxylic acid or its anhydride, applying a 0.001-0.5 part by weight of organic or inorganic metallic compound as a catalyst with respect to 100 parts by weight of aliphatic polyester to be produced; adding a 0.01-3 parts by weight of organic or inorganic phosphorus compound with respect to 100 parts by weight of aliphatic polyester completion of the reaction; and reacting a 0.1-5 parts by weight of polyfunctional isocyanate compound with 100 parts by weight of the aliphatic polyester so that the polyester has a weight average molecular weight of at least 50,000.
Claim 5
Independent Claim
150 words
A method for manufacturing a biodegradable high molecular weight aliphatic polyester comprising the steps of: synthesizing an aliphatic polyester having a number average molecular weight of at least 5,000 and a weight average molecular weight of at least 30,000 by reacting aliphatic or alicyclic qlycol with aliphatic dicarboxylic acid or its anhydride, applying 0.001-0.5 part by weight of organic or inorganic metallic compound as a catalyst with respect to 100 parts by weight of aliphatic polyester to be produced adding a 0.01-3 parts by weight of organic or inorganic phosphorus compound with respect to 100 parts by weight of aliphatic polyester upon completion of the reaction; and reacting a 0.1-5 parts by weight of polyfunctional isocyanate compound with 100 parts by weight of the aliphatic polyester so that the polyester has a number average molecular weight of at least 10,000 and a weight average molecular weight of at least 50,000.
Claim 6
Independent Claim
150 words
A method for manufacturing a biodegradable high molecular weight aliphatic polyester comprising the steps of: synthesizing an aliphatic polyester having a number average molecular weight of at least 5,000 and a weight average molecular weight of at least 30,000 by reacting aliphatic or alicyclic qlycol with aliphatic dicarboxylic acid or its anhydride, applying 0.001-0.5 part by weight of organic or inorganic metallic compound as a catalyst with respect to 100 parts by weight of aliphatic polyester to be produced adding a 0.01-3 parts by weight of organic or inorganic phosphorus compound with respect to 100 parts by weight of aliphatic polyester upon completion of the reaction; and reacting a 0.1-5 parts by weight of polyfunctional isocyanate compound with 100 parts by weight of the aliphatic polyester so that the polyester has a number average molecular weight of at least 10,000 and a weight average molecular weight of at least 50,000.
Claim 7
Independent Claim
81 words
A method for manufacturing a biodegradable high molecular weight aliphatic polyester according to any one of claims 1-3, wherein at least one kind of multifunctional compound selected from a group consisted of polyhydric alcohol having at least three functional groups, polybasic carboxylic acid having at least three functional groups or its anhydride, and oxycarboxylic acid having at least three functional groups, at the reaction of the aliphatic or alicyclic glycol with the aliphatic dicarboxylic acid or its anhydride in the step.
References Cited (Backward Citations)
US4990594A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-05-09 | 1997-11-08 | 1998-05-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-05-09 | 2001-11-08 | 2002-05-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-05-09 | 2005-11-08 | 2006-05-10 | $7700.00 | Window Closed / Lapsed |