Colored polymeric dielectric particles and method of manufacture
Assignee: AUO Corp
•
Filing: 1994-05-11
•
Granted: 1996-03-12
•
Expires: 2014-05-11
Abstract
Abstract A process for forming dielectric particles includes admixing a vinyl halide monomer and a crosslinker in a liquid dispersion medium to form a first mixture. A second mixture of an initiator and a stabilizer is prepared and added to the first mixture to form a third mixture in which the monomer polymerizes to form white crystalline polymer particles which are sonified for uniformity. The particles may be stained by exposure to a dehydrohalegenation reagent and dispersed in an electrophoretic fluid for use in an electrophoretic display.
Inventors
- 👤 Wei-Hsin Hou
- 👤 Thomas B. Lloyd
- 👤 Frederic E. Schubert
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 23:00
CPC Classifications
G; G03; G03G; G03G17/00; G03G17/04; G02; G02F; G02F1/00; G02F1/01; G02F1/165; G02F1/166; G02F1/167; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
157 words
A process for forming dielectric particles used in electrophoretic fluid, comprising: polymerizing a monomer selected from the group consisting of vinyl halide monomers and vinyl monomers having the formula ##STR2## where X is selected from the group consisting of a halide, carboxyl, ether trialkylammonio, acetate, diazoniodialkylsulfonio, cyano, and oxyl imino using dispersion polymerization to form irregularly-shaped crystalline polymer particles, and where n is selected as H or X; wherein said step of polymerizing includes: (a) admixing said monomer and a crosslinker in a dispersion medium to form a first mixture; (b) preparing a second mixture of an initiator and a dispersion stabilizer for retarding the coagulation of said particles during said polymerization; (c) adding said first mixture to said second mixture to form a third mixture and allowing said monomer to polymerize to form said irregularly-shaped crystalline polymer particles; and (d) sonifying said third mixture after polymerizing to make said irregularly-shaped crystalline polymer particles uniform in size.
Claim 2
Dependent Claim
157 words
A process for forming dielectric particles used in electrophoretic fluid, comprising: polymerizing a monomer selected from the group consisting of vinyl halide monomers and vinyl monomers having the formula ##STR2## where X is selected from the group consisting of a halide, carboxyl, ether trialkylammonio, acetate, diazoniodialkylsulfonio, cyano, and oxyl imino using dispersion polymerization to form irregularly-shaped crystalline polymer particles, and where n is selected as H or X; wherein said step of polymerizing includes: (a) admixing said monomer and a crosslinker in a dispersion medium to form a first mixture; (b) preparing a second mixture of an initiator and a dispersion stabilizer for retarding the coagulation of said particles during said polymerization; (c) adding said first mixture to said second mixture to form a third mixture and allowing said monomer to polymerize to form said irregularly-shaped crystalline polymer particles; and (d) sonifying said third mixture after polymerizing to make said irregularly-shaped crystalline polymer particles uniform in size.
Claim 3
Dependent Claim
24 words
The process of claim 1, further including the step of removing inhibitors from said monomer and said crosslinker prior to said step of admixing.
Claim 4
Dependent Claim
17 words
The process of claim 2, wherein said step of polymerizing includes agitating and warming said third mixture.
Claim 5
Dependent Claim
33 words
The process of claim 3, wherein said third mixture is contained within a sealable container and further including the step of purging said container with nitrogen gas after formation of said third mixture.
Claim 6
Dependent Claim
22 words
The process of claim 4, wherein said crystalline particles are formed in a range of sizes from about 0.5 to 5.0 micrometers.
Claim 7
Dependent Claim
28 words
The process of claim 5, wherein said crosslinker is selected from the group consisting of divinylbezene, nonconjugated divinyl compounds, diacrylate compounds, triacrylate compounds, dimethacrylate compounds and trimethacrylate compounds.
Claim 8
Dependent Claim
26 words
The process of claim 6, wherein said initiator is selected from the group consisting of 2,2-azobisisobutyronitrile, 4,4'-azobis(4-cyanopentanoic acid), 2,2'-azobis(2-methylbutyronitrile), benzoyl peroxide, lauroyl peroxide and octanoyl peroxide.
Claim 9
Dependent Claim
29 words
The process of 7, wherein said dispersion stabilizer is selected from the group consisting of poly(vinyl pyrrolidone), poly(vinyl methyl ether), polyethyleneimine, vinyl acetate copolymer, ethyl cellulose and hydroxypropyl cellulose.
Claim 10
Dependent Claim
29 words
The process of 7, wherein said dispersion stabilizer is selected from the group consisting of poly(vinyl pyrrolidone), poly(vinyl methyl ether), polyethyleneimine, vinyl acetate copolymer, ethyl cellulose and hydroxypropyl cellulose.
Claim 11
Dependent Claim
31 words
The process of claim 8, wherein said dispersion medium is selected from the group consisting of ethanol, methanol, benzyl alcohol, hexane, octane, decane, cyclohexane, xylene, ethers, halogenated hydrocarbons, ketones and esters.
Claim 12
Dependent Claim
31 words
The process of claim 4, wherein said steps of agitating and warming include tumbling said third mixture at about 30 revolutions per minute for about twenty hours at sixty degrees Celsius.
Claim 13
Dependent Claim
46 words
The process of claim 2, wherein said step of removing includes washing said monomer and said crosslinker with an aqueous sodium hydroxide solution, drying said monomer and said crosslinker with calcium carbonate and passing said monomer and said crosslinker through a column containing an inhibitor remover.
Claim 14
Dependent Claim
20 words
The process of claim 11, further including the step of refrigerating said monomer and crosslinker after said step of passing.
Claim 15
Dependent Claim
22 words
The process of claim 1, further including the step of coloring said polymer particles by exposing said particles to a dehydrohalogenation reagent.
Claim 16
Dependent Claim
28 words
The process of claim 13, wherein said dehydrohalogenation reagent is in an alcoholic solution and is selected from the group consisting of sodium hydroxide, potassium hydroxide, and amines.
Claim 17
Dependent Claim
54 words
The process of claim 14, wherein said polymer particles are poly (vinylidene chloride), wherein said step of coloring is performed by a sodium hydroxide/ethanol solution with a concentration of sodium hydroxide three times greater than said poly (vinylidene chloride) and wherein said step of exposing is conducted for about thirty minutes at room temperature.
Claim 18
Dependent Claim
28 words
The process of claim 1, wherein said vinyl halide monomer is selected from the group consisting of vinyl chloride, vinyl fluoride, vinyl bromide, vinylidene fluoride and vinylidene bromide.
References Cited (Backward Citations)
US3775107A
Cited
US4093534A
Cited
US4143203A
Cited
US4298448A
Cited
US4285801A
Cited
US4643953A
Cited
US5061766A
Cited
US4655897A
Cited
US4803260A
Cited
US4891286A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-03-12 | 1999-09-11 | 2000-03-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-03-12 | 2003-09-11 | 2004-03-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-03-12 | 2007-09-11 | 2008-03-12 | $7700.00 | Window Closed / Lapsed |