⏱️ 0.0 years remaining
Method for forming self-aligned silicide in a semiconductor device using vapor phase reaction
Assignee: NXP USA Inc
•
Filing: 1995-04-03
•
Granted: 1997-02-25
•
Expires: 2015-04-03
Abstract
Abstract Self-aligned silicide regions (24) are formed in a semiconductor device (10) using vapor phase reaction. A chemical vapor deposition system (40) is used, but rather than depositing a blanket silicide material, a precursor (48) is introduced into the reaction chamber (42) and reacts with only exposed silicon and polysilicon members of the device. The reaction is assisted by heating the substrate to a temperature at which the precursor is volatile. Because the precursor source reacts only with exposed silicon and polysilicon regions, subsequent etch steps are unnecessary. In one form, cobalt silicide regions are formed using a cobalt carbonyl as the precursor source.
Inventors
- 👤 Papu D. Maniar
- 👤 Arkalgud R. Sitaram
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 11:48
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
75 words
A method for forming self-aligned silicide in a semiconductor device comprising the steps of: providing a semiconductor substrate having exposed silicon regions; placing the semiconductor substrate in a reaction chamber; introducing a cobalt precursor into the reaction chamber, without also introducing a silicon source gas; and exposing the cobalt precursor to a heat sufficient to react the cobalt precursor with the exposed silicon regions to form cobalt silicide regions only on the exposed silicon regions.
Claim 2
Independent Claim
75 words
A method for forming self-aligned silicide in a semiconductor device comprising the steps of: providing a semiconductor substrate having exposed silicon regions; placing the semiconductor substrate in a reaction chamber; introducing a cobalt precursor into the reaction chamber, without also introducing a silicon source gas; and exposing the cobalt precursor to a heat sufficient to react the cobalt precursor with the exposed silicon regions to form cobalt silicide regions only on the exposed silicon regions.
Claim 3
Dependent Claim
35 words
The method of claim 1 wherein the step of exposing the cobalt precursor to a heat comprises heating the semiconductor substrate to create a heated substrate and flowing the cobalt precursor over the heated substrate.
Claim 4
Dependent Claim
18 words
The method of claim 1 wherein the step of introducing a cobalt precursor comprises introducing a cobalt carbonyl.
Claim 5
Dependent Claim
46 words
The method of claim 3 wherein the step of introducing a cobalt carbonyl comprises introducing a cobalt carbonyl selected from a group consisting of Co 2 CO 8 , HCo(CO) 4 , Co 4 CO 12 , and RCo(CO) 3 where R is C x H.sub.(2x+1).
Claim 6
Dependent Claim
32 words
The method of claim 3 wherein the step of exposing the cobalt precursor to a heat comprises exposing the cobalt precursor to a heat having a temperature of less than 400° C.
Claim 7
Dependent Claim
30 words
The method of claim 1 further comprising the step of annealing the cobalt silicide regions at a temperature above 600° C. to lower a resistivity of the cobalt silicide regions.
Claim 8
Dependent Claim
18 words
The method of claim 1 further comprising the step of implanting a dopant into the cobalt silicide regions.
Claim 9
Independent Claim
68 words
A method for forming self-aligned silicide in a semiconductor device comprising the steps of: providing a semiconductor substrate having exposed silicon regions; placing the semiconductor substrate in a reaction chamber; introducing a molybdenum precursor into the reaction chamber; and exposing the molybdenum precursor to a heat sufficient to react the molybdenum precursor with the exposed silicon regions to selectively form molybdenum silicide regions on the exposed silicon regions.
Claim 10
Independent Claim
68 words
A method for forming self-aligned silicide in a semiconductor device comprising the steps of: providing a semiconductor substrate having exposed silicon regions; placing the semiconductor substrate in a reaction chamber; introducing a molybdenum precursor into the reaction chamber; and exposing the molybdenum precursor to a heat sufficient to react the molybdenum precursor with the exposed silicon regions to selectively form molybdenum silicide regions on the exposed silicon regions.
Claim 11
Dependent Claim
18 words
The method of claim 8 wherein the step of introducing a molybdenum precursor comprises introducing a molybdenum carbonyl.
Claim 12
Dependent Claim
35 words
The method of claim 8 wherein the step of exposing the molybdenum precursor to a heat comprises heating the semiconductor substrate to create a heated substrate and flowing the molybdenum precursor over the heated substrate.
Claim 13
Dependent Claim
32 words
The method of claim 8 wherein the step of exposing the molybdenum precursor to a heat comprises exposing the molybdenum precursor to a heat having a temperature of less than 700° C.
Claim 14
Dependent Claim
30 words
The method of claim 8 further comprising the step of annealing the molybdenum silicide regions at a temperature above 800° C. to lower a resistivity of the molybdenum silicide regions.
Claim 15
Independent Claim
120 words
A method for forming self-aligned silicide in a semiconductor device comprising the steps of: providing a silicon substrate; forming a gate dielectric on the silicon substrate; depositing a polysilicon layer on the gate dielectric; etching the polysilicon layer to form a gate electrode; etching portions of the gate dielectric beyond the gate electrode to expose a surface of the silicon substrate; placing the silicon substrate in a reaction chamber; heating the silicon substrate to a first temperature; and introducing a gas selected from a group consisting of a cobalt carbonyl and a molybdenum carbonyl into the reaction chamber, without introducing a gaseous silicon source, to selectively form a silicide on the gate electrode and the surface of the silicon substrate.
Claim 16
Independent Claim
120 words
A method for forming self-aligned silicide in a semiconductor device comprising the steps of: providing a silicon substrate; forming a gate dielectric on the silicon substrate; depositing a polysilicon layer on the gate dielectric; etching the polysilicon layer to form a gate electrode; etching portions of the gate dielectric beyond the gate electrode to expose a surface of the silicon substrate; placing the silicon substrate in a reaction chamber; heating the silicon substrate to a first temperature; and introducing a gas selected from a group consisting of a cobalt carbonyl and a molybdenum carbonyl into the reaction chamber, without introducing a gaseous silicon source, to selectively form a silicide on the gate electrode and the surface of the silicon substrate.
Claim 17
Dependent Claim
44 words
The method of claim 13 wherein the step of introducing comprises introducing a cobalt carbonyl gas selected from a group consisting of Co 2 CO 8 , HCo(CO) 4 , Co 4 CO 12 , or RCo(CO) 3 where R is C x H.sub.(2x+1).
Claim 18
Dependent Claim
31 words
The method of claim 13 further comprising the step of annealing the silicon substrate at a second temperature which is higher than the first temperature to lower resistivity of the silicide.
Claim 19
Dependent Claim
23 words
The method of claim 13 further comprising the step of implanting a dopant into the surface of the silicon substrate, through the silicide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-02-25 | 2000-08-26 | 2001-02-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-02-25 | 2004-08-26 | 2005-02-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-02-25 | 2008-08-26 | 2009-02-25 | $7700.00 | Window Closed / Lapsed |