Method for fabricating a coaxial capacitor of a semiconductor device
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1996-01-11
•
Granted: 1997-08-12
•
Expires: 2016-01-11
Abstract
Abstract A method for fabricating a coaxial capacitor with increased capacitance which improves the process tolerances was accomplished. Fabricating this improved coaxial capacitor involves forming an annular groove in a polysilicon layer over the node contact opening. Next, sidewall spacers are formed on the sidewalls of the annular groove. A polyoxide masking layer is formed covering the first conductive layer. The sidewall spacers are removed exposing portions of the first conductive layer. The exposed portions of the first conductive layer are then etched using the masking layer as a mask forming a channel surrounding a central spine. The masking layer is removed. The first conductive layer is masking and etched completing the patterning of the ridge and thereby forming a storage electrode having an annual ridge about the central spine. This use of sidewall spacers to define the capacitor ridges allows smaller ridge definition than capable using photolithographic processes and is more controllable. The coaxial capacitor is then completed by depositing a capacitor dielectric and a top capacitor electrode over the storage electrode.
Inventors
- 👤 Horng-Huei Tseng
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 22:03
CPC Classifications
H; H10; H10B; H10B12/00; H10B12/01; H10B12/02; H10B12/03; H10B12/033; H10B12/30; H10B12/31; H10B12/318
Claims Analysis
Total Claims: 33
Claim 1
Independent Claim
232 words
A method of fabricating a high capacitance coaxial capacitor on a semiconductor substrate having a device area formed thereon comprising the steps of: forming a first insulation layer over said device area and elsewhere over the substrate surface; forming a contact opening in said first insulation layer to expose said device area; forming a first conductive layer on said first insulation layer and in said contact opening; forming an annular groove in said first conductive layer centered over said contact opening; said annular groove having sidewalls; forming sidewall spacers on said sidewalls of said annular groove; forming a masking layer covering said first conductive layer; removing said sidewall spacers exposing portions of said first conductive layer; etching said exposed portions of said first conductive layer using said masking layer as a mask forming a channel surrounding a central spine; removing said masking layer; masking and etching said first conductive layer forming a patterned area of said first conductive layer over and aligned to said device area thereby forming an annular ridge about said central spine; said central spine and said annular ridge comprising a storage electrode; sequentially forming a capacitor dielectric layer and a second conductive layer over said storage electrode; and patterning said capacitor dielectric layer and said second conductive layer to form a capacitor dielectric and top electrode, over and adjacent to said storage electrode thereby forming said coaxial capacitor.
Claim 2
Independent Claim
232 words
A method of fabricating a high capacitance coaxial capacitor on a semiconductor substrate having a device area formed thereon comprising the steps of: forming a first insulation layer over said device area and elsewhere over the substrate surface; forming a contact opening in said first insulation layer to expose said device area; forming a first conductive layer on said first insulation layer and in said contact opening; forming an annular groove in said first conductive layer centered over said contact opening; said annular groove having sidewalls; forming sidewall spacers on said sidewalls of said annular groove; forming a masking layer covering said first conductive layer; removing said sidewall spacers exposing portions of said first conductive layer; etching said exposed portions of said first conductive layer using said masking layer as a mask forming a channel surrounding a central spine; removing said masking layer; masking and etching said first conductive layer forming a patterned area of said first conductive layer over and aligned to said device area thereby forming an annular ridge about said central spine; said central spine and said annular ridge comprising a storage electrode; sequentially forming a capacitor dielectric layer and a second conductive layer over said storage electrode; and patterning said capacitor dielectric layer and said second conductive layer to form a capacitor dielectric and top electrode, over and adjacent to said storage electrode thereby forming said coaxial capacitor.
Claim 3
Dependent Claim
39 words
The method of claim 1 wherein said first insulation layer is composed of a material selected from the group consisting of: silicon oxide and borophosphosilicate glass and has a thickness in the range between about 5000 and 10,000 Å.
Claim 4
Dependent Claim
42 words
The method of claim 1 wherein said first conductive layer is formed of doped polysilicon having an impurity concentration in the range between about 1E20 and 1E21 atoms/cm 3 and has a thickness in the range between about 3000 and 8000 Å.
Claim 5
Dependent Claim
29 words
The method of claim 1 wherein said sidewall spacers are composed silicon nitride, and said sidewall spacers have a width in the range between about 1000 and 2000 Å.
Claim 6
Dependent Claim
40 words
The method of claim 1 wherein said sidewall spacers are formed by depositing an insulation layer composed of silicon nitride over said first conductive layer and anisotropically etching said insulation layer and exposing the surface of said first conductive layer.
Claim 7
Dependent Claim
37 words
The method of claim 1 wherein said masking layer is formed by oxidizing said first conductive layer forming a polyoxide layer and said polyoxide layer has a thickness in the range between about 300 and 1000 Å.
Claim 8
Dependent Claim
33 words
The method of claim 1 wherein said annular groove has a width in the range between about 0.4 and 1.2 μm and a depth in the range between about 0.1 and 0.2 μm.
Claim 9
Dependent Claim
23 words
The method of claim 1 wherein said etching said exposed portions of said first conductive layer is performed with a reactive ion etch.
Claim 10
Dependent Claim
33 words
The method of claim 1 wherein said central spine has a diameter in the range between about 500 and 2000 Å and a height in the range between about 0.2 and 0.8 μm.
Claim 11
Dependent Claim
48 words
The method of claim 1 wherein said annular ridge has a width in the range between about 0.1 and 0.3 μm; a height in the range between about 0.4 and 1.0 μm; and a spacing from said central spine in the range between about 0.5 and 0.2 μm.
Claim 12
Dependent Claim
46 words
The method of claim 1 wherein said capacitor dielectric is composed of a material selected from the group consisting of: silicon oxide/silicon nitride/silicon oxide (ONO), silicon nitride and Ta 2 O 5 ; and has a thickness in the range between about 10 and 100 Å.
Claim 13
Dependent Claim
42 words
The method of claim 1 wherein said top plate electrode is formed of doped polysilicon having a thickness in the range between about 1000 and 2000 Å and an impurity concentration in the range between about 1E20 and 1E22 atoms/cm 3 .
Claim 14
Dependent Claim
35 words
The method of claim 1 wherein said first conductive layer in said contact opening contacts a source region of a field effect transistor in said device area thereby forming a dynamic random access memory cell.
Claim 15
Dependent Claim
24 words
The method of claim 1 wherein said annular groove and ridge have a shape selected from the group consisting of: square, rectangular, and circular.
Claim 16
Independent Claim
275 words
A method of fabricating a high capacitance coaxial capacitor on a semiconductor substrate having a device area formed thereon comprising the steps of: forming a conformal dielectric layer composed of silicon oxide over said device area and elsewhere over the substrate surface; forming a first insulation layer composed of borophosphosilicate glass over said conformal dielectric layer; forming a contact opening in said first insulation layer to expose said device area; forming a first conductive layer composed of polysilicon on said first insulation layer and in said contact hole; forming an annular groove in said first conductive layer centered over said contact opening; said annular groove having sidewalls; forming sidewall spacers composed of silicon nitride on said sidewalls of said annular groove; forming a masking layer composed of polyoxide covering said first conductive layer; removing said sidewall spacers exposing portions of said first conductive layer; etching said exposed portions of said first conductive layer using said masking layer as a mask forming a channel surrounding a central spine in said first conductive layer; removing said masking layer; forming a photoresist layer having a first opening over said first conductive layer defining an annular ridge around said central spine; etching said first conductive layer using said photoresist layer as a mask thereby forming an annual ridge about said central spine; said central spine and said annular ridge comprising a storage electrode; sequentially forming a capacitor dielectric layer and a second conductive layer over said storage electrode; and patterning said capacitor dielectric layer and said second conductive layer to form a capacitor dielectric and top electrode, over and adjacent to said storage electrode; thereby forming said coaxial capacitor.
Claim 17
Independent Claim
275 words
A method of fabricating a high capacitance coaxial capacitor on a semiconductor substrate having a device area formed thereon comprising the steps of: forming a conformal dielectric layer composed of silicon oxide over said device area and elsewhere over the substrate surface; forming a first insulation layer composed of borophosphosilicate glass over said conformal dielectric layer; forming a contact opening in said first insulation layer to expose said device area; forming a first conductive layer composed of polysilicon on said first insulation layer and in said contact hole; forming an annular groove in said first conductive layer centered over said contact opening; said annular groove having sidewalls; forming sidewall spacers composed of silicon nitride on said sidewalls of said annular groove; forming a masking layer composed of polyoxide covering said first conductive layer; removing said sidewall spacers exposing portions of said first conductive layer; etching said exposed portions of said first conductive layer using said masking layer as a mask forming a channel surrounding a central spine in said first conductive layer; removing said masking layer; forming a photoresist layer having a first opening over said first conductive layer defining an annular ridge around said central spine; etching said first conductive layer using said photoresist layer as a mask thereby forming an annual ridge about said central spine; said central spine and said annular ridge comprising a storage electrode; sequentially forming a capacitor dielectric layer and a second conductive layer over said storage electrode; and patterning said capacitor dielectric layer and said second conductive layer to form a capacitor dielectric and top electrode, over and adjacent to said storage electrode; thereby forming said coaxial capacitor.
Claim 18
Dependent Claim
22 words
The method of claim 15 wherein said first insulation layer has a thickness in the range between about 5000 and 10,000 Å.
Claim 19
Dependent Claim
42 words
The method of claim 15 wherein said first conductive layer is formed of doped polysilicon having an impurity concentration in the range between about 1E20 and 1E21 atoms/cm 3 and has a thickness in the range between about 3000 and 8000 Å.
Claim 20
Dependent Claim
29 words
The method of claim 15 wherein said sidewall spacers are composed silicon nitride, and said sidewall spacers have a width in the range between about 1000 and 2000 Å.
Claim 21
Dependent Claim
37 words
The method of claim 15 wherein said masking layer is formed by oxidizing said first conductive layer forming a polyoxide layer and said polyoxide layer has a thickness in the range between about 300 and 1000 Å.
Claim 22
Dependent Claim
33 words
The method of claim 15 wherein said annular groove has a width in the range between about 0.4 and 1.2 μm and a depth in the range between about 0.1 and 0.2 μm.
Claim 23
Dependent Claim
33 words
The method of claim 15 wherein said central spine has a diameter in the range between about 500 and 2000 Å and a height in the range between about 0.2 and 0.8 μm.
Claim 24
Dependent Claim
48 words
The method of claim 15 wherein said annular ridge has a width in the range between about 0.1 and 0.3 μm; a height in the range between about 0.4 and 1.0 μm; and a spacing from the central spine in the range between about 0.5 and 0.2 μm.
Claim 25
Dependent Claim
35 words
The method of claim 15 wherein said first conductive layer in said contact opening contacts a source region of a field effect transistor in said device area thereby forming a dynamic random access memory cell.
Claim 26
Independent Claim
317 words
A method of fabricating a dynamic random access memory device having a coaxial capacitor in device areas for a memory cell unit; said memory device having a source, a drain, and a transfer gate on a substrate; which comprises the steps of: forming a metal oxide semiconductor device having source and drain regions, adjacent to a field oxide region, in a silicon substrate; forming a conductive word line over said field oxide region; forming a first insulation layer over said MOS device, said conductive word line and field oxide region; forming a contact opening in said first insulation layer exposing said source region; forming a first conductive layer on said first insulation layer and in said contact opening; forming an annular groove in said first conductive layer centered over said contact opening; said annular groove having sidewalls; forming sidewall spacers on said sidewalls of said annular groove; forming a masking layer covering said first conductive layer; removing said sidewall spacers exposing portions of said first conductive layer; etching said exposed portions of said first conductive layer using said masking layer as a mask forming a channel surrounding a central spine; removing said masking layer; masking and etching said first conductive layer forming a patterned area of said first conductive layer over and aligned to said device area thereby forming an annual ridge about said central spine; said central spine and said annular ridge comprising a storage electrode; sequentially forming a capacitor dielectric layer and a second conductive layer over said storage electrode; and patterning said capacitor dielectric layer and said second conductive layer to form a capacitor dielectric and top electrode, over and adjacent to said storage electrode; forming a bit line contact opening through said top insulation layer to said drain region; and forming a second conductive layer in said bit line contact opening thereby forming said dynamic random access memory device having a coaxial capacitor.
Claim 27
Independent Claim
317 words
A method of fabricating a dynamic random access memory device having a coaxial capacitor in device areas for a memory cell unit; said memory device having a source, a drain, and a transfer gate on a substrate; which comprises the steps of: forming a metal oxide semiconductor device having source and drain regions, adjacent to a field oxide region, in a silicon substrate; forming a conductive word line over said field oxide region; forming a first insulation layer over said MOS device, said conductive word line and field oxide region; forming a contact opening in said first insulation layer exposing said source region; forming a first conductive layer on said first insulation layer and in said contact opening; forming an annular groove in said first conductive layer centered over said contact opening; said annular groove having sidewalls; forming sidewall spacers on said sidewalls of said annular groove; forming a masking layer covering said first conductive layer; removing said sidewall spacers exposing portions of said first conductive layer; etching said exposed portions of said first conductive layer using said masking layer as a mask forming a channel surrounding a central spine; removing said masking layer; masking and etching said first conductive layer forming a patterned area of said first conductive layer over and aligned to said device area thereby forming an annual ridge about said central spine; said central spine and said annular ridge comprising a storage electrode; sequentially forming a capacitor dielectric layer and a second conductive layer over said storage electrode; and patterning said capacitor dielectric layer and said second conductive layer to form a capacitor dielectric and top electrode, over and adjacent to said storage electrode; forming a bit line contact opening through said top insulation layer to said drain region; and forming a second conductive layer in said bit line contact opening thereby forming said dynamic random access memory device having a coaxial capacitor.
Claim 28
Dependent Claim
42 words
The method of claim 24 wherein said first conductive layer is formed of doped polysilicon having an impurity concentration in the range between about 1E20 and 1E21 atoms/cm 3 and has a thickness in the range between about 3000 and 8000 Å.
Claim 29
Dependent Claim
29 words
The method of claim 24 wherein said sidewall spacers are composed silicon nitride, and said sidewall spacers have a width in the range between about 1000 and 2000 Å.
Claim 30
Dependent Claim
37 words
The method of claim 24 wherein said masking layer is formed by oxidizing said first conductive layer forming a polyoxide layer and said polyoxide layer has a thickness in the range between about 300 and 1000 Å.
Claim 31
Dependent Claim
33 words
The method of claim 24 wherein said annular groove has a width in the range between about 0.4 and 1.2 μm and a depth in the range between about 0.1 and 0.2 μm.
Claim 32
Dependent Claim
33 words
The method of claim 24 wherein said central spine has a diameter in the range between about 500 and 2000 Å and a height in the range between about 0.2 and 0.8 μm.
Claim 33
Dependent Claim
48 words
The method of claim 24 wherein said annular ridge has a width in the range between about 0.1 and 0.3 μm; a height in the range between about 0.4 and 1.0 μm; and a spacing from the central spine in the range between about 0.5 and 0.2 μm.
References Cited (Backward Citations)
US5185282A
Cited
US5084405A
Cited
US5403767A
Cited
US5399518A
Cited
US5516719A
Cited
US5443993A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-08-11 | 2001-02-10 | 2001-08-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-08-11 | 2005-02-10 | 2005-08-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-08-11 | 2009-02-10 | 2009-08-12 | $7700.00 | Window Closed / Lapsed |