Method for manufacturing liquid crystal display apparatus with drain/source silicide electrodes made by sputtering process
Assignee: Gold Charm Ltd
•
Filing: 1997-06-23
•
Granted: 1999-08-24
•
Expires: 2017-06-23
Abstract
Abstract In a method for manufacturing a liquid crystal display apparatus, a gate electrode is formed on an insulating substrate, and a gate insulating layer is formed on the gate electrode. Then, a semiconductor active layer is formed on the gate insulating layer. Then, a metal silicide layer is formed on the semiconductor active layer by using a sputtering process, and a metal layer is formed on the metal silicide layer. Then, the metal layer is etched by a dry etching process using a mask, an the metal silicide layer is etched by a wet etching process using the same mask. Finally, the semiconductor active layer is etched by using the metal layer as a mask.
Inventors
- 👤 Akitoshi Maeda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 06:18
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/031; H10D30/0312; H10D30/0316; H10D30/0321; H10D30/60; H10D30/67; H10D30/6729; H10D30/6737; H10D30/674; H10D30/6741; H10D30/6743
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
119 words
A method for manufacturing a liquid crystal display apparatus, comprising the steps of: forming a gate electrode on an insulating substrate; forming a gate insulating layer on said gate electrode; forming a semiconductor active layer on said gate insulating layer; forming a metal silicide layer on said semiconductor active layer by using a sputtering process; forming a metal layer on said metal silicide layer; etching said metal layer by a first dry etching process using a mask; etching said metal silicide layer by a wet etching process using said mask, after said first dry etching process is carried out; etching said semiconductor active layer using said metal layer as a mask, after said wet etching process is carried out.
Claim 2
Independent Claim
119 words
A method for manufacturing a liquid crystal display apparatus, comprising the steps of: forming a gate electrode on an insulating substrate; forming a gate insulating layer on said gate electrode; forming a semiconductor active layer on said gate insulating layer; forming a metal silicide layer on said semiconductor active layer by using a sputtering process; forming a metal layer on said metal silicide layer; etching said metal layer by a first dry etching process using a mask; etching said metal silicide layer by a wet etching process using said mask, after said first dry etching process is carried out; etching said semiconductor active layer using said metal layer as a mask, after said wet etching process is carried out.
Claim 3
Dependent Claim
22 words
The method as set forth in claim 1, wherein said semiconductor active layer etching step carries out a second dry etching process.
Claim 4
Dependent Claim
37 words
The method as set forth in claim 1, wherein said metal silicide layer and said metal layer form drain and source electrodes of a thin film transistor and a signal bus line connected to said drain electrode.
Claim 5
Dependent Claim
30 words
The method as set forth in claim 1, wherein said metal layer is made of refractory metal, and said metal silicide layer is made of silicide of said refractory metal.
Claim 6
Dependent Claim
24 words
The method as set forth in claim 1, wherein said metal layer is made of a double configuration of different kinds of refractory metal.
Claim 7
Dependent Claim
24 words
The method as set forth in claim 1, wherein said metal layer is made of a double configuration of refractory metal and non-refractory metal.
Claim 8
Dependent Claim
23 words
The method as set forth in claim 1, wherein said semiconductor active layer is made of non-doped amorphous silicon and impurity-doped amorphous silicon.
Claim 9
Independent Claim
144 words
A method for manufacturing a liquid crystal display apparatus, comprising the steps of: forming a gate electrode on an insulating substrate; forming a gate insulating layer on said gate electrode; forming a non-doped semiconductor active layer on said gate insulating layer; forming an etching production layer on said non-doped semiconductor active layer; forming an impurity-doped semiconductor active layer on said etching protection layer; forming a metal silicide layer on said impurity-doped semiconductor active layer by using a sputtering process; forming a metal layer on said metal silicide layer; etching said metal layer by a first dry etching process using a mask; etching said metal silicide layer by a wet etching process using said mask, after said first dry etching process is carried out; etching said non-doped semiconductor active layer using said metal layer as a mask, after said wet etching process is carried out.
Claim 10
Independent Claim
144 words
A method for manufacturing a liquid crystal display apparatus, comprising the steps of: forming a gate electrode on an insulating substrate; forming a gate insulating layer on said gate electrode; forming a non-doped semiconductor active layer on said gate insulating layer; forming an etching production layer on said non-doped semiconductor active layer; forming an impurity-doped semiconductor active layer on said etching protection layer; forming a metal silicide layer on said impurity-doped semiconductor active layer by using a sputtering process; forming a metal layer on said metal silicide layer; etching said metal layer by a first dry etching process using a mask; etching said metal silicide layer by a wet etching process using said mask, after said first dry etching process is carried out; etching said non-doped semiconductor active layer using said metal layer as a mask, after said wet etching process is carried out.
Claim 11
Dependent Claim
23 words
The method as set forth in claim 8, wherein said impurity-doped semiconductor active layer etching step carries out a second dry etching process.
Claim 12
Dependent Claim
37 words
The method as set forth in claim 8, wherein said metal silicide layer and said metal layer form drain and source electrodes of a thin film transistor and a signal bus line connected to said drain electrode.
Claim 13
Dependent Claim
30 words
The method as set forth in claim 8, wherein said metal layer is made of refractory metal, and said metal silicide layer is made of silicide of said refractory metal.
Claim 14
Dependent Claim
24 words
The method as set forth in claim 8, wherein said metal layer is made of a double configuration of different kinds of refractory metal.
Claim 15
Dependent Claim
24 words
The method as set forth in claim 8, wherein said metal layer is made of a double configuration of refractory metal and non-refractory metal.
Claim 16
Dependent Claim
31 words
The method as set forth in claim 8, wherein said non-doped semiconductor active layer is made of amorphous silicon, and said impurity-doped semiconductor active layer is made of impurity-doped amorphous silicon.
References Cited (Backward Citations)
JPS61248564A
Cited
JPS62172761A
Cited
US5028551A
Cited
JPH02206131A
Cited
JPH05235034A
Cited
US5427962A
Cited
US5334544A
Cited
US5821622A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-08-23 | 2003-02-22 | 2003-08-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-08-23 | 2007-02-22 | 2007-08-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-08-23 | 2011-02-22 | 2011-08-24 | $7700.00 | Window Closed / Lapsed |