Synthetic paper and inkjet recording paper with the use of the same
Assignee: Yupo Corp
•
Filing: 1998-01-23
•
Granted: 2000-07-11
•
Expires: 2018-01-23
Abstract
Abstract A synthetic paper made of a stretched resin film; said stretched resin film being obtained by stretching a resin film having as a support a resin composition which contains: (A) from 30 to 80% by weight of a crystalline polyolefin resin; and (B) from 70 to 20% by weight of milled calcium carbonate particles at a temperature lower than the melting point of said crystalline polyolefin resin employed as the component (A); and an inkjet recording paper made by using this synthetic paper. Because of having projections of finely milled calcium carbonate particles with a hydrophilic surface around which a number of fine cracks are formed, the synthetic paper shows improved moisture absorptivity for water color inks and aqueous adhesives, quick drying properties and excellent printability.
Inventors
- 👤 Masaaki Yamanaka
- 👤 Kazuyuki Kimura
- 👤 Kazumasa Hirano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 05:11
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/18; C08K; C08K3/00; C08K3/18; C08K3/24; C08K3/26; C08K5/00; C08K5/16; C08K5/17; C08K5/36; C08K5/41; C08K5/42; G; G03; G03G; G03G5/00; G03G5/14; G03G5/147; G03G5/14708; G03G5/14713; G03G5/14717; G03G5/14721; C08J2323/00; C08J2323/02; C08J2323/04; C08J2323/08; C08J2323/10; C08J2323/12; C08K2003/265; C08K2201/00; C08K2201/002; C08K2201/005; C08L; C08L23/00; C08L23/02; C08L23/04; C08L23/08; C08L23/0807; C08L23/0815; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249955; Y10T428/249956; Y10T428/25; Y10T428/258; Y10T428/31504; Y10T428/31855; Y10T428/31909
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
309 words
A synthetic paper made of a stretched resin film; said stretched resin film being obtained by stretching a resin film having a support layer which comprises: (A) from 30 to 80% by weight of said composition of a crystalline polyolefin resin; and (B) from 70 to 20% by weight of said composition of milled calcium carbonate particles selected from the group consisting of: (b1) milled calcium carbonate particles having an average particle size of from 0.3 to 2 μm prepared by wet-milling 100 parts by weight of calcium carbonate particles in an aqueous medium in the presence of from 0.05 to 2 parts by weight of a dispersant comprising a copolymer of from 10 to 95% by mol of an amine salt selected from the group consisting of diallylamine salts and alkylallylamine salts with from 90 to 5% by mol of an amide selected from the group consisting of acrylamide and methacrylamide, followed by drying; and (b2) milled calcium carbonate particles having an average particle size of from 0.3 to 2 μm prepared by wet-milling 100 parts by weight of calcium carbonate particles in an aqueous medium in the presence of from 0.05 to 2 parts by weight of a dispersant comprising a copolymer of from 10 to 95% by mol of an amine salt selected from the group consisting of diallylamine salts and alkylallylamine salts with from 90 to 5% by mol of an amide selected from the group consisting of acrylamide and methacrylamide and then treating the thus milled product in an aqueous medium with 0.5 to 10 parts by weight of a sulfonate selected from the group consisting of sulfonates of alkylene oxide adducts of monohydric alcohols, alkylsulfonates and alkylbenzenesulfonates followed by drying; and wherein said stretching is performed at a temperature lower than the melting point of said crystalline polyolefin resin employed as component (A).
Claim 2
Dependent Claim
309 words
A synthetic paper made of a stretched resin film; said stretched resin film being obtained by stretching a resin film having a support layer which comprises: (A) from 30 to 80% by weight of said composition of a crystalline polyolefin resin; and (B) from 70 to 20% by weight of said composition of milled calcium carbonate particles selected from the group consisting of: (b1) milled calcium carbonate particles having an average particle size of from 0.3 to 2 μm prepared by wet-milling 100 parts by weight of calcium carbonate particles in an aqueous medium in the presence of from 0.05 to 2 parts by weight of a dispersant comprising a copolymer of from 10 to 95% by mol of an amine salt selected from the group consisting of diallylamine salts and alkylallylamine salts with from 90 to 5% by mol of an amide selected from the group consisting of acrylamide and methacrylamide, followed by drying; and (b2) milled calcium carbonate particles having an average particle size of from 0.3 to 2 μm prepared by wet-milling 100 parts by weight of calcium carbonate particles in an aqueous medium in the presence of from 0.05 to 2 parts by weight of a dispersant comprising a copolymer of from 10 to 95% by mol of an amine salt selected from the group consisting of diallylamine salts and alkylallylamine salts with from 90 to 5% by mol of an amide selected from the group consisting of acrylamide and methacrylamide and then treating the thus milled product in an aqueous medium with 0.5 to 10 parts by weight of a sulfonate selected from the group consisting of sulfonates of alkylene oxide adducts of monohydric alcohols, alkylsulfonates and alkylbenzenesulfonates followed by drying; and wherein said stretching is performed at a temperature lower than the melting point of said crystalline polyolefin resin employed as component (A).
Claim 3
Dependent Claim
47 words
The synthetic paper as claimed in claim 1, which has a void ratio of from 10 to 50% as calculated using the following formula: ##EQU2## wherein ρ 0 represents the density of the resin film before stretching; and ρ represents the density of the stretched resin film.
Claim 4
Dependent Claim
58 words
The synthetic paper as claimed in claim 1, wherein said crystalline polyolefin resin is one having a crystallinity of from 10 to 75% and is selected from the group consisting of homopolymers of a-olefins having 2 to 8 carbon atoms and random or block copolymers of 2 to 5 kinds of α-olefins having 2 to 8 carbon atoms.
Claim 5
Dependent Claim
36 words
The synthetic paper as claimed in claim 3, wherein said crystalline polyolefin resin is a propylene homopolymer having a melt flow rate, ASTM D1238: 230° C., load 2.16 kg, of from 0.2 to 50 g/10 min.
Claim 6
Dependent Claim
37 words
The synthetic paper as claimed in claim 1, wherein said diallylamine salts and alkyldiallylamine salts are diallylamine or alkyldiallylamine salts of acids selected from the group consisting of hydrochloric acid, sulfuric acid, nitric acid and acetic acid.
Claim 7
Dependent Claim
21 words
The synthetic paper as claimed in claim 1, wherein said dispersant is a copolymer obtained by reacting diallylamine hydrochloride with acrylamide.
Claim 8
Dependent Claim
42 words
The synthetic paper as claimed in claim 1, wherein a dispersion of 10 parts by weight of the milled calcium carbonate (b2) in 100 parts by weight of deionized water shows at 25° C., an electrical conductivity of at least 200 μS/cm.
Claim 9
Dependent Claim
90 words
The synthetic paper as claimed in claim 1, wherein said sulfonate of an alkylene oxide adduct of a monohydric alcohol is one represented by the following formula (6): RO(AO).sub.m SO.sub.3 M (6) wherein R represents an alkyl group having 2 to 18 carbon atoms or an allyl group optionally substituted by an alkyl group having 1 to 10 carbon atoms; A represents an alkylene group having 2 to 4 carbon atoms; M represents Na, K, Li or an ammonium group; and m is a number of from 2 to 20.
Claim 10
Dependent Claim
44 words
The synthetic paper as claimed in claim 1, wherein said alkylsulfonate is one represented by the following formula (7): R'--SO.sub.3 M (7) wherein R' represents an alkyl group having 6 to 30 carbon atoms; and M represents Na, K, Li or an ammonium group.
Claim 11
Dependent Claim
42 words
The synthetic paper as claimed in claim 1, wherein said alkylbenzenesulfonate is one represented by the following formula (8): ##STR2## wherein R" represents an alkyl group having 6 to 23 carbon atoms; and M represents Na, K, Li or an ammonium group.
Claim 12
Dependent Claim
29 words
The synthetic paper as claimed in claim 1, wherein said sulfonate is one selected from the group consisting of sodium stearyl polyethylene ether sulfonate, sodium dodecylbenzenesulfonate and sodium alkylsulfonates.
Claim 13
Dependent Claim
21 words
The synthetic paper as claimed in claim 1, wherein said dispersant has a weight-average molecular weight of from 1,000 to 1,000,000.
Claim 14
Dependent Claim
82 words
An inkjet recording paper made of the synthetic paper as claimed in claim 1, such that when a water color ink, 100% by weight in total, of the following composition is dropped onto the surface thereof, the contact angle of said water color ink to said recording paper is 20 to 42°: ______________________________________
C.I. Food Black 2 2% by weight,
N-methyl-2-pyrrolidone 10% by weight,
diethylene glycol 20% by weight,
polyethylene glycol (m.w.: 200) 15% by weight, and
water 53% by weight.
______________________________________
References Cited (Backward Citations)
US4081583A
Cited
US4341880A
Cited
US4386965A
Cited
US4605591A
Cited
US4892902A
Cited
US5000871A
Cited
US4981748A
Cited
US5865951A
Cited
US5320897A
Cited
US5652326A
Cited
US5489471A
Cited
US5747146A
Cited
US5670225A
Cited
US5698627A
Cited
EP0736374A1
Cited
EP0745488A1
Cited
US5798078A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-07-11 | 2004-01-10 | 2004-07-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-07-11 | 2008-01-10 | 2008-07-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-07-11 | 2012-01-10 | 2012-07-11 | $7700.00 | Window Closed / Lapsed |