US6143431A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Production of Palladium-103
Assignee: BWXT Medical Ltd
•
Filing: 1998-05-04
•
Granted: 2000-11-07
•
Expires: 2018-05-04
Abstract
Abstract Palladium-103 radiochemical of high radionuclidic purity can be produced in commercial scale quantities by irradiating enriched Palladium targets comprising a mixture of Pd isotopes with protons or deuterons in the 10-50 MeV energy range. Commercially viable batch sizes with acceptable specific activity of the product Pd-103 are achieved by adjusting the irradiation energy, irradiation time, irradiation current, current density, plated target mass, plated target shape, plated target size, target isotope enrichment levels, and incident angle of the target to the beam. The method for the production of Pd-103 comprises providing a target material enriched with Pd isotopes comprising atomic masses equal to or greater than Pd-103, applying the target material onto a target support; irradiating the target material with protons or deuterons of sufficient incident energy and time to convert at least some of the Pd isotopes within the target material to Pd-103; and purifying Pd from the non-Pd components.
Inventors
- 👤 Brian A. Webster
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 05:48
CPC Classifications
G; G21; G21G; G21G1/00; G21G1/04; G21G1/10; G21G4/00; G21G4/04; G21G4/06; G21G4/08; A; A61; A61N; A61N5/00; A61N5/10; A61N5/1001; A61N5/1027; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12771; Y10T428/12861; Y10T428/12868; Y10T428/12875
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
73 words
A method for the production of Pd-103 comprising; i) providing a target material enriched with Pd isotopes comprising atomic masses equal to or greater than Pd-103; ii) applying the target material onto a target support; iii) irradiating the target material with protons or deuterons of sufficient incident energy and time to convert at least some of the Pd isotopes within the target material to Pd-103; and iv) purifying Pd from the non-Pd components.
Claim 2
Independent Claim
73 words
A method for the production of Pd-103 comprising; i) providing a target material enriched with Pd isotopes comprising atomic masses equal to or greater than Pd-103; ii) applying the target material onto a target support; iii) irradiating the target material with protons or deuterons of sufficient incident energy and time to convert at least some of the Pd isotopes within the target material to Pd-103; and iv) purifying Pd from the non-Pd components.
Claim 3
Dependent Claim
19 words
The method of claim 1 wherein the target material is enriched with Pd-104, Pd-105, Pd-106, or a combination thereof.
Claim 4
Dependent Claim
13 words
The method of claim 2 wherein the target material is enriched with Pd-104.
Claim 5
Dependent Claim
27 words
The method of claim 3 wherein the target material is a foil, or the target material is applied to the target support using electroplating, deposition, or precipitation.
Claim 6
Dependent Claim
13 words
The method of claim 4 wherein the target material is applied using electroplating.
Claim 7
Dependent Claim
32 words
The method of claim 4 wherein the target material is formed by layering Pd isotope-containing target materials so that each layer is enriched with Pd isotopes comprised of predominantly different atomic mass.
Claim 8
Dependent Claim
18 words
The method of claim 1 wherein the target support is protected by a coating comprising a barrier layer.
Claim 9
Dependent Claim
13 words
The method of claim 7, wherein the barrier layer is comprised of rhodium.
Claim 10
Dependent Claim
20 words
The method of claim 8, wherein the incident energy of said protons or deuterons is greater than about 10 MeV.
Claim 11
Dependent Claim
31 words
The method of claim 9 wherein the protons or deuterons are provided as a beam angled from about 1 to about 90° as measured from the surface of the target material.
Claim 12
Dependent Claim
31 words
The method of claim 10, wherein the target material is of a shape that is similar to the shape of the proton beam that strikes the surface of the target material.
Claim 13
Dependent Claim
39 words
The method of claim 11, wherein the incident energy of the protons is from about 23 to about 30 MeV, and the angle of the proton beam is about 7° as measured from the surface of the target material.
Claim 14
Dependent Claim
23 words
The method of claim 12, wherein the target material is irradiated with protons or deuterons from about 1 hour to about 1,000 hours.
Claim 15
Dependent Claim
18 words
The method of claim 1, wherein the specific activity of the Pd-103 is greater than about 5 Ci/gm.
Claim 16
Dependent Claim
14 words
The method of claim 1, wherein the Pd-103 is reused as the target material.
Claim 17
Dependent Claim
58 words
The method of claim 1 wherein the step of purifying Pd-103 comprises: i) adding a solvent to remove the target material from the target support to produce a target material solution; ii) adding at least one carrier; iii) removing the at least one carrier from the target material solution; and iv) reducing the Pd to the metallic state.
Claim 18
Dependent Claim
29 words
The method of claim 16 wherein the step of removing the at least one carrier from the Pd, adsorbs and selectively removes impurities produced during the production of Pd-103.
Claim 19
Dependent Claim
20 words
The method of claim 17, wherein the carrier is silver, and an iodide salt is added to selectively remove silver.
Claim 20
Dependent Claim
22 words
The method of claim 17, wherein the carrier is rhodium, and it is removed from the Pd precipitate using an ion-exchange resin.
Claim 21
Dependent Claim
20 words
The method of claim 19, wherein rhodium is further removed from Pd-103 during reduction of Pd to the metallic state.
Claim 22
Independent Claim
42 words
A method of coating a silver device by emersion plating comprising, immersing the silver device in an acidified Pd solution, heating the Pd solution containing the silver device to produce a Pd-coated device, removing the Pd solution; and drying the Pd-coated device.
Claim 23
Independent Claim
42 words
A method of coating a silver device by emersion plating comprising, immersing the silver device in an acidified Pd solution, heating the Pd solution containing the silver device to produce a Pd-coated device, removing the Pd solution; and drying the Pd-coated device.
Claim 24
Dependent Claim
18 words
The method of claim 21 wherein the Pd solution is a 0.1 to 1.0 N HCl Pd solution.
Claim 25
Dependent Claim
11 words
A Pd-coated silver device produced by the method of claim 21.
Claim 26
Dependent Claim
41 words
The Pd-coated silver device of claim 23, wherein the Pd-coated silver device can comprise a variety of surface geometries, and is selected from the group consisting of: stent, expandable stent, catheter, seed, protheses, valves, and staples or other wound closure device.
References Cited (Backward Citations)
US3351049A
Cited
US4815449A
Cited
US4702228A
Cited
US4994013A
Cited
US5163896A
Cited
US5575749A
Cited
US5178745A
Cited
US5405309A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-11-07 | 2004-05-08 | 2004-11-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-11-07 | 2008-05-08 | 2008-11-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-11-07 | 2012-05-08 | 2012-11-07 | $7700.00 | Window Closed / Lapsed |