Method for pressure bonding metal members by utilizing eutectic reaction
Assignee: Hitachi Ltd
•
Filing: 1979-04-06
•
Granted: 1982-05-25
•
Expires: 1999-04-06
Abstract
Abstract A method for pressure bonding metal members by utilizing eutectic reaction comprising the steps of bringing two metal members of dissimilar metals to be bonded into contact with each other under a predetermined contacting pressure P 1 lower than the plastic deformation pressures of the metals of the two members and heating the contacting surfaces of the two members to a temperature lower than melting point temperatures of the metals and not lower than the eutectic temperature thereof to produce a liquid of eutectic composition by eutectic reaction between the surfaces of the two members to be bonded, applying an upset pressure P 2 higher than the contacting pressure P 1 to the surfaces to be bonded to squeeze out the liquid from the contacting surfaces of the two members to outside, and cooling the bonded surfaces of the two members. When the members to be joined by pressure bonding are of the same metal, an insert comprising an element undergoing eutectic reaction with the metal of the two members is interposed between the surfaces of the two members to be bonded.
Inventors
- 👤 Kunio Miyazaki
- 👤 Takeo Tamamura
- 👤 Tomio Iizuka
- 👤 Hitoshi Suzuki
- 👤 Izumi Ochiai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 09:42
CPC Classifications
B; B23; B23K; B23K13/00; B23K13/01; B23K13/02; B23K20/00; B23K20/22; B23K20/233
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
111 words
A method for pressure bonding metal members which comprises the steps of: forming contacting surfaces of at least two metal members, wherein the contacting surfaces contain an element which forms a eutectic composition upon heating to a temperature at which a eutectic reaction takes place, heating the contacting surfaces under a pressure lower than a plastic deformation pressure of the members for a time sufficient to form the eutectic composition, increasing the contacting pressure applied to the contacting surfaces to squeeze out substantially all of the liquid of eutectic composition from the contacting surfaces before the temperature becomes lower than eutectic temperature, and cooling the bonded surfaces of the two members.
Claim 2
Independent Claim
111 words
A method for pressure bonding metal members which comprises the steps of: forming contacting surfaces of at least two metal members, wherein the contacting surfaces contain an element which forms a eutectic composition upon heating to a temperature at which a eutectic reaction takes place, heating the contacting surfaces under a pressure lower than a plastic deformation pressure of the members for a time sufficient to form the eutectic composition, increasing the contacting pressure applied to the contacting surfaces to squeeze out substantially all of the liquid of eutectic composition from the contacting surfaces before the temperature becomes lower than eutectic temperature, and cooling the bonded surfaces of the two members.
Claim 3
Independent Claim
171 words
A method for pressure bonding metal members by utilizing eutectic reaction, comprising the steps of: bringing two members of dissimilar metals to be pressure bonded into contact with each other under a predetermined contacting pressure P 1 lower than plastic deformation pressures of the metals of the two members and heating contacting surfaces of the two members to a temperature lower than melting point temperatures of the metals and not lower than a eutectic temperature thereof to produce a liquid of eutectic composition by eutectic reaction between surfaces of the two members to be bonded; applying an upset pressure P 2 higher than said contacting pressure P 1 to the surfaces of the two members to be bonded to squeeze out substantially all of the liquid eutectic composition from the contacting surfaces to outside; and cooling the bonded surfaces of the two members at a cooling rate for substantially preventing the production of a phase by eutectic reaction and an intermetallic compound phase on the bonded surfaces of the two members.
Claim 4
Independent Claim
171 words
A method for pressure bonding metal members by utilizing eutectic reaction, comprising the steps of: bringing two members of dissimilar metals to be pressure bonded into contact with each other under a predetermined contacting pressure P 1 lower than plastic deformation pressures of the metals of the two members and heating contacting surfaces of the two members to a temperature lower than melting point temperatures of the metals and not lower than a eutectic temperature thereof to produce a liquid of eutectic composition by eutectic reaction between surfaces of the two members to be bonded; applying an upset pressure P 2 higher than said contacting pressure P 1 to the surfaces of the two members to be bonded to squeeze out substantially all of the liquid eutectic composition from the contacting surfaces to outside; and cooling the bonded surfaces of the two members at a cooling rate for substantially preventing the production of a phase by eutectic reaction and an intermetallic compound phase on the bonded surfaces of the two members.
Claim 5
Dependent Claim
36 words
A method for pressure bonding metal members by utilizing eutectic reaction as set forth in claim 2, wherein one of said contacting surfaces of said two metal members is formed with at least one projecting portion.
Claim 6
Independent Claim
154 words
A method for pressure bonding to metal members by utilizing eutectic reaction the method comprising the steps of: bringing together a member of aluminum and a member of copper to be pressure bonded into contact with each other under a predetermined contacting pressure P 1 , lower than plastic deformation pressure of the aluminum and copper and heating contact surfaces of the two members to a range between eutectic temperature and eutectic temperature +50° C.; applying an upset pressure P 2 to the surfaces of the members to be bonded in a range of between 1.5 and 7.0 kg per mm 2 to squeeze out substantially all the liquid eutectic composition from the contacting surfaces to outside; and cooling the bonded surfaces of the two members at a cooling rate for substantially preventing the production of a phase by eutectic reaction and an intermetallic compound phase on the bonded surfaces of the two members.
Claim 7
Independent Claim
154 words
A method for pressure bonding to metal members by utilizing eutectic reaction the method comprising the steps of: bringing together a member of aluminum and a member of copper to be pressure bonded into contact with each other under a predetermined contacting pressure P 1 , lower than plastic deformation pressure of the aluminum and copper and heating contact surfaces of the two members to a range between eutectic temperature and eutectic temperature +50° C.; applying an upset pressure P 2 to the surfaces of the members to be bonded in a range of between 1.5 and 7.0 kg per mm 2 to squeeze out substantially all the liquid eutectic composition from the contacting surfaces to outside; and cooling the bonded surfaces of the two members at a cooling rate for substantially preventing the production of a phase by eutectic reaction and an intermetallic compound phase on the bonded surfaces of the two members.
Claim 8
Dependent Claim
25 words
A method for pressure bonding metal members by utilizing eutectic reaction as set forth in claim 2, wherein said dissimilar metals are copper and silver.
Claim 9
Independent Claim
175 words
A method for pressure bonding metal members by utilizing eutectic reaction, comprising the steps of: bringing two members of dissimilar metals to be pressure bonded into contact with each other under a predetermined contacting pressure P 1 lower than a plastic deformation pressure of the metals of the two members and heating contact surfaces of the two members to a temperature lower than a melting point temperature of the metals and not lower than a eutectic temperature thereof to produce a liquid of eutectic composition by eutectic reaction between surfaces of the two members to be bonded; applying an upset pressure P 2 higher than said contacting pressure P 1 to the surfaces of the two members to be bonded to squeeze out substantially all of the liquid of eutectic composition from the contacting surfaces to outside; and rapidly cooling the bonded surfaces of the two members at a cooling rate for substantially preventing the production of a phase by eutectic reaction and an intermediate compound phase on the bonded surfaces of the two members.
Claim 10
Independent Claim
175 words
A method for pressure bonding metal members by utilizing eutectic reaction, comprising the steps of: bringing two members of dissimilar metals to be pressure bonded into contact with each other under a predetermined contacting pressure P 1 lower than a plastic deformation pressure of the metals of the two members and heating contact surfaces of the two members to a temperature lower than a melting point temperature of the metals and not lower than a eutectic temperature thereof to produce a liquid of eutectic composition by eutectic reaction between surfaces of the two members to be bonded; applying an upset pressure P 2 higher than said contacting pressure P 1 to the surfaces of the two members to be bonded to squeeze out substantially all of the liquid of eutectic composition from the contacting surfaces to outside; and rapidly cooling the bonded surfaces of the two members at a cooling rate for substantially preventing the production of a phase by eutectic reaction and an intermediate compound phase on the bonded surfaces of the two members.
Claim 11
Dependent Claim
25 words
A method for pressure bonding metal members by utilizing eutectic reaction as set forth in claim 6, wherein said dissimilar metals are aluminum and copper.
Claim 12
Dependent Claim
25 words
A method for pressure bonding metal members by utilizing eutectic reaction as set forth in claim 6, wherein said dissimilar metals are copper and silver.
Claim 13
Independent Claim
194 words
A method for pressure bonding metal members by utilizing eutectic reaction, comprising the steps of: placing an insert between two members of the same metal to be pressure bonded to maintain contacting surfaces of the two members and the insert interposed therebetween under a predetermined contacting pressure P 1 lower than plastic deformation pressures of the metal of the two members, said insert comprising an element undergoing eutectic reaction with the metal of the two members, and heating the contacting surfaces of the two members and the insert therebetween to a temperature lower than a melting point temperature of the metal of the two members and not lower than a eutectic temperature of the element of the insert and the metal of the two members to produce a liquid of eutectic composition by eutectic reaction between the surfaces of the two members to be bonded; applying an upset pressure P 2 higher than said contacting pressure P 1 to the surfaces of the two members to be bonded to squeeze out substantially all of the liquid of eutectic composition from the contacting surfaces to outside; and cooling the bonded surfaces of the two members.
Claim 14
Independent Claim
194 words
A method for pressure bonding metal members by utilizing eutectic reaction, comprising the steps of: placing an insert between two members of the same metal to be pressure bonded to maintain contacting surfaces of the two members and the insert interposed therebetween under a predetermined contacting pressure P 1 lower than plastic deformation pressures of the metal of the two members, said insert comprising an element undergoing eutectic reaction with the metal of the two members, and heating the contacting surfaces of the two members and the insert therebetween to a temperature lower than a melting point temperature of the metal of the two members and not lower than a eutectic temperature of the element of the insert and the metal of the two members to produce a liquid of eutectic composition by eutectic reaction between the surfaces of the two members to be bonded; applying an upset pressure P 2 higher than said contacting pressure P 1 to the surfaces of the two members to be bonded to squeeze out substantially all of the liquid of eutectic composition from the contacting surfaces to outside; and cooling the bonded surfaces of the two members.
Claim 15
Dependent Claim
34 words
A method for pressure bonding metal members by utilizing eutectic reaction as set forth in claim 9, wherein said metal forming said two members is aluminum, and wherein said insert is formed of copper.
Claim 16
Dependent Claim
34 words
A method for pressure bonding metal members by utilizing eutectic reaction as set forth in claim 9, wherein said metal forming said two members is aluminum, and wherein said insert is formed of silver.
Claim 17
Dependent Claim
34 words
A method for pressure bonding metal members by utilizing eutectic reaction as set forth in claim 9, wherein said metal forming said two members is aluminum, and wherein said insert is formed of silicon.
Claim 18
Dependent Claim
54 words
A method for pressure bonding metal members by utilizing eutectic reaction as set forth in claim 9, wherein said metal forming said two members is aluminum, and wherein said insert is formed of a material selected from the group consisting of hypereutectic alloys of aluminum and silver, aluminum and copper and aluminum and silicon.
Claim 19
Dependent Claim
34 words
A method for pressure bonding metal members by utilizing eutectic reaction as set forth in claim 9, wherein said metal forming said two members is copper, and wherein said insert is formed of silver.
Claim 20
Dependent Claim
34 words
A method for pressure bonding metal members by utilizing eutectic reaction as set forth in claim 9, wherein said metal forming said two members is copper, and wherein said inset is formed of aluminum.
Claim 21
Dependent Claim
52 words
A method for pressure bonding metal members by utilizing eutectic reaction as set forth in claim 9, wherein said metal forming said two members is copper, and wherein said insert is formed of a material selected from the group consisting of the hypereutectic alloys of copper and silver and copper and aluminum.
Claim 22
Dependent Claim
38 words
A method for pressure bonding metal members by utilizing eutectic reaction as set forth in claim 1, wherein the contacting pressure applied is sufficient to squeeze out all of the liquid eutectic composition remaining between the contacting surfaces.
Claim 23
Dependent Claim
33 words
A method for pressure bonding metal members by utilizing eutectic reaction as set forth in claim 1, wherein the step of increasing the contacting pressure includes applying the contact pressure with an impact.
Claim 24
Independent Claim
43 words
A method for pressure bonding metal members by utilizing eutectic reaction as set forth in one of claims 2, 6, or 9, wherein the upsetting pressure applied is sufficinet to squeeze out all of the liquid eutectic composition remaining between the contacting surfaces.
Claim 25
Independent Claim
31 words
A method for pressure bonding metal members by utilizing eutectic reaction as set forth in one of claims 2, 6, or 9, wherein the upset pressure is applied with an impact.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-05-24 | 1985-11-23 | 1986-05-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-05-24 | 1989-11-23 | 1990-05-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-05-24 | 1993-11-23 | 1994-05-25 | $7700.00 | Window Closed / Lapsed |