Crystalline copolyamide from terephthalic acid, isophthalic acid and C.sub.6
Assignee: Syensqo Specialty Polymers USA LLC
•
Filing: 1985-05-16
•
Granted: 1986-10-14
•
Expires: 2005-05-16
Abstract
Abstract A crystalline polyamide which has improved tensile strength and which has a heat deflection temperature in excess of 240 DEG C. when filled is formed from dicarboxylic acid compounds comprising compounds of terephthalic acid and isophthalic acid in a molar ratio of at least 80:20 to about 99:1 and diamines comprising hexamethylene diamine and trimethylhexamethylene diamine in a molar ratio of about 98:2 to about 60:40.
Inventors
- 👤 Wassily Poppe
- 👤 Yu-Tsai Chen
- 👤 Edward E. Paschke
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 14:38
CPC Classifications
C; C08; C08G; C08G69/00; C08G69/02; C08G69/26; C08G69/265
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
65 words
A crystalline polyamide resin having improved tensile strength formed from dicarboxylic acid compounds and diamines wherein said dicarboxylic acid compounds comprise compounds of terephthalic acid (TA) and isophthalic acid (IA) in a molar ratio TA:IA of at least 80:20 to about 99:1 and wherein said diamines comprise hexamethylene diamine (HMDA) and trimethylhexamethylene diamine (TMHMDA) in a molar ratio HMDA:TMHMDA of about 98:2 to about 60:40.
Claim 2
Dependent Claim
65 words
A crystalline polyamide resin having improved tensile strength formed from dicarboxylic acid compounds and diamines wherein said dicarboxylic acid compounds comprise compounds of terephthalic acid (TA) and isophthalic acid (IA) in a molar ratio TA:IA of at least 80:20 to about 99:1 and wherein said diamines comprise hexamethylene diamine (HMDA) and trimethylhexamethylene diamine (TMHMDA) in a molar ratio HMDA:TMHMDA of about 98:2 to about 60:40.
Claim 3
Dependent Claim
26 words
The polyamide resin of claim 1 wherein said TA:IA molar ratio is about 75:25 to 90:10 and said HMDA:TMHMDA molar ratio is about 65:35 to 95:5.
Claim 4
Dependent Claim
17 words
The polyamide resin of claim 1 wherein said dicarboxylic acid compounds are terephthalic acid and isophthalic acid.
Claim 5
Dependent Claim
35 words
The polyamide resin of claim 1 in combination with about 10 to about 60 weight percent of a filler selected from the group consisting of glass fibers, glass beads, minerals, graphite fibers, or mixtures thereof.
Claim 6
Dependent Claim
10 words
A molded article comprising the polyamide resin of claim 1.
Claim 7
Dependent Claim
102 words
A blend having a heat deflection temperature of at least 240° C., said blend comprising (1) about 80 to about 50 parts by weight of a polyamide resin of terephthalic acid (TA) and isophthalic acid (IA) and diamines wherein the molar ratio of TA to IA is at least 80:20 to about 95:5 and wherein said diamines comprise hexamethylene diamine (HMDA) and trimethylhexamethylene diamine (TMHMDA) in a molar ratio HMDA:TMHMDA of about 98:2 to about 60:40, and (2) about 20 to about 50 parts by weight of a filler selected from the group consisting of glass fibers, graphite fibers, and mixtures thereof.
Claim 8
Dependent Claim
102 words
A blend having a heat deflection temperature of at least 240° C., said blend comprising (1) about 80 to about 50 parts by weight of a polyamide resin of terephthalic acid (TA) and isophthalic acid (IA) and diamines wherein the molar ratio of TA to IA is at least 80:20 to about 95:5 and wherein said diamines comprise hexamethylene diamine (HMDA) and trimethylhexamethylene diamine (TMHMDA) in a molar ratio HMDA:TMHMDA of about 98:2 to about 60:40, and (2) about 20 to about 50 parts by weight of a filler selected from the group consisting of glass fibers, graphite fibers, and mixtures thereof.
Claim 9
Dependent Claim
11 words
A molded article comprising the filled polyamide resin of claim 4.
Claim 10
Dependent Claim
120 words
A crystalline injection moldable polyamide copolymer of terephthalic acid and isophthalic acid and an aliphatic diamines, which copolymer has a heat deflection temperature of at least about 240° C. when molded and filled with glass fibers, glass beads or graphite fibers, comprising the following recurring structural units: ##STR2## wherein the mole ratio of A units to B units is between about 81/19 to about 99/1 and R is a straight chain aliphatic hydrocarbon radical comprising 6 carbon atoms and a trimethyl-substituted saturated hydrocarbon radical 6 carbon atoms in length with two of three methyl groups on the same carbon atom wherein the mole ratio of the straight chain hydrocarbon to the trimethyl substituted hydrocarbon is about 55/45 to about 98/2.
Claim 11
Dependent Claim
120 words
A crystalline injection moldable polyamide copolymer of terephthalic acid and isophthalic acid and an aliphatic diamines, which copolymer has a heat deflection temperature of at least about 240° C. when molded and filled with glass fibers, glass beads or graphite fibers, comprising the following recurring structural units: ##STR2## wherein the mole ratio of A units to B units is between about 81/19 to about 99/1 and R is a straight chain aliphatic hydrocarbon radical comprising 6 carbon atoms and a trimethyl-substituted saturated hydrocarbon radical 6 carbon atoms in length with two of three methyl groups on the same carbon atom wherein the mole ratio of the straight chain hydrocarbon to the trimethyl substituted hydrocarbon is about 55/45 to about 98/2.
References Cited (Backward Citations)
US3475387A
Cited
US3926924A
Cited
US3627736A
Cited
US3941755A
Cited
US4022756A
Cited
US4113708A
Cited
US4238603A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-10-13 | 1990-04-14 | 1990-10-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-10-13 | 1994-04-14 | 1994-10-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-10-13 | 1998-04-14 | 1998-10-14 | $7700.00 | Window Closed / Lapsed |