Method of manufacturing a semiconductor device, in which a silicon slice is locally provided with field oxide with a channel stopper
Assignee: US Philips Corp
•
Filing: 1986-06-02
•
Granted: 1988-05-10
•
Expires: 2006-06-02
Abstract
Abstract A method of manufacturing a semiconductor device, in which a silicon slice (1) is locally provided with field oxide (10, 30) with a subjacent channel stopper zone (12, 32), which are formed during the same oxidizing heat treatment. The formed field oxide layer (10, 30) is removed in part by an etching treatment with a thinner and smaller field oxide layer (11, 31) being formed. The temperature at which the heat treatment is carried out is chosen so that lateral diffusion (15, 35) of the dopant forming the channel stopper zone (12, 32) extends in lateral direction practically over the same distance as the reduced field oxide layer (11, 31). Thus, it is achieved that, for example, for the manufacture of a MOS transistor an oxidation mask (7) having substantially the same width as a channel zone (17) to be formed can be used.
Inventors
- 👤 Jozef J. J. Bastiaens
- 👤 Marcus A. Sprokel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 06:20
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10W; H10W10/00; H10W10/10; H10W10/13; H10P; H10P14/00; H10P14/20; H10P14/24; H10P50/00; H10P50/20; H10P50/28; H10P50/282; H10P95/00; H10P95/90; H10W10/01; H10W10/011; H10W10/012; H10W10/0125; H10W10/0126
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
225 words
A method of manufacturing a semiconductor device comprising the steps of (a) forming an oxidation mask locally on a surface of a silicon slice; (b) providing a layer portion of said surface laterally adjacent to said oxidation mask with atoms of dopant; (c) subjecting said silicon slice to a first oxidizing heat treatment which forms a field oxide layer on said layer portion adjoining said oxidation mask and which forms a channel stopper zone beneath said field oxide layer by diffusion of said atoms of said dopant into said silicon slice, said channel stopper zone being extended in the lateral direction for a similar amount as said field oxide; (d) removing said oxidation mask from said surface of said silicon slice by etching; (e) subjecting said silicon slice to a second oxidizing heat treatment to form a gate oxide at said surface of said silicon slice where said oxidation mask has been removed; and (f) subjecting said silicon slice to a further etching treatment to etch away a part of said field oxide layer, said field oxide layer becoming thinner and smaller in a lateral direction, wherein said silicon slice between said first and said second oxidizing heat treatment is subjected to an additional oxidizing heat treatment, and subsequent etching is carried out to etch away silicon oxide formed by said additional oxidizing heat treatment.
Claim 2
Independent Claim
225 words
A method of manufacturing a semiconductor device comprising the steps of (a) forming an oxidation mask locally on a surface of a silicon slice; (b) providing a layer portion of said surface laterally adjacent to said oxidation mask with atoms of dopant; (c) subjecting said silicon slice to a first oxidizing heat treatment which forms a field oxide layer on said layer portion adjoining said oxidation mask and which forms a channel stopper zone beneath said field oxide layer by diffusion of said atoms of said dopant into said silicon slice, said channel stopper zone being extended in the lateral direction for a similar amount as said field oxide; (d) removing said oxidation mask from said surface of said silicon slice by etching; (e) subjecting said silicon slice to a second oxidizing heat treatment to form a gate oxide at said surface of said silicon slice where said oxidation mask has been removed; and (f) subjecting said silicon slice to a further etching treatment to etch away a part of said field oxide layer, said field oxide layer becoming thinner and smaller in a lateral direction, wherein said silicon slice between said first and said second oxidizing heat treatment is subjected to an additional oxidizing heat treatment, and subsequent etching is carried out to etch away silicon oxide formed by said additional oxidizing heat treatment.
Claim 3
Dependent Claim
32 words
A method according to claim 1, wherein said field oxide layer formed during said first oxidizing heat treatment is etched away to a thickness of 50 to 70% of an original thickness.
Claim 4
Dependent Claim
37 words
A method according to claim 1 or claim 2, wherein said oxidation mask is formed of a first layer of silicon oxynitride on said silicon slice and a second layer of silicon nitride on said first layer.
Claim 5
Dependent Claim
24 words
A method according to claim 3, wherein said first oxidizing heat treatment is carried out in a temperature range of 825° to 875° C.
Claim 6
Dependent Claim
25 words
A method according to claim 4, wherein said first oxidizing heat treatment is carried out in a dry gas mixture containing oxygen, nitrogen and hydrogen.
Claim 7
Dependent Claim
24 words
A method according to claim 3, wherein said first layer of silicon oxynitride is deposited by an LPCVD process from silane, laughing-gas and ammonia.
Claim 8
Dependent Claim
26 words
A method according to claim 6, wherein said LPCVD process is carried out to provide a refractive index of 1.6 to 1.8 to said silicon oxynitride.
Claim 9
Independent Claim
205 words
A method of manufacturing a semiconductor device comprising the steps of (a) forming an oxidation mask locally on a surface of a silicon slice; (b) providing a layer portion of said surface laterally adjacent to said oxidation mask with atoms of dopant; (c) subjecting said silicon slice to a first oxidizing heat treatment which forms a field oxide layer on said layer portion adjoining said oxidation mask and which forms a channel stopper zone beneath said field oxide layer by diffusion of said atoms of said dopant into said silicon slice, said channel stopper zone being extended in the lateral direction for a similar amount as said field oxide; (d) removing said oxidation mask from said surface of said silicon slice by etching (e) subjecting said silicon slice to a second oxidizing heat treatment to form a gate oxide at said surface of said silicon slice where said oxidation mask has been removed; and subjecting said silicon slice to a further etching treatment to etch away a part of said field oxide layer, said field oxide layer becoming thinner and smaller in a lateral direction, wherein said channel stopper zone is extended in a lateral direction for a similar amount as said field oxide layer.
Claim 10
Independent Claim
205 words
A method of manufacturing a semiconductor device comprising the steps of (a) forming an oxidation mask locally on a surface of a silicon slice; (b) providing a layer portion of said surface laterally adjacent to said oxidation mask with atoms of dopant; (c) subjecting said silicon slice to a first oxidizing heat treatment which forms a field oxide layer on said layer portion adjoining said oxidation mask and which forms a channel stopper zone beneath said field oxide layer by diffusion of said atoms of said dopant into said silicon slice, said channel stopper zone being extended in the lateral direction for a similar amount as said field oxide; (d) removing said oxidation mask from said surface of said silicon slice by etching (e) subjecting said silicon slice to a second oxidizing heat treatment to form a gate oxide at said surface of said silicon slice where said oxidation mask has been removed; and subjecting said silicon slice to a further etching treatment to etch away a part of said field oxide layer, said field oxide layer becoming thinner and smaller in a lateral direction, wherein said channel stopper zone is extended in a lateral direction for a similar amount as said field oxide layer.
Claim 11
Dependent Claim
32 words
A method according to claim 8, wherein said field oxide layer formed during said first oxidizing heat treatment is etched away to a thickness of 50 to 70% of an original thickness.
Claim 12
Dependent Claim
37 words
A method according to claim 8 or claim 9, wherein said oxidation mask is formed of a first layer of silicon oxynitride on said silicon slice and a second layer of silicon nitride on said first layer.
Claim 13
Dependent Claim
24 words
A method according to claim 10, wherein said first oxidizing heat treatment is carried out in a temperature range of 825° to 875° C.
Claim 14
Dependent Claim
25 words
A method according to claim 11, wherein said first oxidizing heat treatment is carried out in a dry gas mixture containing oxygen, nitrogen and hydrogen.
Claim 15
Dependent Claim
24 words
A method according to claim 10, wherein said first layer of silicon oxynitride is deposited by an LPCVD process from silane, laughing-gas and ammonia.
Claim 16
Dependent Claim
26 words
A method according to claim 7, wherein said LPCVD process is carried out to provide a refractive index of 1.6 to 1.8 to said silicon oxynitride.
References Cited (Backward Citations)
US4110899A
Cited
US4268321A
Cited
EP0071203A2
Cited
US4574465A
Cited
US4407696A
Cited
US4601098A
Cited
JPS60128635A
Cited
US4569117A
Cited
US4622096A
Cited
US4577394A
Cited
US4551910A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-05-10 | 1991-11-09 | 1992-05-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-05-10 | 1995-11-09 | 1996-05-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-05-10 | 1999-11-09 | 2000-05-10 | $7700.00 | Window Closed / Lapsed |