Assignee: Roehm GmbH Darmstadt
•
Filing: 1988-07-13
•
Granted: 1990-01-09
•
Expires: 2008-07-13
Abstract
Abstract Polymer powders comprising aggregated polymer particles, said powders having a low content of fines and being suitable as processing aids in the manufacture of polyvinyl chloride, are made by spray drying an aqueous dispersion (latex) of two emulsion polymers, one of which has a dynamic glass transition temperature above 90° C. and the other of which has a dynamic glass transition below 105° C., the latter being at least 10 K. degrees below the former.
Inventors
- 👤 Wolfgang Klesse
- 👤 Hubert Rauch
- 👤 Peter J. Arndt
- 👤 Norbert Suetterlin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 22:24
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/12; C08J3/122; B; B01; B01D; B01D1/00; B01D1/16; B01D1/18; C08F; C08F6/00; C08F6/14; C08F6/18
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
114 words
Powder grains consisting essentially of aggregated particles of two different polymers (A) and (B), wherein (1) 70 to 99.5 percent by weight of said powder grains comprise particles of polymer (A) having a dynamic glass transition temperature which is above 90° C., said particles of polymer (A) not being sintered together, and (2) 30 to 0.5 percent by weight of said powder grains comprise particles of polymer (B) having a dynamic glass transition temperature from 55° C. to 90° C. and which is at least 10 Centigrade degrees less than the dynamic glass transition temperature of polymer (A), said particles of polymer (B) being sintered to one another and to particles of polymer (A).
Claim 2
Dependent Claim
114 words
Powder grains consisting essentially of aggregated particles of two different polymers (A) and (B), wherein (1) 70 to 99.5 percent by weight of said powder grains comprise particles of polymer (A) having a dynamic glass transition temperature which is above 90° C., said particles of polymer (A) not being sintered together, and (2) 30 to 0.5 percent by weight of said powder grains comprise particles of polymer (B) having a dynamic glass transition temperature from 55° C. to 90° C. and which is at least 10 Centigrade degrees less than the dynamic glass transition temperature of polymer (A), said particles of polymer (B) being sintered to one another and to particles of polymer (A).
Claim 3
Dependent Claim
22 words
Powder grains as in claim 1 wherein the particles of polymer (B) are smaller in size than the particles of polymer (A).
Claim 4
Dependent Claim
82 words
Powder grains as in claim 1 wherein polymer (A) comprises 70 to 100 percent by weight of at least one member selected from the group consisting of methyl methacrylate, styrene, acrylic acid, methacrylic acid, acrylonitrile, and methacrylonitrile; 0 to 20 percent by weight of a member selected from the group consisting of alkyl acrylates and alkyl methacrylates other than methyl methacrylate; and 0 to 10 percent by weight of another copolymerizable vinyl monomer different from the members of both of said groups.
Claim 5
Dependent Claim
51 words
Powder grains as in claim 1 wherein polymer (B) comprises from 15 to 100 percent by weight of an alkyl acrylate or of an alkyl methacrylate having more than three carbon atoms in the alkyl group thereof and from 0 to 85 percent by weight of another, different, copolymerizable vinyl monomer.
Claim 6
Independent Claim
183 words
A method for making powder grains comprising aggregated particles of at least two different polymers, (A) and (B), which method comprises spray drying in an air stream an aqueous dispersion consisting essentially of latex particles of said two different polymers such that said powder grains consist essentially of 70 to 99.5 percent by weight of particles of polymer (A), polymer (A) having a dynamic glass transition temperature above 90° C., and from 30 to 0.5 percent by weight of particles of polymer (B), polymer (B) having a dynamic glass transition temperature from 55° C. to 90° C. and which is at least 10 Centigrade degrees less than the dynamic glass transition temperature of polymer (A), said powder particles being separated from the air stream used for drying said aqueous dispersions at a temperature in the range of temperatures between the static glass transition temperature of polymer (A) and the static glass transition temperature of polymer (B), whereby the particles of polymer (A) are not sintered together but the particles of polymer (B) are sintered to one another and to particles of polymer (A).
Claim 7
Independent Claim
183 words
A method for making powder grains comprising aggregated particles of at least two different polymers, (A) and (B), which method comprises spray drying in an air stream an aqueous dispersion consisting essentially of latex particles of said two different polymers such that said powder grains consist essentially of 70 to 99.5 percent by weight of particles of polymer (A), polymer (A) having a dynamic glass transition temperature above 90° C., and from 30 to 0.5 percent by weight of particles of polymer (B), polymer (B) having a dynamic glass transition temperature from 55° C. to 90° C. and which is at least 10 Centigrade degrees less than the dynamic glass transition temperature of polymer (A), said powder particles being separated from the air stream used for drying said aqueous dispersions at a temperature in the range of temperatures between the static glass transition temperature of polymer (A) and the static glass transition temperature of polymer (B), whereby the particles of polymer (A) are not sintered together but the particles of polymer (B) are sintered to one another and to particles of polymer (A).
Claim 8
Dependent Claim
56 words
A method as in claim 5 wherein said powder particles are separated from the air stream used for drying said aqueous dispersion at a temperature within the range of temperatures at which polymer (A) has a shear modulus of at least 800N/mm 2 and polymer (B) has a shear modulus not greater than 800N/mm 2 .
Claim 9
Dependent Claim
9 words
Powder particles made by the method of claim 5.
References Cited (Backward Citations)
DE2101808A1
Cited
GB1365581A
Cited
US3998768A
Cited
US4112215A
Cited
DE2629924A1
Cited
US4071653A
Cited
US4169737A
Cited
US4151138A
Cited
US4199486A
Cited
US4268636A
Cited
EP0030590A1
Cited
US4433076A
Cited
US4520172A
Cited
US4522959A
Cited
DE3344242A1
Cited
DE3436477A1
Cited
US4722595A
Cited
US4737357A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-01-08 | 1993-07-10 | 1994-01-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-01-08 | 1997-07-10 | 1998-01-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-01-08 | 2001-07-10 | 2002-01-09 | $7700.00 | Window Closed / Lapsed |