Diffusion barrier for copper features
Assignee: Microelectronics and Computer Technology Corp
•
Filing: 1991-03-15
•
Granted: 1992-11-17
•
Expires: 2011-03-15
Abstract
Abstract A diffusion barrier which reduces the diffusion of a copper feature into an oxygen containing polymer is provided by a copper metal alloy. The diffusion barrier is fabricated by coating a metal on a copper feature, heating the metal and copper feature to form an alloy of the copper feature and the metal, etching the non-alloyed metal which covers the alloy, and depositing an oxygen containing polymer on the alloy. Preferably the metal is aluminum and a copper aluminum alloy diffusion barrier is at least 300 angstroms thick and contains at least 8 percent aluminum on the surface in contact with the polymer.
Inventors
- 👤 Nalin Kumar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 01:48
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/40; H10W20/41; H10W20/425; H10W20/01; H10W20/031; H10W20/032; H10W20/038; H10W20/039; H10W20/047; H10W20/049; H10W20/435; H10W20/44; H10W20/4403; H10W20/4421; H10W20/4424
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
78 words
A method for making a diffusion barrier for a copper feature, comprising the following steps in the sequence set forth: coating a metal on a copper feature; heating the metal and copper feature to form an alloy of the copper feature and the metal on the copper feature; etching the non-alloyed metal; and depositing an oxygen containing polymer over the alloy, wherein the alloy provides a diffusion barrier which reduces diffusion of the copper feature into the polymer.
Claim 2
Independent Claim
78 words
A method for making a diffusion barrier for a copper feature, comprising the following steps in the sequence set forth: coating a metal on a copper feature; heating the metal and copper feature to form an alloy of the copper feature and the metal on the copper feature; etching the non-alloyed metal; and depositing an oxygen containing polymer over the alloy, wherein the alloy provides a diffusion barrier which reduces diffusion of the copper feature into the polymer.
Claim 3
Dependent Claim
18 words
The method of claim 1 wherein the metal is selected from the group consisting of aluminum and nickel.
Claim 4
Dependent Claim
17 words
The method of claim 1 wherein the metal is aluminum and the alloy is copper aluminum alloy.
Claim 5
Dependent Claim
16 words
The method of claim 3 wherein the copper aluminum alloy is at least 300 angstroms thick.
Claim 6
Dependent Claim
20 words
The method of claim 3 wherein the outer surface of the copper aluminum alloy contains at least 8 percent aluminum.
Claim 7
Dependent Claim
28 words
The method of claim 3 wherein the copper feature protrudes above a base and the coating forms an aluminum layer which covers the copper feature and the base.
Claim 8
Dependent Claim
25 words
The method of claim 3 wherein after the copper aluminum alloy is formed the electrical resistivity of the copper feature is at most 10 micro-ohm-cm.
Claim 9
Dependent Claim
31 words
The method of claim 3 wherein the etching is by a wet chemical etchant which removes all of the non-alloyed aluminum without removing the copper aluminum alloy or the copper feature.
Claim 10
Dependent Claim
15 words
The method of claim 3 wherein the heating is performed by a rapid thermal anneal.
Claim 11
Independent Claim
126 words
A method for making a diffusion barrier for a copper feature, comprising the following steps in the sequence set forth: coating a layer of aluminum at least 300 angstroms thick on a copper feature; heating the aluminum and copper feature to form a copper aluminum alloy at least 300 angstroms thick which covers the copper feature, adheres to the copper feature, and is covered by non-alloyed aluminum; etching the non-alloyed aluminum to expose an outer surface of copper aluminum alloy which contains at least 8 percent aluminum; and depositing an oxygen containing polymer on the outer surface of the copper aluminum alloy, wherein the copper aluminum alloy adheres to the polymer and provides a diffusion barrier which reduces diffusion of the copper feature into the polymer.
Claim 12
Independent Claim
126 words
A method for making a diffusion barrier for a copper feature, comprising the following steps in the sequence set forth: coating a layer of aluminum at least 300 angstroms thick on a copper feature; heating the aluminum and copper feature to form a copper aluminum alloy at least 300 angstroms thick which covers the copper feature, adheres to the copper feature, and is covered by non-alloyed aluminum; etching the non-alloyed aluminum to expose an outer surface of copper aluminum alloy which contains at least 8 percent aluminum; and depositing an oxygen containing polymer on the outer surface of the copper aluminum alloy, wherein the copper aluminum alloy adheres to the polymer and provides a diffusion barrier which reduces diffusion of the copper feature into the polymer.
Claim 13
Dependent Claim
20 words
The method of claim 10 wherein the heating is between 400° C. to 600° C. for 30 to 180 minutes.
Claim 14
Dependent Claim
15 words
The method of claim 10 wherein the heating is performed by a rapid thermal anneal.
Claim 15
Dependent Claim
17 words
The method of claim 12 wherein the rapid thermal anneal is approximately 1100° C. for 1 minute.
Claim 16
Dependent Claim
14 words
The method of claim 10 wherein the etching is by a wet chemical etchant.
Claim 17
Dependent Claim
10 words
The method of claim 10 wherein the polymer is polyimide.
Claim 18
Dependent Claim
66 words
The method of claim 10 wherein a plurality of spaced copper features protrude above the top surface of a base, prior to etching the layer of aluminum entirely covers the outer surface of the copper features and the top surface of the base, and after etching the non-alloyed aluminum on the top surface of the base between the copper aluminum alloy covered copper features is removed.
Claim 19
Dependent Claim
14 words
The method of claim 16 wherein the base is part of an electronic component.
Claim 20
Dependent Claim
14 words
The method of claim 17 wherein the electronic component is an electrical interconnect substrate.
Claim 21
Dependent Claim
15 words
The method of claim 18 wherein the base is polyimide and the polymer is polyimide.
References Cited (Backward Citations)
US4019877A
Cited
US4372809A
Cited
US4650545A
Cited
US4717439A
Cited
JPH0199239A
Cited
JPH01204449A
Cited
JPH01231351A
Cited
JPH01232746A
Cited
JPH01239954A
Cited
US4810332A
Cited
US4983250A
Cited
US4952275A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-11-17 | 1996-05-18 | 1996-11-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-11-17 | 2000-05-18 | 2000-11-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-11-17 | 2004-05-18 | 2004-11-17 | $7700.00 | Window Closed / Lapsed |