US5308802A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Sol-gel process of making glass, particulary gradient-index glass
Assignee: University of Rochester
•
Filing: 1993-06-25
•
Granted: 1994-05-03
•
Expires: 2013-06-25
Abstract
Abstract The present invention relates to a process for making glass by the sol-gel process. A mixture of silicon alkoxide, at least two other metal alkoxides, and alcohol in a solution sufficiently acidic to hydrolyze partially the silicon alkoxide is formed. Water is then added under agitation to convert the metal alkoxides to a network of corresponding metal oxides suitable for gelation. The mixture containing the network of metal oxides is then molded for a sufficient time to form a gel. Substantially only oxides of one of the at least two other metals is then removed from the gel, which is then fixed in a liquid capable of arresting such additional removal. The fixed gel is then dried and sintered to form a glass. The step of removing the at least one other metal oxide from the gel can be followed with a step of withdrawing partially oxides of one of the remaining at least two other metals in order to form a transparent gradient-index glass after sintering.
Inventors
- 👤 Niels Haun
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 03:36
CPC Classifications
C; C03; C03C; C03C1/00; C03C1/006
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
108 words
A process for making glass comprising: forming a mixture of a silicon alkoxide, at least two other metal alkoxides, and an alcohol in a solution sufficiently acidic to hydrolyze partially the silicon alkoxide; adding water to the mixture to convert the metal alkoxides to a network of corresponding metal oxides suitable for gelation; containing the mixture containing the network of metal oxides for sufficient time to form a gel; removing substantially only one of the at least two other metal oxides from the gel; fixing the gel in a liquid capable of arresting said removing; drying the fixed gel; and sintering the dried gel to form a glass.
Claim 2
Dependent Claim
108 words
A process for making glass comprising: forming a mixture of a silicon alkoxide, at least two other metal alkoxides, and an alcohol in a solution sufficiently acidic to hydrolyze partially the silicon alkoxide; adding water to the mixture to convert the metal alkoxides to a network of corresponding metal oxides suitable for gelation; containing the mixture containing the network of metal oxides for sufficient time to form a gel; removing substantially only one of the at least two other metal oxides from the gel; fixing the gel in a liquid capable of arresting said removing; drying the fixed gel; and sintering the dried gel to form a glass.
Claim 3
Dependent Claim
23 words
A process according to claim 1, wherein the at least two other metals are a gel structure modifying metal and an additional metal.
Claim 4
Dependent Claim
22 words
A process according to claim 2, wherein the additional metal is selected from the group consisting of titanium, zirconium, and mixtures thereof.
Claim 5
Dependent Claim
14 words
A process according to claim 2, wherein the gel structure modifying metal is aluminum.
Claim 6
Dependent Claim
52 words
A process according to claim 2, wherein an oxide of substantially all the gel structure modifying metal is taken out of the gel during said removing and said process further comprises: withdrawing an oxide of the additional metal from the gel after said removing the oxide of the gel structure modifying metal.
Claim 7
Dependent Claim
20 words
A process according to claim 5, wherein the additional metal is titanium and the gel structure modifying metal is aluminum.
Claim 8
Dependent Claim
21 words
A process according to claim 1, wherein said removing is carried out by contacting the gel with a monocarboxylic acid solvent.
Claim 9
Dependent Claim
29 words
A process according to claim 7, wherein the monocarboxylic acid solvent is selected from the group consisting of acetic acid, formic acid, propionic acid, butyric acid, and mixtures thereof.
Claim 10
Dependent Claim
14 words
A process according to claim 7, wherein the monocarboxylic acid solvent is acetic acid.
Claim 11
Dependent Claim
27 words
A process according to claim 1, wherein the liquid for carrying out said fixing is selected from the group consisting of water, alcohol, acetone, and mixtures thereof.
Claim 12
Dependent Claim
17 words
A process according to claim 1 further comprising: washing the molded gel with water before said removing.
Claim 13
Dependent Claim
132 words
A process for making gradient index glass comprising: forming a mixture of a silicon alkoxide, at least two other metal alkoxides, and an alcohol in a solution sufficiently acidic to hydrolyze partially the silicon alkoxide; adding water to the mixture to convert the metal alkoxides to a network of corresponding metal oxides suitable for gelation; containing the mixture containing the network of metal oxides for sufficient time to form a gel; removing substantially only one of the at least two other metal oxides from the gel; withdrawing partially one of the at least two other metal oxides from the gel remaining after said removing; fixing the gel in a liquid capable of arresting said removing and withdrawing; drying the fixed gel; and sintering the dried gel to form a transparent gradient-index glass.
Claim 14
Dependent Claim
132 words
A process for making gradient index glass comprising: forming a mixture of a silicon alkoxide, at least two other metal alkoxides, and an alcohol in a solution sufficiently acidic to hydrolyze partially the silicon alkoxide; adding water to the mixture to convert the metal alkoxides to a network of corresponding metal oxides suitable for gelation; containing the mixture containing the network of metal oxides for sufficient time to form a gel; removing substantially only one of the at least two other metal oxides from the gel; withdrawing partially one of the at least two other metal oxides from the gel remaining after said removing; fixing the gel in a liquid capable of arresting said removing and withdrawing; drying the fixed gel; and sintering the dried gel to form a transparent gradient-index glass.
Claim 15
Dependent Claim
24 words
A process according to claim 12, wherein the at least two other metals comprise a gel structure modifying metal and an index modifying metal.
Claim 16
Dependent Claim
23 words
A process according to claim 13, wherein the index modifying metal is selected from the group consisting of titanium, zirconium, and mixtures thereof.
Claim 17
Dependent Claim
39 words
A process according to claim 14, wherein the alkoxide of the index modifying metal is present in the mixture in an amount sufficient to produce a gradient-index glass containing 0.1 to 25 mole % of corresponding index modifying oxide.
Claim 18
Dependent Claim
14 words
A process according to claim 13, wherein the gel structure modifying metal is aluminum.
Claim 19
Dependent Claim
41 words
A process according to claim 16, wherein the alkoxide of the gel structure modifying metal is present in the mixture in an amount sufficient to produce a gradient index glass containing less than 25 mole % of corresponding additional metal oxide.
Claim 20
Dependent Claim
41 words
A process according to claim 13, wherein an oxide of the gel structure modifying metal is taken out of the gel during said removing and an oxide of the index modifying metal is taken out of the gel during said withdrawing.
Claim 21
Dependent Claim
21 words
A process according to claim 18, wherein the index modifying metal is titanium and the gel structure modifying metal is aluminum.
Claim 22
Dependent Claim
21 words
A process according to claim 12, wherein said removing is carried out by contacting the gel with a monocarboxylic acid solvent.
Claim 23
Dependent Claim
29 words
A process according to claim 20, wherein the monocarboxylic acid solvent is selected from the group consisting of acetic acid, formic acid, propionic acid, butyric acid, and mixtures thereof.
Claim 24
Dependent Claim
14 words
A process according to claim 21, wherein the monocarboxylic acid solvent is acetic acid.
Claim 25
Dependent Claim
35 words
A process according to claim 12, wherein said withdrawing is carried out in a bath comprising water and an acid selected from the group consisting of an inorganic acid, a dicarboxylic acid, and mixtures thereof.
Claim 26
Dependent Claim
28 words
A process according to claim 23, wherein the acid is an inorganic acid selected from the group consisting of hydrochloric acid, sulfuric acid, nitric acid, and mixtures thereof.
Claim 27
Dependent Claim
25 words
A process according to claim 23, wherein the acid is a dicarboxylic acid selected from group consisting of oxalic acid, malonic acid, and mixtures thereof.
Claim 28
Dependent Claim
27 words
A process according to claim 12, wherein the liquid for carrying out said fixing is selected from the group consisting of water, alcohol, acetone, and mixtures thereof.
Claim 29
Dependent Claim
32 words
A process according to claim 12, wherein the silicon alkoxide is incorporated in the mixture in an amount sufficient to produce a gradient-index glass containing 60 to 98 mole % silicon dioxide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-05-02 | 1997-11-01 | 1998-05-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-05-02 | 2001-11-01 | 2002-05-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-05-02 | 2005-11-01 | 2006-05-03 | $7700.00 | Window Closed / Lapsed |