Plasma cleaning method for removing residues in a plasma process chamber
Assignee: Lam Research Corp
•
Filing: 1995-12-22
•
Granted: 1997-07-15
•
Expires: 2015-12-22
Abstract
Abstract A method for cleaning and conditioning a plasma processing chamber wherein oxide residues have been previously formed on interior surfaces of the chamber. The method includes introducing a cleaning gas including a fluorine-based gas into the chamber followed by performing a plasma cleaning step. The plasma cleaning step is performed by activating the cleaning gas mixture and forming a plasma cleaning gas, contacting interior surfaces of the chamber with the plasma cleaning gas and removing oxide residues on the interior surfaces. The cleaning step is followed by coating the interior surfaces with silicon dioxide to adhere loose particles to the interior surfaces and a conditioning step wherein uncoated interior surfaces are treated to remove fluorine therefrom. An advantage of the cleaning and conditioning method is that it is not necessary to open the chamber. Also, it is possible to remove oxide residues during the cleaning step and remove fluorine remaining after the cleaning step during the conditioning step. The conditioning step is carried out by introducing a hydrogen-containing gas into the chamber as a purge gas or the chamber can be pressurized by the hydrogen-containing gas followed by evacuating the chamber.
Inventors
- 👤 Larry Williams
- 👤 David R. Pirkle
- 👤 William Harshbarger
- 👤 Timothy Ebel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 11:14
CPC Classifications
B; B08; B08B; B08B7/00; B08B7/0035; C; C23; C23C; C23C16/00; C23C16/44; C23C16/4401; C23C16/4404; C23C16/4405; Y; Y10; Y10S; Y10S438/00; Y10S438/905
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
168 words
A plasma cleaning method for removing oxide residues in a plasma process chamber wherein substrates are processed, comprising steps of: introducing a cleaning gas comprising a fluorine-based gas into the plasma process chamber; performing a plasma cleaning step by activating the cleaning gas and forming a plasma cleaning gas, contacting interior surfaces of the chamber with the plasma cleaning gas for a time sufficient to remove oxide residues on the interior surfaces; coating the interior surfaces with silicon dioxide, the coating step being carried out by introducing a coating gas mixture comprising a silicon-containing gas into the chamber, activating the coating gas mixture and forming a plasma coating gas, and contacting the interior surfaces with the plasma coating gas until the interior surfaces are coated with silicon dioxide; and conditioning uncoated interior surfaces by introducing a conditioning gas comprising a hydrogen-containing gas into the chamber, contacting the interior surfaces with the conditioning gas in a non-plasma state for a time sufficient to remove fluorine from the interior surfaces.
Claim 2
Dependent Claim
168 words
A plasma cleaning method for removing oxide residues in a plasma process chamber wherein substrates are processed, comprising steps of: introducing a cleaning gas comprising a fluorine-based gas into the plasma process chamber; performing a plasma cleaning step by activating the cleaning gas and forming a plasma cleaning gas, contacting interior surfaces of the chamber with the plasma cleaning gas for a time sufficient to remove oxide residues on the interior surfaces; coating the interior surfaces with silicon dioxide, the coating step being carried out by introducing a coating gas mixture comprising a silicon-containing gas into the chamber, activating the coating gas mixture and forming a plasma coating gas, and contacting the interior surfaces with the plasma coating gas until the interior surfaces are coated with silicon dioxide; and conditioning uncoated interior surfaces by introducing a conditioning gas comprising a hydrogen-containing gas into the chamber, contacting the interior surfaces with the conditioning gas in a non-plasma state for a time sufficient to remove fluorine from the interior surfaces.
Claim 3
Dependent Claim
17 words
The method of claim 1, wherein the fluorine-based gas comprises 100% by volume of the cleaning gas.
Claim 4
Dependent Claim
18 words
The method of claim 1, wherein the cleaning gas further comprises ≦10 volume % of an oxygen-containing gas.
Claim 5
Dependent Claim
16 words
The method of claim 1, wherein the cleaning gas further contains ≦10 volume % of argon.
Claim 6
Dependent Claim
13 words
The method of claim 1, wherein the hydrogen-containing gas comprises SiH 4 .
Claim 7
Dependent Claim
21 words
The method of claim 1, wherein the fluorine-based gas comprises NF 3 , SF 6 , a fluorocarbon or mixture thereof.
Claim 8
Dependent Claim
19 words
The method of claim 6, wherein the fluorocarbon comprises CF 4 , C 2 F 6 or mixture thereof.
Claim 9
Dependent Claim
20 words
The method of claim 1, wherein the plasma cleaning gas converts silicon dioxide on the interior surfaces to gas by-products.
Claim 10
Dependent Claim
14 words
The method of claim 1, wherein the chamber is evacuated during the cleaning step.
Claim 11
Dependent Claim
20 words
The method of claim 1, wherein the conditioning step is carried out by flowing the hydrogen-containing gas through the chamber.
Claim 12
Dependent Claim
45 words
The method of claim 1, wherein the conditioning step is carried out by flowing the hydrogen-containing gas into the chamber and building up pressure to 0.25 to 1 Torr therein followed by suddenly evacuating the chamber and removing the hydrogen-containing gas and loose particles therefrom.
Claim 13
Dependent Claim
54 words
The method of claim 1, further comprising a step of depositing one or more layers on at least one semiconductor substrate in the chamber prior to the plasma cleaning step, the layers including at least one oxide film and the depositing step causing oxide residues to be deposited on interior surfaces of the chamber.
Claim 14
Dependent Claim
16 words
The method of claim 12, wherein the oxide residues are removed by the plasma cleaning gas.
Claim 15
Dependent Claim
25 words
The method of claim 1, wherein the conditioning step removes fluorine from the interior surfaces in the form of SiF 4 and HF 4 .
Claim 16
Dependent Claim
23 words
The method of claim 1, wherein the coating step is carried out until the coating has a thickness of 2000 Åto 2 μm.
Claim 17
Dependent Claim
26 words
The method of claim 1, wherein the conditioning step is followed by introducing a substrate into the chamber and depositing an oxide layer on the substrate.
Claim 18
Dependent Claim
39 words
The method of claim 1, wherein the plasma cleaning gas is generated in a plasma generating chamber of an ECR reactor and the coating step coats interior surfaces in a substrate treatment chamber located adjacent the plasma generating chamber.
Claim 19
Dependent Claim
14 words
The method of claim 1, wherein the chamber is located in an ECR reactor.
Claim 20
Dependent Claim
20 words
The method of claim 1, wherein the silicon dioxide is coated directly on the interior surfaces during the coating step.
Claim 21
Dependent Claim
21 words
The method of claim 1, wherein the interior surfaces are maintained at a temperature below 100° C. during the conditioning step.
Claim 22
Dependent Claim
179 words
A plasma cleaning method for removing oxide residues in a plasma process chamber wherein substrates are processed, comprising steps of: introducing a cleaning gas comprising a fluorine-based gas into the plasma process chamber; performing a plasma cleaning step by activating the cleaning gas and forming a plasma cleaning gas, contacting interior surfaces of the chamber with the plasma cleaning gas for a time sufficient to remove oxide residues on the interior surfaces; coating the interior surfaces with silicon dioxide, the coating step being carried out by introducing a coating gas mixture comprising a silicon-containing gas into the chamber, activating the coating gas mixture and forming a plasma coating gas, and contacting the interior surfaces with the plasma coating gas until the interior surfaces are coated with silicon dioxide; the coating gas comprising SiH 4 , O 2 and Ar and conditioning uncoated interior surfaces by introducing a conditioning gas comprising a hydrogen-containing gas into the chamber, contacting the interior surfaces with the conditioning gas in a non-plasma state for a time sufficient to remove fluorine from the interior surfaces.
Claim 23
Dependent Claim
179 words
A plasma cleaning method for removing oxide residues in a plasma process chamber wherein substrates are processed, comprising steps of: introducing a cleaning gas comprising a fluorine-based gas into the plasma process chamber; performing a plasma cleaning step by activating the cleaning gas and forming a plasma cleaning gas, contacting interior surfaces of the chamber with the plasma cleaning gas for a time sufficient to remove oxide residues on the interior surfaces; coating the interior surfaces with silicon dioxide, the coating step being carried out by introducing a coating gas mixture comprising a silicon-containing gas into the chamber, activating the coating gas mixture and forming a plasma coating gas, and contacting the interior surfaces with the plasma coating gas until the interior surfaces are coated with silicon dioxide; the coating gas comprising SiH 4 , O 2 and Ar and conditioning uncoated interior surfaces by introducing a conditioning gas comprising a hydrogen-containing gas into the chamber, contacting the interior surfaces with the conditioning gas in a non-plasma state for a time sufficient to remove fluorine from the interior surfaces.
Claim 24
Dependent Claim
24 words
The method of claim 21, wherein the O 2 and SiH 4 are present in a ratio of O 2 :SiH 4 of 1.3-4:1.
Claim 25
Dependent Claim
220 words
A plasma cleaning method for removing oxide residues in a plasma process chamber wherein substrates are processed, comprising steps of: introducing a cleaning gas comprising a fluorine-based gas into the plasma process chamber; performing a plasma cleaning step by activating the cleaning gas and forming a plasma cleaning gas, contacting interior surfaces of the chamber with the plasma cleaning gas for a time sufficient to remove oxide residues on the interior surfaces; coating the interior surfaces with silicon dioxide, the coating step being carried out by introducing a coating gas mixture comprising a silicon-containing gas into the chamber, activating the coating gas mixture and forming a plasma coating gas, and contacting the interior surfaces with the plasma coating gas until the interior surfaces are coated with silicon dioxide; conditioning uncoated interior surfaces by introducing a conditioning gas comprising a hydrogen-containing gas into the chamber, contacting the interior surfaces with the conditioning gas in a non-plasma state for a time sufficient to remove fluorine from the interior surfaces; and the chamber being located in an ECR reactor and including water-cooled aluminum chamber walls and at least one water-cooled aluminum component maintained at a temperature of less than 100° C. during the plasma cleaning step, the component being coated with a silicon dioxide coating which traps Al and F in the coating.
Claim 26
Dependent Claim
220 words
A plasma cleaning method for removing oxide residues in a plasma process chamber wherein substrates are processed, comprising steps of: introducing a cleaning gas comprising a fluorine-based gas into the plasma process chamber; performing a plasma cleaning step by activating the cleaning gas and forming a plasma cleaning gas, contacting interior surfaces of the chamber with the plasma cleaning gas for a time sufficient to remove oxide residues on the interior surfaces; coating the interior surfaces with silicon dioxide, the coating step being carried out by introducing a coating gas mixture comprising a silicon-containing gas into the chamber, activating the coating gas mixture and forming a plasma coating gas, and contacting the interior surfaces with the plasma coating gas until the interior surfaces are coated with silicon dioxide; conditioning uncoated interior surfaces by introducing a conditioning gas comprising a hydrogen-containing gas into the chamber, contacting the interior surfaces with the conditioning gas in a non-plasma state for a time sufficient to remove fluorine from the interior surfaces; and the chamber being located in an ECR reactor and including water-cooled aluminum chamber walls and at least one water-cooled aluminum component maintained at a temperature of less than 100° C. during the plasma cleaning step, the component being coated with a silicon dioxide coating which traps Al and F in the coating.
References Cited (Backward Citations)
US4340462A
Cited
JPS57201016A
Cited
US4576698A
Cited
US4857139A
Cited
JPS61136981A
Cited
JPS61250185A
Cited
US4657616A
Cited
US4749440A
Cited
JPS62214175A
Cited
US4786352A
Cited
US4842683A
Cited
US5158644A
Cited
US4816113A
Cited
JPS63267430A
Cited
US4986877A
Cited
US5006192A
Cited
US5041311A
Cited
JPH0362520A
Cited
US4948458A
Cited
US5207836A
Cited
US5129958A
Cited
US5089441A
Cited
US5022958A
Cited
US5200232A
Cited
US5356478A
Cited
US5413670A
Cited
US5503676A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-07-14 | 2001-01-13 | 2001-07-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-07-14 | 2005-01-13 | 2005-07-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-07-14 | 2009-01-13 | 2009-07-15 | $7700.00 | Window Closed / Lapsed |