Method of fabricating step poly to improve program speed in split gate flash
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1998-07-15
•
Granted: 1999-03-09
•
Expires: 2018-07-15
Abstract
Abstract A method is provided for forming a split-gate flash memory cell having a step poly supporting an interpoly oxide of varying thickness for the purposes of improving the over-all performance of the cell. Polyoxide is formed over portions of a first polysilicon layer which in turn is partially etched to form a step adjacent to the side-wall of a floating gate underlying the polyoxide. A spacer is next formed of a hot temperature oxide over the step poly. An interpoly oxynitride is then formed and control gate is patterned overlapping the floating gate with the intervening interpoly oxide. The step poly and the spacer thereon form proper distances between the control gate and the floating gate while keeping the distance between the poly tip and the control gate unchanged so that appropriate couplings between the control gate and the floating gate, and between the floating gate and the substrate are achieved, thus improving the over-all performance of the split-gate flash memory having a step poly.
Inventors
- 👤 Chia-Ta Hsieh
- 👤 Yai-Fen Lin
- 👤 Hung-Cheng Sung
- 👤 Chuang-Ke Yeh
- 👤 Di-Son Kuo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 11:49
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/0411; H10D30/60; H10D30/68; H10D30/6891
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
294 words
A method of forming a step poly to improve program speed in a split-gate flash memory cell comprising the steps of: providing a silicon substrate having a plurality of active and field regions defined; forming a tunnel oxide layer over said substrate; forming a first polysilicon layer over said tunnel oxide layer; forming a layer of nitride over said tunnel oxide layer; forming and patterning a first photoresist layer to form a photoresist mask with a pattern corresponding to the floating gate of said split-gate flash memory cell; etching said layer of nitride through said photoresist mask to form openings in said layer of nitride and to expose portions of said first polysilicon layer corresponding to said floating gate pattern; removing said first photoresist layer; oxidizing portions of said first polysilicon layer exposed in said openings in said layer of nitride to form polyoxide; removing said layer of nitride; using said polyoxide as a hard mask to etch portions of said first polysilicon layer not covered by said polyoxide hard mask to form floating gate with a step underlying said polyoxide; forming a layer of hot thermal oxide (HTO) over said substrate conformally covering said polyoxide overlying said floating gate; forming HTO spacer on sidewall of said floating gate; using said polyoxide and HTO spacer as mask, etching further said first polysilicon layer and said tunnel oxide; forming a layer of interpoly oxide over said substrate conformally covering said polyoxide overlying said floating gate; depositing a second polysilicon layer over said interpoly oxide; and patterning said second polysilicon layer with a second photoresist mask having control gate pattern to form a control gate to complete the forming of said split-gate flash memory cell with said step poly to improve program speed of said memory.
Claim 2
Independent Claim
294 words
A method of forming a step poly to improve program speed in a split-gate flash memory cell comprising the steps of: providing a silicon substrate having a plurality of active and field regions defined; forming a tunnel oxide layer over said substrate; forming a first polysilicon layer over said tunnel oxide layer; forming a layer of nitride over said tunnel oxide layer; forming and patterning a first photoresist layer to form a photoresist mask with a pattern corresponding to the floating gate of said split-gate flash memory cell; etching said layer of nitride through said photoresist mask to form openings in said layer of nitride and to expose portions of said first polysilicon layer corresponding to said floating gate pattern; removing said first photoresist layer; oxidizing portions of said first polysilicon layer exposed in said openings in said layer of nitride to form polyoxide; removing said layer of nitride; using said polyoxide as a hard mask to etch portions of said first polysilicon layer not covered by said polyoxide hard mask to form floating gate with a step underlying said polyoxide; forming a layer of hot thermal oxide (HTO) over said substrate conformally covering said polyoxide overlying said floating gate; forming HTO spacer on sidewall of said floating gate; using said polyoxide and HTO spacer as mask, etching further said first polysilicon layer and said tunnel oxide; forming a layer of interpoly oxide over said substrate conformally covering said polyoxide overlying said floating gate; depositing a second polysilicon layer over said interpoly oxide; and patterning said second polysilicon layer with a second photoresist mask having control gate pattern to form a control gate to complete the forming of said split-gate flash memory cell with said step poly to improve program speed of said memory.
Claim 3
Dependent Claim
26 words
The method of claim 1, wherein said forming a tunnel oxide layer is accomplished by thermal growth at a temperature between about 850° to 950° C.
Claim 4
Dependent Claim
20 words
The method of claim 2, wherein said tunnel oxide layer has a thickness between about 80 to 90 angstroms (Å).
Claim 5
Dependent Claim
30 words
The method of claim 1, wherein said forming a first polysilicon layer is accomplished with silicon source SiH 4 using LPCVD at a temperature between about 550° to 650° C.
Claim 6
Dependent Claim
20 words
The method of claim 1, wherein said first polysilicon layer has a thickness between about 1100 to 1300 angstroms (Å).
Claim 7
Dependent Claim
39 words
The method of claim 1, wherein said forming a layer of nitride is accomplished with LPCVD at a temperature between about 750° C. to 830° C. by reacting dichlorosilane (SiCl 2 H 2 ) with ammonia (NH 3 ).
Claim 8
Dependent Claim
20 words
The method of claim 4, wherein the thickness of said layer of nitride is between about 750 to 850 Å.
Claim 9
Dependent Claim
19 words
The method of claim 1, wherein said photoresist mask has a thickness between about 0.5 to 1.5 micrometers (μm).
Claim 10
Dependent Claim
41 words
The method of claim 1, wherein said etching said layer of nitride is accomplished with etch recipe comprising Ar, CHF 3 , CF 4 at flow rates between about 700 to 1000, 5 to 20 and 50 to 100 sccm, respectively.
Claim 11
Dependent Claim
18 words
The method of claim 1, wherein said removing said first photoresist layer is accomplished by oxygen plasma ashing.
Claim 12
Dependent Claim
31 words
The method of claim 1, wherein said oxidizing portions of said first polysilicon layer to form polyoxide is accomplished by wet oxidation at a temperature between about 900° to 1100° C.
Claim 13
Dependent Claim
18 words
The method of claim 11, wherein the thickness of said polyoxide is between about 1400 to 1600 Å.
Claim 14
Dependent Claim
24 words
The method of claim 1, wherein said removing said layer of nitride is accomplished with a wet solution of H 3 PO 4 .
Claim 15
Dependent Claim
52 words
The method of claim 1, wherein said etching said first polysilicon layer using said polyoxide as a hard mask to form said floating gate with a step is accomplished using a recipe comprising gases HBr and Cl 2 with flow rates between about 30 to 200 sccm, and 30 to 200 sccm.
Claim 16
Dependent Claim
28 words
The method of claim 14, wherein said floating gate with step is step poly having a depth between about one-half to two-thirds thickness of said first polysilicon layer.
Claim 17
Dependent Claim
20 words
The method of claim 1, wherein said forming a layer of hot thermal oxide (HTO) is accomplished by LPCVD process.
Claim 18
Dependent Claim
20 words
The method of claim 16, wherein the thickness of said layer of HTO is between about 100 to 300 Å.
Claim 19
Dependent Claim
28 words
The method of claim 1, wherein said forming said HTO spacer is accomplished by performing an anisotropic etch using a recipe comprising CF 4 and CHF 3 .
Claim 20
Dependent Claim
27 words
The method of claim 1, wherein etching further said first polysilicon layer and said tunnel oxide is accomplished with a recipe comprising HBr and Cl 2 .
Claim 21
Dependent Claim
20 words
The method of claim 1, wherein said interpoly oxide is oxynitride with a thickness between about 100 to 300 Å.
Claim 22
Dependent Claim
34 words
The method of claim 1, wherein said depositing a second polysilicon layer over said interpoly oxide is accomplished with silicon source SiH 4 using LPCVD at a temperature between about 550° to 650° C.
Claim 23
Dependent Claim
24 words
The method of claim 1, wherein said second polysilicon layer to form a control gate has a thickness between about 1000 to 2000 Å.
References Cited (Backward Citations)
US4339767A
Cited
US4687541A
Cited
US4818715A
Cited
US5067108A
Cited
US5227322A
Cited
US5447878A
Cited
US5340769A
Cited
US5493138A
Cited
US5670017A
Cited
US5674782A
Cited
US5769952A
Cited
US5614747A
Cited
US5422292A
Cited
US5652161A
Cited
US5814551A
Cited
US5656532A
Cited
US5814853A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-03-08 | 2002-09-07 | 2003-03-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-03-08 | 2006-09-07 | 2007-03-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-03-08 | 2010-09-07 | 2011-03-09 | $7700.00 | Window Closed / Lapsed |