Sol-gel process of making gradient-index glass
Assignee: University of Rochester
•
Filing: 1993-06-25
•
Granted: 1994-03-15
•
Expires: 2013-06-25
Abstract
Abstract The present invention relates to a process for making glass by a sol-gel process. The process is initiated by forming a mixture of silicon alkoxide and an alcohol in a solution sufficiently acidic to partially hydrolyze the silicon alkoxide. An index modifying metal alkoxide selected from the group consisting of alkoxides of titanium and zirconium is then added to the mixture. Water is next added to convert the metal alkoxides to a network of corresponding metal oxides suitable for gelation. The mixture containing the network of metal oxides is then contained for sufficient time to form a gel. The gel is acid leached for enough time to remove some of the index modifying metal oxide. To prevent further removal of index modifying metal oxide from the gel, the gel is fixed. The fixed gel is then rinsed with a solvent to remove precipitates from the gel, dried, and sintered into a transparent gradient-index glass. In another aspect of the present invention, the fixing agent can be acetone or a mixture of water and acetone.
Inventors
- 👤 Niels Haun
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 02:38
CPC Classifications
C; C03; C03C; C03C1/00; C03C1/006; C03C3/00; C03C3/04
Claims Analysis
Total Claims: 36
Claim 1
Independent Claim
128 words
A process for making a gradient-index glass comprising: forming a mixture of a silicon alkoxide and an alcohol in a solution sufficiently acidic to partially hydrolyze the silicon alkoxide; adding to the mixture an index modifying metal alkoxide selected from the group consisting of alkoxides of titanium and zirconium; adding water to the mixture to convert the metal alkoxides to a network of corresponding metal oxides suitable for gelation; containing the mixture containing the network of metal oxides for sufficient time to form a gel; acid leaching the contained gel for sufficient time to remove some of the index modifying metal oxide; fixing the gel in acetone or a mixture of water and acetone; drying the fixed gel; and sintering the dried gel into a transparent gradient-index glass.
Claim 2
Dependent Claim
128 words
A process for making a gradient-index glass comprising: forming a mixture of a silicon alkoxide and an alcohol in a solution sufficiently acidic to partially hydrolyze the silicon alkoxide; adding to the mixture an index modifying metal alkoxide selected from the group consisting of alkoxides of titanium and zirconium; adding water to the mixture to convert the metal alkoxides to a network of corresponding metal oxides suitable for gelation; containing the mixture containing the network of metal oxides for sufficient time to form a gel; acid leaching the contained gel for sufficient time to remove some of the index modifying metal oxide; fixing the gel in acetone or a mixture of water and acetone; drying the fixed gel; and sintering the dried gel into a transparent gradient-index glass.
Claim 3
Dependent Claim
36 words
A process according to claim 1 further comprising: adding to the mixture at least one additional metal alkoxide element selected from the group consisting of alkoxides of aluminum, boron, and germanium prior to said adding water.
Claim 4
Dependent Claim
18 words
A process according to claim 2 further comprising: washing the contained gel with water before said acid leaching.
Claim 5
Dependent Claim
29 words
A process according to claim 2, wherein the silicon alkoxide is added in an amount sufficient to produce a gradient-index glass containing 60 to 98 mole percent silicon oxide.
Claim 6
Dependent Claim
33 words
A process according to claim 2, wherein the index modifying alkoxide is added in an amount sufficient to produce a gradient-index glass containing 0.1 to 25 mole percent of corresponding index modifying oxide.
Claim 7
Dependent Claim
37 words
A process according to claim 2, wherein the additional metal alkoxide element is added in an amount sufficient to produce a gradient index glass containing between 1 and 25 mole percent of corresponding additional metal oxide element.
Claim 8
Dependent Claim
36 words
A process according to claim 2, wherein said acid leaching is carried out in a bath comprising water and an acid selected from the group consisting of an inorganic acid, a dicarboxylic acid, and mixtures thereof.
Claim 9
Dependent Claim
28 words
A process according to claim 7, wherein the acid is an inorganic acid selected from the group consisting of hydrochloric acid, sulfuric acid, nitric acid, and mixtures thereof.
Claim 10
Dependent Claim
26 words
A process according to claim 7, wherein the acid is a dicarboxylic acid selected from the group consisting of oxalic acid, malonic acid, and mixtures thereof.
Claim 11
Dependent Claim
26 words
A process according to claim 2, wherein the index modifying metal alkoxide is titanium alkoxide and the at least one additional metal alkoxide is aluminum alkoxide.
Claim 12
Dependent Claim
36 words
A process according to claim 10, wherein the glass comprises: 89 to 98 mole % SiO 2 , 0.1 to 6 mole % TiO 2 ; and 0to 5 mole % 1/2(Al 2 O 3 ).
Claim 13
Dependent Claim
14 words
A process according to claim 1, wherein said fixing is carried out in acetone.
Claim 14
Dependent Claim
19 words
A process according to claim 1, wherein said fixing is carried out in a mixture of acetone and water.
Claim 15
Dependent Claim
43 words
A process according to claim 13, wherein said fixing is carried out in a mixture of acetone and water which contains acetone and water in a ratio that will result in a maximum difference in refractive index (Δn) in the gradient index glass.
Claim 16
Dependent Claim
39 words
A process according to claim 13, wherein said fixing is carried out in a mixture of acetone and water which contains acetone and water in a ratio that will result in gradient index glass having a substantially parabolic shape.
Claim 17
Dependent Claim
145 words
A process for making a gradient-index glass comprising: forming a mixture of a silicon alkoxide and an alcohol in a solution sufficiently acidic to partially hydrolyze the silicon alkoxide; adding to the mixture an index modifying metal alkoxide selected from the group consisting of alkoxides of titanium and zirconium; adding water to the mixture to convert the metal alkoxides to a network of corresponding metal oxides suitable for gelation; containing the mixture containing the network of metal oxides for sufficient time to form a gel; acid leaching the contained gel for sufficient time to remove some of the index modifying metal oxide; fixing the gel to prevent further removal of the index modifying metal oxide from the gel; rinsing the fixed gel with a solvent to remove precipitates from the gel; drying the fixed gel; and sintering the dried gel into a transparent gradient-index glass.
Claim 18
Dependent Claim
145 words
A process for making a gradient-index glass comprising: forming a mixture of a silicon alkoxide and an alcohol in a solution sufficiently acidic to partially hydrolyze the silicon alkoxide; adding to the mixture an index modifying metal alkoxide selected from the group consisting of alkoxides of titanium and zirconium; adding water to the mixture to convert the metal alkoxides to a network of corresponding metal oxides suitable for gelation; containing the mixture containing the network of metal oxides for sufficient time to form a gel; acid leaching the contained gel for sufficient time to remove some of the index modifying metal oxide; fixing the gel to prevent further removal of the index modifying metal oxide from the gel; rinsing the fixed gel with a solvent to remove precipitates from the gel; drying the fixed gel; and sintering the dried gel into a transparent gradient-index glass.
Claim 19
Dependent Claim
11 words
A process according to claim 16, wherein the solvent is water.
Claim 20
Dependent Claim
19 words
A process according to claim 16, wherein said fixing is carried out with a material which causes precipitation formation.
Claim 21
Dependent Claim
26 words
A process according to claim 18, wherein said fixing is carried out with alcohol alone, alcohol mixed with water, acetone alone, or acetone mixed with water.
Claim 22
Dependent Claim
21 words
A process according to claim 16, wherein said rinsing results in an increased difference in refractive index in the gradient-index glass.
Claim 23
Dependent Claim
35 words
A process according to claim 16 further comprising: adding to the mixture at least one additional metal alkoxide selected from the group consisting of alkoxides of aluminum, boron, and germanium prior to said adding water.
Claim 24
Dependent Claim
33 words
A process according to claim 21, wherein the silicon alkoxide is incorporated in the mixture in an amount sufficient to produce a gradient index glass containing 60 to 98 mole percent silicon oxide.
Claim 25
Dependent Claim
26 words
A process according to claim 21, wherein the index modifying metal alkoxide is titanium alkoxide and the at least one additional metal alkoxide is aluminum alkoxide.
Claim 26
Dependent Claim
37 words
A process according to claim 23, wherein the glass comprises: 89 to 98 mole % SiO 2 ; 0.1 to 6 mole % TiO 2 ; and 0 to 5 mole % 1/2(Al 2 O 3 ).
Claim 27
Dependent Claim
14 words
A process according to claim 17, wherein said fixing is carried out in acetone.
Claim 28
Dependent Claim
19 words
A process according to claim 25, wherein said fixing is carried out in a mixture of acetone and water.
Claim 29
Dependent Claim
35 words
A process according to claim 26, wherein the mixture of acetone and water contains acetone and water in a ratio that will result in a maximum difference in refractive index (Δ) in the gradient-index glass.
Claim 30
Dependent Claim
31 words
A process according to claim 26, wherein the mixture of acetone and water contains acetone and water in a ratio that will result in gradient-index glass having a substantially parabolic shape.
Claim 31
Dependent Claim
18 words
A process according to claim 17 further comprising: washing the contained gel with water before said acid leaching.
Claim 32
Dependent Claim
36 words
A process according to claim 17, wherein the index modifying alkoxide is added to the mixture in an amount sufficient to produce a gradient-index glass containing 0.1 to 25 mole percent of corresponding index modifying oxide.
Claim 33
Dependent Claim
40 words
A process according to claim 17, wherein the additional metal alkoxide element is added to the mixture in an amount sufficient to produce a gradient index glass containing between 1 and 25 mole percent of corresponding additional metal oxide element.
Claim 34
Dependent Claim
36 words
A process according to claim 17, wherein said acid leaching is carried out in a bath comprising water and an acid selected from the group consisting of an inorganic acid, a dicarboxylic acid, and mixtures thereof.
Claim 35
Dependent Claim
28 words
A process according to claim 32, wherein the acid is an inorganic acid selected from the group consisting of hydrochloric acid, sulfuric acid, nitric acid, and mixtures thereof.
Claim 36
Dependent Claim
26 words
A process according to claim 32, wherein the acid is a dicarboxylic acid selected from the group consisting of oxalic acid, malonic acid, and mixtures thereof.
References Cited (Backward Citations)
US5196382A
Cited
US4686195A
Cited
US4797376A
Cited
US4902650A
Cited
US5238880A
Cited
US5068208A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-03-14 | 1997-09-13 | 1998-03-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-03-14 | 2001-09-13 | 2002-03-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-03-14 | 2005-09-13 | 2006-03-15 | $7700.00 | Window Closed / Lapsed |