Plasma-resistant polymeric material, preparation thereof, and use thereof

Claim 2

A process which comprises: a. providing a layer of polymeric material wherein said polymeric material contains at least reactive hydrogen functional groups or reactive hydrogen functional precursor groups and when said polymeric material contains said precursor groups, converting said precursor groups to reactive hydrogen functional groups; b. then reacting at least a portion of said layer of polymeric material with a multifunctional organometallic material containing at least two functional groups which are reactive with the reactive groups of said polymeric material to thereby render the said at least portion of said layer resistant to oxygen plasma which is at least about 20 times greater than is the polymeric material before it is reacted with said organometallic material and; c. then subjecting said layer to a gas plasma atmosphere.

Claim 3

The process of claim 1 wherein said gas plasma atmosphere is an oxygen-containing plasma atmosphere.

Claim 4

The process of claim 1 wherein the resistance to oxygen plasma is increased at least about 50 times, as compared to the polymeric material before it is reacted with the organometallic material.

Claim 5

The process of claim 1 wherein the increase in resistance to oxygen plasma is at least about 100 times that of the polymeric material before it is reacted with the organometallic material.

Claim 6

The process of claim 1 wherein at least about 25% of the thickness of the layer of polymeric material is reacted with the organometallic material.

Claim 7

The process of claim 1 wherein at least about 50% of the thickness of the layer of polymeric material is reacted with the organometallic material.

Claim 8

The process of claim 1 wherein at least substantially, the entire thickness of the layer of polymeric material is reacted with the organometallic material.

Claim 9

The process of claim 1 wherein said multifunctional organometallic material is provided as a liquid composition in a solvent for the organometallic material wherein the solvent is nonreactive with the organometallic material.

Claim 10

The process of claim 1 wherein that portion of the layer which is reacted contains at least about 1 part by weight of the metallic component of the organometallic material per 20 parts of polymeric material.

Claim 11

The process of claim 9 wherein that portion of the layer which is reacted contains up to 1 part by weight of the metallic component of the organometallic material per 2 parts by weight of the polymeric material.

Claim 12

The process of claim 1 wherein that portion of the layer which is reacted contains a ratio of a metallic component of the organometallic material to the polymeric material of about 1:15 to about 1:4.

Claim 13

The process of claim 1 wherein said organometallic material is an organosilicon material.

Claim 14

The process of claim 1 wherein said organometallic material is a cyclic organosilicon compound.

Claim 15

The process of claim 1 wherein said organometallic material is hexamethylcyclotrisilazane.

Claim 16

The process of claim 1 wherein said layer is about 0.4 to about 10 microns thick.

Claim 17

A process for rendering a polymeric material resistant to oxygen plasma which comprises: providing a polymeric material containing at least reactive hydrogen functional groups or reactive hydrogen functional precursor groups, and when said polymeric material contains said precursor groups, converting said precursor groups to reactive hydrogen functional groups and wherein said polymeric material is a phenolic-formaldehyde polymer; providing a liquid composition containing a multifunctional organosilicon material containing at least two functional groups which are reactive with the reactive functional groups of said phenolic-formaldehyde polymeric material, a solvent for said multifunctional organosilicon material wherein said solvent is nonreactive with said organosilicon material, and a solvent for said polymeric material in an amount effective to decrease the reaction time between said multifunctional organosilicon material and said polymeric material, and not sufficient to dissolve said polymeric material, and wherein said solvent for said polymeric material is not reactive with said multifunctional organosilicon material; and contacting said liquid composition with said polymeric material to thereby render said polymeric material resistant to oxygen plasma.

Claim 18

A process for rendering a polymeric material resistant to oxygen plasma which comprises: providing a polymeric material containing at least reactive hydrogen functional groups or reactive hydrogen functional precursor groups, and when said polymeric material contains said precursor groups, converting said precursor groups to reactive hydrogen functional groups and wherein said polymeric material is a phenolic-formaldehyde polymer; providing a liquid composition containing a multifunctional organosilicon material containing at least two functional groups which are reactive with the reactive functional groups of said phenolic-formaldehyde polymeric material, a solvent for said multifunctional organosilicon material wherein said solvent is nonreactive with said organosilicon material, and a solvent for said polymeric material in an amount effective to decrease the reaction time between said multifunctional organosilicon material and said polymeric material, and not sufficient to dissolve said polymeric material, and wherein said solvent for said polymeric material is not reactive with said multifunctional organosilicon material; and contacting said liquid composition with said polymeric material to thereby render said polymeric material resistant to oxygen plasma.

Claim 19

The process of claim 16 wherein said organosilicon material is hexamethylcyclotrisilazane.

Claim 20

The process of claim 17 wherein said reacting is carried out at about room temperature to about 75° C.

Claim 21

The process of claim 17 wherein said reacting is carried out at about 40° C.

Claim 22

A process for rendering a polymeric material resistant to oxygen plasma which comprises: providing a polymeric material containing at least reactive hydrogen functional groups or reactive hydrogen functional precursor groups, and when said polymeric material contains said precursor groups, converting said precursor groups to reactive hydrogen functional groups; providing a liquid composition containing a multifunctional organosilicon material containing at least two functional groups which are reactive with the reactive functional groups of said polymeric material, a solvent for said multifunctional organosilicon material wherein said solvent is nonreactive with said organosilicon material and is an aromatic hydrocarbon or substituted aromatic hydrocarbon, and a solvent for said polymeric material in an amount effective to decrease the reaction time between said multifunctional organosilicon material and said polymeric material, and not sufficient to dissolve said polymeric material, and wherein said solvent for said polymeric material is not reactive with said multifunctional organosilicon material; and contacting said liquid composition with said polymeric material to thereby render said polymeric material resistant to oxygen plasma.

Claim 23

A process for rendering a polymeric material resistant to oxygen plasma which comprises: providing a polymeric material containing at least reactive hydrogen functional groups or reactive hydrogen functional precursor groups, and when said polymeric material contains said precursor groups, converting said precursor groups to reactive hydrogen functional groups; providing a liquid composition containing a multifunctional organosilicon material containing at least two functional groups which are reactive with the reactive functional groups of said polymeric material, a solvent for said multifunctional organosilicon material wherein said solvent is nonreactive with said organosilicon material and is an aromatic hydrocarbon or substituted aromatic hydrocarbon, and a solvent for said polymeric material in an amount effective to decrease the reaction time between said multifunctional organosilicon material and said polymeric material, and not sufficient to dissolve said polymeric material, and wherein said solvent for said polymeric material is not reactive with said multifunctional organosilicon material; and contacting said liquid composition with said polymeric material to thereby render said polymeric material resistant to oxygen plasma.

Claim 24

The process of claim 20 wherein said organic solvent for the polymeric material is present in an amount of about 0.01 to about 25% by volume based on the total amount of organic solvent.

Claim 25

The process of claim 20 wherein said organic solvent for the polymeric material is present in an amount of about 0.25 to about 5% by volume based upon the total amount of organic solvent in the composition.

Claim 26

The process of claim 20 wherein said polymeric material is in the form of a layer.

Claim 27

The process of claim 20 wherein said organosilicon composition is a solution of hexamethylcyclotrisilazane in xylene containing a solvent for the polymeric material selected from the group of N-methylpyrrolidone and γ-butyrolactone.

Claim 28

The process of claim 24 wherein said polymeric material is a phenolic-formaldehyde polymer.