Method of making top floating-gate flash EEPROM structure
Assignee: United Microelectronics Corp
•
Filing: 1994-07-15
•
Granted: 1995-10-10
•
Expires: 2014-07-15
Abstract
Abstract A method for forming, and a resultant structure of, a top floating gate FLASH EEPROM cell are described. There is a first insulating structure over a silicon substrate, whereby the first insulating structure is a gate oxide. A first conductive structure is formed over the first insulating structure, whereby the first conductive structure is a control gate. There is a first insulating layer over the surfaces of the first conductive structure, whereby the first insulating layer is an interpoly dielectric. There is a second conductive structure formed over the first insulating layer and over a portion of the silicon substrate adjacent to the first insulating structure, whereby the second conductive structure is a floating gate. A second insulating layer is formed between the silicon substrate and the second conductive structure, whereby the second insulating layer is a tunnel oxide. Active regions in the silicon substrate, implanted with a conductivity-imparting dopant, are formed under the second insulating layer but are horizontally a distance from the first insulating structure.
Inventors
- 👤 Gary Hong
- 👤 Chen-Chiu Hsue
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 20:02
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/0411; H10B; H10B41/00
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
219 words
A method of forming a top floating gate flash EEPROM cell, comprising the steps of: forming a first insulating layer over a silicon substrate; forming a first conductive layer over said first insulating layer; forming a top interpoly dielectric of oxide/nitride/oxide over said first conductive layer; patterning said top interpoly dielectric and said first conductive layer to form a conductive line; forming a side interpoly dielectric of oxide/nitride on the vertical surfaces of said conductive line; removing said first insulating layer in the region not masked by said conductive line, and simultaneously removing the top oxide of said top interpoly dielectric; forming an oxide insulating layer over said silicon substrate, in the region not masked by said conductive line, and over said top and side interpoly dielectrics, whereby said top and side interpoly dielectrics have an oxide/nitride/oxide structure, and whereby said oxide insulating layer forms a tunnel oxide for said EEPROM cell; forming a second conductive layer over said conductive line, said side interpoly dielectric and said top interpoly dielectric; patterning said second conductive layer to form a floating gate over vertical and horizontal surfaces of said conductive line, and over a portion of said tunnel oxide adjacent to said conductive line; and forming active regions in said silicon substrate in the area not masked by said floating gate.
Claim 2
Independent Claim
219 words
A method of forming a top floating gate flash EEPROM cell, comprising the steps of: forming a first insulating layer over a silicon substrate; forming a first conductive layer over said first insulating layer; forming a top interpoly dielectric of oxide/nitride/oxide over said first conductive layer; patterning said top interpoly dielectric and said first conductive layer to form a conductive line; forming a side interpoly dielectric of oxide/nitride on the vertical surfaces of said conductive line; removing said first insulating layer in the region not masked by said conductive line, and simultaneously removing the top oxide of said top interpoly dielectric; forming an oxide insulating layer over said silicon substrate, in the region not masked by said conductive line, and over said top and side interpoly dielectrics, whereby said top and side interpoly dielectrics have an oxide/nitride/oxide structure, and whereby said oxide insulating layer forms a tunnel oxide for said EEPROM cell; forming a second conductive layer over said conductive line, said side interpoly dielectric and said top interpoly dielectric; patterning said second conductive layer to form a floating gate over vertical and horizontal surfaces of said conductive line, and over a portion of said tunnel oxide adjacent to said conductive line; and forming active regions in said silicon substrate in the area not masked by said floating gate.
Claim 3
Dependent Claim
41 words
The method of claim 1 wherein said first insulating layer is formed to a thickness of between about 150 to 400 Angstroms, by thermal oxidation at a temperature of between about 800° to 1000° C. between about 10 to 30 minutes.
Claim 4
Dependent Claim
26 words
The method of claim 1, wherein said first conductive layer is formed of doped polycrystalline silicon at a thickness of between about 1000 to 5000 Angstroms.
Claim 5
Dependent Claim
85 words
The method of claim 1, wherein said forming a top interpoly dielectric comprises the steps of: forming a first layer of silicon oxide, over said first insulating layer, to a thickness of between about 60 to 150 Angstroms; forming a layer of silicon nitride, over said first layer of silicon oxide, to a thickness of between about 80 to 200 Angstroms; and forming a second layer of silicon oxide, over said layer of silicon nitride, to a thickness of between about 20 to 80 Angstroms.
Claim 6
Dependent Claim
75 words
The method of claim 1 wherein said forming a side interpoly dielectric comprises the steps of: forming a layer of silicon oxide, over said conductive line, to a thickness of between about 60 to 200 Angstroms; forming a layer of silicon nitride, over said layer of silicon oxide, to a thickness of between about 100 to 300 Angstroms; and anisotropically etching said layers of silicon oxide and silicon nitride to form said side interpoly dielectric.
Claim 7
Dependent Claim
42 words
The method of claim 1 wherein said oxide insulating layer is formed to a thickness of between about 60 to 120 Angstroms, by thermal oxidation at a temperature of between about 800° to 1000° C. for between about 10 to 50 minutes.
Claim 8
Dependent Claim
26 words
The method of claim 1, wherein said second conductive layer is formed of doped polycrystalline silicon to a thickness of between about 1000 to 5000 Angstroms.
Claim 9
Dependent Claim
41 words
The method of claim 1, wherein active regions are formed by ion implanting with arsenic AS75 at a dose of between about 1 E 15 to 8 E 15 atoms/cm. 2 and an energy of between about 40 to 100 KeV.
Claim 10
Dependent Claim
34 words
The method of claim 1 wherein said portion of said tunnel oxide over which said floating gate extends has a horizontal distance from said first insulating layer of between about 0.2 to 0.8 micrometers.
References Cited (Backward Citations)
US4868629A
Cited
US5061654A
Cited
US5045488A
Cited
US5049515A
Cited
US5293328A
Cited
US5284786A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-10-09 | 1999-04-10 | 1999-10-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-10-09 | 2003-04-10 | 2003-10-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-10-09 | 2007-04-10 | 2007-10-10 | $7700.00 | Window Closed / Lapsed |